| Analysis of Quenching Residual Stress of P110 Oil Casing by Incremental Hole Drilling Method |
| Li Ya-xin |
| |
|
|
|
|
Abstract In order to reduce the thermal stress and structural stress of P110 oil casing in the process of quench cooling, water quenching+air cooling+water quenching was proposed. The residual stresses of direct quenching and water quenching+air cooling+water quenching were determined by incremental hole drilling method and the residual stresses of two processes on crack formation and propagation was analysed. The results show that under the direct quenching the tangential and axial residual tensile stress are 229~281MPa and 191~237MPa. Under the water quenching+air cooling+water quenching process, the tangential residual stress is compressive stress at -422~-185MPa and the axial residual tensile stress is 90~190MPa. Compared to the direct quenching process, the tangential and axial stresses of proposed cooling methods are both decreased, then the microcrack formation and propagation is relieved.
|
|
Received: 22 September 2009
|
|
|
|
| [1] |
LI Bo, YANG Fei-fei, LIU Hua-song, LUO Ming, ZHANG Zhong-hua, ZHANG Jia-quan. Effect of solidification structure on banded defects of high strength corrosion resistant tubes[J]. Iron and Steel, 2020, 55(3): 87-95. |
| [2] |
LI Rong-feng，XU Liang，ZHANG Shu-yan. Application of the high speed drilling method of residual stress on thick wall pipeline steel pipe[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(6): 1-5. |
| [3] |
CUI Jin-xing1， HAN Shi-chao2， SUN Jian-liang1， PENG Yan1. Evolution characteristics of residual stresses in medium-thick plate during thinning process[J]. Iron and Steel, 2019, 54(5): 39-46. |
| [4] |
. [J]. , 2019, 44(3): 0-0. |
| [5] |
SUN Jian-liang1，2， LI Kai1， DU Xing-ming1， PENG Yan1，2. Straightening process of longitude profiled plate based on matching straightening roller system[J]. Iron and Steel, 2019, 54(3): 47-55,62. |
| [6] |
XIONG Mao-xian， YANG Sha-sha， XIE Jun-feng， JI Bing-yin， MA Lei， SHI Jiao-qi. Discussion about correlation between blind-hole technology and the ring method in testing residual-stress of oil casing[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(3): 33-35. |
|
|
|
|
2010, Vol. 45 