Investigation of hot compression on 403Nb blade steel |
Zheng-Dong LIU YANG Gang |
|
|
|
Abstract In order to provide dates for realizing the structure and property prediction system of 403Nb blade steel hot tandem rolling, the hot compression was carried out using the Gleeble-3500. According to the experimental dates, the parameter Z and flow stress equation were worked out respectively: ,σP=14.5926ln +1002406.111•T-1-604.613658. The analysis of the structure shows that the 403Nb dynamic recrystallization forms the nuclear under the bulging mechanism. There are a few thin twins with width 30~100nm. The NbC particles in the matrix can stick the dislocations, which improves the hot deformation activation energy.
|
Received: 12 June 2009
|
|
|
|
[1] |
HU Xiao,BAO Si- qian,CAI Zhen,,ZHAO Gang,LIU Bing- bing,KE Shan- shan. Deformation induced pearlite transformation and dynamic spheroidization in a eutectoid steel[J]. , 2018, 30(8): 657-665. |
[2] |
WANG Qing- juan,LI Xiang- jun,REN Yao- jia,ZHOU Hai- xiong. Effect of initial state on hot deformation behavior of 65 wire rod[J]. , 2018, 30(12): 998-1005. |
[3] |
FAN Ming- qiang,,MAO Lei,,ZHANG Yun- fei,TIAN Zhi- qiang,SUN Zhong- hua,QIN Sen. Effects of temperature rise on deformation behavior and microstructure of H13 steel during high temperature compression process[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 756-761. |
[4] |
ZHANG Shi-wei,,,YANG Ming,,,LIANG Yi-long,,,JIANG Yun,,LONG Shao-lei,,. Constitutive equations and dynamic recrystallization behaviors of 20CrNi2Mo steel at stage of high temperature deformation[J]. Iron and Steel, 2017, 52(8): 97-105. |
[5] |
LIU Zi- long,WANG Zhi- meng,XING Peng- da,CAO Wen- quan,PENG Yan,WANG Yu- hui. Static recrystallization behavior of GCr15 bearing steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 671-677. |
[6] |
GONG?Qian-jiang,,,,LIANG?Yi-long,,, ,YANG?Ming,,,, JIANG Yun,,,,XU?Xiang,,,. Physical model and 3D thermal processing map of hot deformation of 20CrMnTiH steel[J]. Iron and Steel, 2017, 52(7): 76-83. |
|
|
|
|