Microstructure and PostTreatment of M2 High Speed Steel Cast Strip |
DING Peidao,ZHANG Caidong,JIANG Bin,ZHOU Shouze |
College of Materials Science & Engineering, Chongqing University, Chongqing 400044, China |
|
|
Abstract The solidification microstructure of M2 high speed steel produced by different technologies and the evolution of carbide in industrial cast strip processed by different heat treatment and hot deformation were investigated. The solidification rate and the average thickness of eutectic carbide net were measured. The transmission electron microscopy was adopted to study the influence of subsequent heat treatment and hot deformation on the carbide phase. The effect of different technologies and post processing on the microstructure was analyzed by quantitative metallographic analysis. The results show that application of the twinroll strip casting technology can refine the dendrite of solidification microstructure, reduce the thickness of eutectic carbide net and improve the carbide distribution in M2 high speed steel. The carbide morphology could be optimized by subsequent heat treatment and hot deformation. It is suggested that both heat treatment and hot deformation should be adopted to improve the M2 cast strip microstructure.
|
Received: 01 January 1900
|
|
|
|
[1] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[2] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
[3] |
TIAN Ya-qiang1,BI Wen-qiang1,PAN Hong-bo2,LI Hong-bin1,ZHENG Xiao-ping1,CHEN Lian-sheng1. Effect of carbide evolution on Lüders behavior of cold rolled ART 0.1C-7Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 505-511. |
[4] |
FENG Lu-lu1,2,HU Feng1,QIAO Wen-wei3,LU Xiu-yu4,ZHANG Guo-hong5. Microstructure and properties of 150mm ultra heavy 07MnCrMoVR hydropower steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 400-405. |
[5] |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
[6] |
. Study on NbC Precipitate of Nb Microalloying Mid-carbon Steel[J]. , 2020, 45(3): 0-0. |
|
|
|
|