Experimental Research of Hot Metal Predephosphorizing With Premelted Dephosphorizer |
WEI Yingjuan1,YUAN Shouqian1,ZHANG Xifeng1, WANG Wei1,LIANG Dean2,ZHANG Qiye2 |
1.The School of Metallurgical Engineering, Xi’an University of Architecture and Technology, Xi’an 710055, Shaanxi, China;2. Jiaozuo Zhende Refractory Co., Ltd., Jiaozuo 454001,Henan, China |
|
|
Abstract With CaOFe2O3CaF2 system slag as dephosphorizer,the influencing factors of such premelted dephosphorizer,composition,addition rate, treating temperature, initial phosphors content in hot metal and granularity of premelted slag was studied in laboratory. As a result, at 1350 ℃ and with a ratio of w(CaO)/w(Fe2O3) about 1.0,adding 10% premelted dephosphorizer could lower the phosphorus content in hot metal to 0.0079% with a dephosphorization rate of 96.24%. The dephosphorization rate was not affected by initial phosphorus content in hot metal and granularity of premelted slag.
|
Received: 01 January 1900
|
|
|
|
[1] |
ZHANG Jian-liang, SUN Min-min, LI Ke-jiang, LI Hong-tao. Present situation and prospect of dissolution behavior of metallurgical coke in blast furnace hot metal[J]. Iron and Steel, 2020, 55(4): 1-11. |
[2] |
YANG Li-bin, ZENG Jia-qing, DENG Yong, XU Xiao-wei, WU Li-ping. Highly efficiency and long-life combined blowing technology of big converter[J]. Iron and Steel, 2020, 55(4): 45-52. |
[3] |
ZHAO Dong,ZHANG Jing,LUO Guo-ping,CHEN Yan-biao,ZHANG Xiang. Effect of SiO2 and Na2CO3 addition on gasification dephosphorization during prereduction and sintering of iron concentrate[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 204-211. |
[4] |
DONG Wen-liang, PAN Hong-wei, LUO Lei, JI Chen-xi, LI Hai-bo, TIAN Zhi-hong. Phosphorous distribution in dephosphorization slag[J]. Iron and Steel, 2020, 55(2): 75-81. |
[5] |
CHEN Wen1,LEI Ying2,HE Wen-hao3,LIAO Zhen-hong1,WANG Xin2. Iron increase and phosphorous reduction mechanism of oolitic hematite by microwave heating[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(1): 9-19. |
[6] |
ZHANG Jian. Quantitative analysis of hot metal composition and TiO2 load #br# for effective furnace maintenance in Shougang Jingtang[J]. Iron and Steel, 2019, 54(9): 39-43. |
|
|
|
|