Dehydration and Sintering Mechanism of Indonesian Nickeliferous Laterite |
L Xuewei1,2,BAI Chenguang1,ZHANG Lifeng2,QIU Guibao1,HU Tu1,XIE Hao1 |
1.College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China; 2. Department of Materials Science and Engineering, Missouri University of Science and Technology, Rolla 65401, USA |
|
|
Abstract The chemical analysis, as well as thermogravimetric, differential thermal analysis and Xray diffraction analysis were firstly carried out for Indonesian nickeliferous laterite to understand the drying and sintering mechanism. The dehydration of laterite could be divided into steps of removing free water, crystal water and hydroxyl group at different temperature. The sintering experiment of laterite with different carbon content were carried out, and the effect of carbon content on sintering velocity, agglomeration ratio, mass loss, temperatures of off gas and yield was studied. The Xray diffraction and SEM results showed that pyroxene ((Mg,Fe)SiO3) and magnesiowustite (Mg(Ni)Fe2O4) were the main adhesives in the sinter.
|
Received: 01 January 1900
|
|
|
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
ZHU De-qing1,TIAN Hong-yu1,PAN Jian1,LIAO Hui2,GUO Zheng-qi1,XUE Yu-xiao1. Comprehensive utilization status and progress of low-grade laterite nickel ore[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 351-362. |
[3] |
ZHOU Ming-shun, WANG Yi-dong, ZHAO Dong-ming, HAN Hong-liang,LI Xian-chun, LU Li-ming. Development on sintering technologies with high proportion of magnetite concentrates[J]. Iron and Steel, 2020, 55(5): 1-9. |
[4] |
HE Zhan-wei, XUE Xiang-xin. Basic sintering characteristics of several typical vanadium titanium magnetite[J]. Iron and Steel, 2020, 55(5): 20-25. |
[5] |
ZHANG Wei-li, WU Sheng-li, HU Zhong-jie. Analysis of affecting factors of activated coke denitrationefficiency for sintering flue gas[J]. Iron and Steel, 2020, 55(5): 109-115. |
[6] |
ZHANG Wei-li1,WU Sheng-li1,HU Zhong-jie1,2. Statistical analysis of factors affecting desulfurization rate of activated coke for sintering flue gas[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 281-288. |
|
|
|
|