| Hydrogen Content Control and Improvement of Central Carbon Segregation of Slab |
| ZHU Zhiyuan1,NING Linxin1,WANG Guolian2 |
| 1. Research Institute of Technology, Shougang Group, Beijing 100041, China; 2. No.2 Steelmaking Plant, Shougang Group, Beijing 100041, China |
|
|
|
|
Abstract The change of hydrogen content during steelmaking process was investigated firstly. It was found that hydrogen content in liquid steel is rapidly increased in LF process. In the slab, the negative carbon segregation region and positive segregation in the center are observed simultaneously. By using simplified diffusion equation, the element diffusion model was built for 12slab stack cooling process. The surface temperature of each slab was measured at different stack cooling time. Applying the measured temperature to the model, carbon and hydrogen diffusion results were calculated. Using these results, it can be concluded that slab stack cooling can promote the diffusion of hydrogen, but weakly affect central carbon segregation. Increasing the temperature and holding time of reheating, central carbon segregation can be improved a great deal.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
ZHENG Zhong, WANG Yong-zhou, LU Yi, GAO Xiao-qiang. Intelligent optimization model and system of plate and slab design of medium steel plate[J]. Iron and Steel, 2020, 55(4): 53-59. |
| [2] |
chishirong chishirongchishirong. [J]. , 2020, 45(3): 0-0. |
| [3] |
. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0. |
| [4] |
Gan-Shui ZHOU. Diagnosis of instability during trial production of the billet continuous casting in a steel factory in Vietnam[J]. , 2020, 45(2): 0-0. |
| [5] |
LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22. |
| [6] |
ZHANG Si-yuan1,2,LONG Mu-jun1,2,AI Song-yuan1,2,TAN Kai1,2,CHEN Deng-fu1,2,HUANG Yun-wei1,2. Oxidation behavior of continuous casting slabs and its effect on temperature during cooling process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 129-134. |
|
|
|
|
2006, Vol. 41 