| Mild Cooling Mold Powder for Slab Casting |
| ZHU Zumin,ZHANG Chen,CAI Dexiang,CHEN Ronghuan,LIU Jiming |
| Research and Development Center, Baoshan Iron and Steel Co., Ltd., Shanghai 201900, China |
|
|
|
|
Abstract The slabs produced by new No.3 castes at Baosteel are mainly used for heavy plates, the size of which is 220,250,300 mm×（12002300） mm with 2000 mm is a dominant one. Internal and surface quality of slabs is good, except some longitudinal cracks were observed in some cracksensitive peritectic slabs with the thickness of 220 mm. A kind of mold powder for cracksensitive heavy plate steel was developed, which has high basicity, high crystallization rate and low viscosity. High crystallization rate increases the heat resistance of slag film, which makes slab cool mildly in mold, so the longitudinalcrackrate of slab is decreased. Suitable lubrication can be obtained by use of low viscosity mold powder to ensure smooth casting process.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
LIU Ke, HAN Yi-hua, YANG Fan, ZHU Li-guang. Effect of MgO on microstructure of CaO-Al2O3 based quaternary system mold fluxes[J]. Iron and Steel, 2020, 55(5): 52-58. |
| [2] |
ZHENG Zhong, WANG Yong-zhou, LU Yi, GAO Xiao-qiang. Intelligent optimization model and system of plate and slab design of medium steel plate[J]. Iron and Steel, 2020, 55(4): 53-59. |
| [3] |
zheng yuanshou. High speed production technology of 160 × 160mm2 continuous casting in SanGangsteel[J]. , 2020, 45(3): 0-0. |
| [4] |
. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0. |
| [5] |
AI Ke-nan, ZHANG Pan-pan, ZHAO Meng-hao, LI Cheng-liang, ZHANG Zhi-ming, FU Jian-xun. Analysis of formation mechanism of surface crack of 1215 free-cutting steel during drawing[J]. Iron and Steel, 2020, 55(2): 88-94. |
| [6] |
YANG Jie1,YAO Hai-ming2,WU Zhen-gang1,GAO Qian-yun2. Clogging control of submerged entry nozzle during IF steelproduction by middle-thin slab process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(1): 20-26. |
|
|
|
|
2007, Vol. 42 