Study of Rolled Plate Surface Edge Crack on Microalloy Steel |
XU Zhen |
|
|
|
Abstract Linearity crack sometimes appears on microalloy steel plate surface about 100mm from edge in “ingot casting + bloom rolling”,which is regularly deep or shallow,and
conduces so much waste product that affects normal production.These have been thought of rolling fault,but this text judges them coming from steel ingot surface microcrack based on macro-scopical shape and micro-structure research. Microalloy steel plate will craze at the most pull-stress position,which provides theoretical foundation for product quality improvement.These fault has greatly reduced after we adopt effective technique measure.
|
Received: 25 November 2009
|
|
|
|
[1] |
SHAO Chun-juan,ZHEN Fan,ZHANG Ji-ming,QU Jin-bo,ZHANG Lei. Effect of sample thinning on DWTT property of heavy wall X80 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 497-504. |
[2] |
CHEN Ming-xin1,YANG Xiao-jiang2,MENG Qing-yong2. Study on high temperature thermoplasticity of medium manganese steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 519-524. |
[3] |
SUN Ming-han, ZHU Zhi-wang, ZHENG Li-kang, ZHENG Chuan-xing, DU Feng-shan. Mechanism of oblique edge crack formation of cast-rolling strip[J]. Iron and Steel, 2020, 55(4): 60-67. |
[4] |
Danny Wei. [J]. , 2020, 45(3): 0-0. |
[5] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
[6] |
ZHOU Ren-yuan, ZHU Li-hui, LI Shi-xian, ZHAI Guo-li. Improvement of reheat-cracking susceptibility and microstructure of T23 steel[J]. Iron and Steel, 2020, 55(3): 80-86. |
|
|
|
|