Effect of Magnesia addition on Sinter Reducibility |
|
|
|
Abstract In this paper, the influence of MgO on sinter reducibility has been studied and analyzed through determining the reduction rate of sinter at different temperature and chemical composition via thermogravimetric analysis combining microstrcture of sinter. The study has shown that MgO has different rules on sinter reducibility at 850℃ and 1220℃, i.e.,it promotes reducibility of sinter at 850℃ and restrains sinter reduction at 1220℃. At the meanwhile, the effects of SiO2 and basicity on reducibility are effected by MgO, i.e., enhancement of basicity is inclined to reducibility, and the enhancing SiO2 content has adeverse effect on sinter reducibility, but both of which are weakend with the addition of MgO and Al2O3.
Keywords: calcium ferrite MgO reducibility
|
Received: 27 October 2008
|
|
|
|
[1] |
Xin Jiang, Huai‑yu Zhang, Hai‑yan Zheng, Qiang‑jian Gao, Feng‑man Shen. Three-segment control theory of MgO/Al2O3 ratio based on viscosity experiments and phase diagram analyses at 1500 °C[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(6): 624-630. |
[2] |
LIU Ke, HAN Yi-hua, YANG Fan, ZHU Li-guang. Effect of MgO on microstructure of CaO-Al2O3 based quaternary system mold fluxes[J]. Iron and Steel, 2020, 55(5): 52-58. |
[3] |
HU Chang-qing, WANG Xiao-lei, SHI Xue-feng, WANG Zhi-xing, HAN Wei-gang. Effect of MgO and basicity on liquid phase formation of FeOx-SiO2-CaO-MgO-Al2O3 system[J]. Iron and Steel, 2020, 55(4): 27-33. |
[4] |
FAN Cheng-wei,JIA Juan,HUANG Xian-bo,CHENG Zhao-yang,SONG Xin-li. Effect of MgO coating on texture and inhibitor of Hi-B steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 234-241. |
[5] |
HU Chang-qing,WANG Xiao-lei,SHI Xue-feng,WANG Zhi-xing,HAN Wei-gang. Effect of alkalinity and MgO content on mineral composition and microstructure of FeOx-SiO2-CaO-MgO-Al2O3 system[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 103-110. |
[6] |
YANG Nan,GUO Xing-min. Effect of SiO2 on composition and microstructure of crystal products of CaOFe2O3 melt[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 712-717. |
|
|
|
|