Study of Controlling Nitrogen Content of NBearing Stainless Steel During AOD Process |
LI Xuefeng1,2,LI Zhengbang2 |
1. Quallity Department, Taiyuan Iron and Steel (Group)Co., Taiyuan 030003, Shanxi, China; 2. Institute of Metallurgical Technology, Center Iron and Steel Research Institute, Beijing 100081, China |
|
|
Abstract The solution of nitrogen in molten stainless steel was studied thermodynamically and kinetically. The results showed that the solubility of nitrogen is increased with decreasing temperature and increasing Cr, Mn, Mo content. The theory and practice of nitrogen alloying model by blowing nitrogen into AOD were studied, and it was indicated that nitrogen content is changed with the changing of carbon content and temperature of molten,oxygen and argon gas flowing rate. The process is suitable to produce Nbearing stainless steel which nitrogen content value below 90% and to assure the accuracy of nitrogen content control, the nitrogen content should be below 80% of solubility under normal pressure.
|
Received: 01 January 1900
|
|
|
|
[1] |
BI Chuan-guang, HUANG Chun-chao, NING Xiao-jun, ZHANG Jian-liang, WANG Guang-wei, PENG Zheng-fu. Best ratio of semi-coke for blast furnace injection[J]. Iron and Steel, 2020, 55(6): 25-32. |
[2] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[3] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[4] |
ZENG Ze-yun, LI Chang-rong, LI Zhi-ying, LIU Zhan-lin,LI Zheng-song, ZHAI Yong-qiang. Thermodynamic analysis of titanium precipitation in HRB500E seismic steel[J]. Iron and Steel, 2020, 55(5): 45-51. |
[5] |
LIU Ke, HAN Yi-hua, YANG Fan, ZHU Li-guang. Effect of MgO on microstructure of CaO-Al2O3 based quaternary system mold fluxes[J]. Iron and Steel, 2020, 55(5): 52-58. |
[6] |
XIAO Shao-bin, WANG Wei, LIU Tian-yu, ZHANG Qin, LÜ Zhi-qing. Effects of vacancies and C atoms on mechanical properties of Fe grain boundary[J]. Iron and Steel, 2020, 55(4): 75-81. |
|
|
|
|