Effect of SlagMetal Reaction on Formation of Nonmetallic Inclusions of Lower Melting Temperature in High Strength Alloyed Structural Steel |
WANG Xinhua1,CHEN Bin2,JIANG Min1,WANG Wanjun1 |
1.School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2. Research Institute of Shougang, Beijing 100041, China |
|
|
Abstract If the nonmetallic inclusions in alloying steels are of low melting temperature, the fatigue life of steels can be significantly improved. A laboratory study was carried out to investigate the inter reaction between slag, metal and inclusions. It was found that the amount of the high melting temperature inclusions of MgOAl2O3 type decreased with increasing the slagmetal reaction time. Compared with using the slag containing about 20% Al2O3 and with a basicity of about 5, by using higher Al2O3 and higher basicity slag (Al2O3:41%, CaO/SiO2:6.5), the portion of CaOMgOAl2O3SiO2 inclusions could be increased from 24.4% to 81.7% and most of them were of low melting temperature (≤1500 ℃).
|
Received: 01 January 1900
|
|
|
|
[1] |
HOU Xin-mei, LIU Yun-song, WANG En-hui. Effect of ladle-lining refractory on non-metallic inclusions in steel[J]. Iron and Steel, 2020, 55(6): 15-24. |
[2] |
LI Lin, LI Ming-ming, LI Qiang, ZOU Zong-shu. Melt splashing behavior of steelmaking converter with nozzle-twisted lance[J]. Iron and Steel, 2020, 55(6): 54-60. |
[3] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[4] |
ZHAO Zhong-yu, ZHAO Jun-xue, TAN Ze-xin, QU Bo-qiao, LU Liang, CUI Ya-ru. Effect of heating rate and pre-melting process on melting point of fluorine-containing slag[J]. Iron and Steel, 2020, 55(6): 123-128. |
[5] |
HU Chang-qing, WANG Xiao-lei, SHI Xue-feng, WANG Zhi-xing, HAN Wei-gang. Effect of MgO and basicity on liquid phase formation of FeOx-SiO2-CaO-MgO-Al2O3 system[J]. Iron and Steel, 2020, 55(4): 27-33. |
[6] |
LIU Zhen-tong, YANG Wen, REN Ying, ZHANG Li-feng, WANG Wei-jian. Analysis of influencing factors on effect of calcium treatment in Al-killed steels[J]. Iron and Steel, 2020, 55(3): 29-34. |
|
|
|
|