Development and Application of Slag Forming Agent for Steelmaking With SemiSteel |
BAI Ruiguo,ZHOU Xueyu,WENG Yujuan,XU Lishan,GAO Hai |
Steelmaking Plant, Chengde Xinxin Vanadium and Titanium Co., Ltd., Chengde 067002, Hebei, China |
|
|
Abstract During semisteel smelting process, less silicon,manganese are oxidized making.Slag formation difficult.A study was carried out to find suitable technology,which can reduce slag amount,give a new slag system of high metallurgical effect.Thus three slag forming.They set down three agents were tested.The results showed,that all three agents are satisfactory in terms of slag formation time,operation of blowing,consumption of slag forming agents dephosphorization.In this way, the metallurgical effect of slag can be increased by adding such agents to obtain slag with reasonable basicity,low FeO content.
|
Received: 01 January 1900
|
|
|
|
[1] |
LI Lin, LI Ming-ming, LI Qiang, ZOU Zong-shu. Melt splashing behavior of steelmaking converter with nozzle-twisted lance[J]. Iron and Steel, 2020, 55(6): 54-60. |
[2] |
YANG Li-bin, ZENG Jia-qing, DENG Yong, XU Xiao-wei, WU Li-ping. Highly efficiency and long-life combined blowing technology of big converter[J]. Iron and Steel, 2020, 55(4): 45-52. |
[3] |
DONG Wen-liang, PAN Hong-wei, LUO Lei, JI Chen-xi, LI Hai-bo, TIAN Zhi-hong. Phosphorous distribution in dephosphorization slag[J]. Iron and Steel, 2020, 55(2): 75-81. |
[4] |
ZHOU Zhenyu, TANG Ping, ZHOU Zunchuan, HOU Zibing, WEN Guanghua. Optimization on nozzle parameters of 200 t combined blowing vanadium extraction converter[J]. Iron and Steel, 2019, 54(9): 50-56. |
[5] |
WANG Linzhu,BAO Yanping,LI Xiang. Comparison of twostage dephosphorization during remaining #br# slagdouble slag process in converter[J]. Iron and Steel, 2019, 54(8): 37-42. |
[6] |
HUANG Bing,ZHU Ming-mei,ZHONG Yong,ZHANG Ai-ping,WANG Yu. Thermodynamic calculation of phase composition of CaOSiO2FeOCr2O3MgOMnO slag system[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 718-725. |
|
|
|
|