Investigation on RHTB Vacuum Decarburization for IF Steel |
ZHANG Jingang1,2,LI Degang2,YU Gongli2,WEN Tieguang2,HUANG Yuping2 |
1. School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China; 2. Anshan Iron and Steel Group Co., Anshan 114001, Liaoning, China |
|
|
Abstract For super low carbon IF Steel, the RHTB vacuum treatment, was investigated. The effect of initial molten steel conditions and suitable methods for molten steel with different initial conditions were studied by natural decarbonization and forced decarbonization processes. The results showed that the optimum initial composition is as followings: w(C)=0.030%0.040%, a[O]=0.050%0.070%, t=15901610 ℃. The final composition of w(C)≤0.0025%, w(TO)≤0.0025%, can be stably obtained after RHTB treatment. The test result was proved in production.
|
Received: 01 January 1900
|
|
|
|
[1] |
YU Hui-xiang, PAN Ming, YANG De-xin. Behavior of inclusions in ultra-low carbon IF steel during deoxidation and alloying process[J]. Iron and Steel, 2020, 55(6): 46-53. |
[2] |
ZHU Tan-hua, ZHOU Qiu-yue, REN Ying, DUAN Hao-jian, ZHANG Li-feng. Inclusion evolution in IF steel during tundish reoxidation[J]. Iron and Steel, 2020, 55(3): 35-39. |
[3] |
YANG Jie1,YAO Hai-ming2,WU Zhen-gang1,GAO Qian-yun2. Clogging control of submerged entry nozzle during IF steelproduction by middle-thin slab process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(1): 20-26. |
[4] |
XIAO Pengcheng,ZHAO Maoguo,ZHU Liguang,HE Shengping. Mathematical simulation and experiment on #br# solidification hook of IF steel[J]. Iron and Steel, 2019, 54(7): 49-55. |
[5] |
LIU Lan-xiao,CHEN Ling-feng,GUAN Jian-dong,WU Nai,ZHOU Na,LIU Juan. Analysis of cross striation on the surface of IFsteel[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(5): 51-55. |
[6] |
ZHU Rui-qi,SONG Xin-li,ZHENG Ai-qin,CHEN Rong-dong,JIA Juan,FAN Li-xia. Strain hardening and microstructure characteristic of high strength IF bearing phosphorus steel[J]. Iron and Steel, 2018, 53(2): 55-59. |
|
|
|
|