Study on the Backup Roll Contour for CSP Continuous Hot Rolling Mill |
LI Hongbo1,ZHANG Jie1,CAO Jianguo1,WANG Qiang2,ZHANG Shushan2 |
1. School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. Ma′anshan Iron and Steel Co., Ltd., Ma′anshan 243003, Anhui,China |
|
|
Abstract Several domestic continuous hot rolling mills in CSP (compact strip production) have CVC (continuously varible crown) work rolls and conventional backup rolls. As the CSP production process is different from the conventional hot rolling with less product varieties,widths, and different roll service periods of stands, the wear characteristics of the rolls are different too. Through tracing and testing the backup rolls, it was found that the backup rolls of the 1800 mm CSP continuous hot rolling mill have two typical wear characteristics on different stands, the serious wear of backup rolls affects the controllability of the mill for profile and flatness of products, and increases the roll consumption.Based on theoretical analysis, two new backup roll contours were proposed for two wear characteristics. Both the trial and the FEM analysis proved that the new roll contours have good property of selfmaintenance, and can work well during the whole service period.
|
Received: 01 January 1900
|
|
|
|
[1] |
LI Ji-wu, CAO Qian-qian, YANG Hai-ru. Thinning of 304 stainless steel pipeline under impact fretting wear[J]. Iron and Steel, 2020, 55(6): 118-122. |
[2] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[3] |
. 本钢三连铸的单流宽板坯连铸机从达涅利公司引进,于2008年12月4日建成投产,结晶器液位控制采用NKK技术。本文介绍了7#连铸机生产过程中,结晶器液位出现不稳定性波浪的原因,并通过改进NKK液位控制工艺,微调PID控制参数,以及优化结晶器流场等措施,提高了宽幅汽车板生产时的结晶器液位控制精度,并且解决和消除了不稳定型波浪的问题,使宽幅汽车板的轧制成材率大幅提升。[J]. , 2020, 45(2): 0-0. |
[4] |
Gan-Shui ZHOU. Diagnosis of instability during trial production of the billet continuous casting in a steel factory in Vietnam[J]. , 2020, 45(2): 0-0. |
[5] |
ZHANG Yu-cheng,WEN Juan,CUI Gui-bin,JIA Hui-ping,QI Qi-ge,JU Xin-hua. Analysis of microstructure and stability of retained austenitein X90 pipeline steel[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(4): 6-11. |
[6] |
ZHANG Hai-jun, DU Wen-hua, XIN Dong-mei. Effects of spray forming and powder metallurgy on microstructureand property of 2030 steels[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(4): 400-406. |
|
|
|
|