Thermodynamic Study on Boron and Iron Separation From Low Grade Paigeite |
CAI Haitao,ZHANG Jianliang |
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract The thermodynamic analysis on iron and boron separation from low grade paigeite was based on carbothermic method. The results indicate that boron and iron could be separated by selective reduction at less than 1500 ℃ and oxide impurities in ore had no influence on it. According a chemical equivalent of C/O = 1 to blend carbon,an experiment was performed. The results indicate that boron and iron could not separated on sufficiently at a temperature less than 1200 ℃ because of ore inset distribution. If roasting temperature was too high then energy consumption was increased without improvement in iron and boron concentrate grade. Therefore the best roasting temperature range was 12001350 ℃ and iron and boron concentrate grade can reach to more than 80% and 12% respectively. The comprehensive utilization of low grade paigeite can be realized.
|
Received: 01 January 1900
|
|
|
|
[1] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[2] |
ZENG Ze-yun, LI Chang-rong, LI Zhi-ying, LIU Zhan-lin,LI Zheng-song, ZHAI Yong-qiang. Thermodynamic analysis of titanium precipitation in HRB500E seismic steel[J]. Iron and Steel, 2020, 55(5): 45-51. |
[3] |
WANG Feng1,XIANG Jia-fa2,GUO Yu-feng1,ZHENG Fu-qiang1. Research progress of sintering optimization ore blending method based on basic process performance of iron ore[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 89-95. |
[4] |
XING Xiang-dong1,2,WANG Sha1,ZHANG Qiu-li1,2,CHEN Yun-fei3,WANG Chun-guang4,CHEN Gui-he4. High temperature carbothermal reduction mechanism of South Africa chromite[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 96-102. |
[5] |
LIN Jie, YANG Cheng, WANG Yuanming, MOU Fenyun, HOU Dong, WANG Deyong. Deoxidation thermodynamics in electroslag remelting process[J]. Iron and Steel, 2019, 54(9): 44-49. |
[6] |
WANG Linzhu,BAO Yanping,LI Xiang. Comparison of twostage dephosphorization during remaining #br# slagdouble slag process in converter[J]. Iron and Steel, 2019, 54(8): 37-42. |
|
|
|
|