梅钢中磷铁水低磷钢冶炼问题的探讨

Abstract
Figure/Table
References
Related Citation (7)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract As phosphorus content in hot metal is high at Meishan, it is difficult to produce low phosphorus steel. Through analyzing the dephosphorization methods including the dephosphorization pretreatment of hot metal, SRP and the double slag technique,a new method of dephosphorization in one converter was proposed and tested.The steel of phosphorus content less than 0.01% through slag forming in early period and deslagging in the middle could be produced.

Key words： TBM combined blowing dephosphorization rate medium phosphorus hot metal lowphosphorus steel

Received: 01 January 1900

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	TANG Hongle
	WANG Hongfeng
	SUN Xiaohui

Cite this article:

TANG Hongle,WANG Hongfeng,SUN Xiaohui. Study on Production of Low Phosphorus Steel From Medium Phosphorus Hot Metal at Meishan Steel[J]. Iron and Steel, 2008, 43(10): 34-0.

URL:

http://www.chinamet.cn/Jweb_gt/EN/ OR http://www.chinamet.cn/Jweb_gt/EN/Y2008/V43/I10/34

[1]	ZHAO Bin，WU Wei，WU Wei，WANG Chengyi，CUI Huaizhou. Application of top blowing oxygen and powder injection #br# stirring process for hot metal dephosphorization[J]. Iron and Steel, 2019, 54(11): 33-39.
[2]	WANG Peng，WU Wei，MENG Hua-dong，YIN Chuan-lei ，LI Xiang-chen. Process optimization for improving hit rate of BOF end-point temperature in Huaigang Works[J]. Iron and Steel, 2018, 53(3): 96-103.
[3]	ZHAO Hai-quan，，QI Yuan-hong，SHI Yong-lin，FENG Huan-lin，NA Xian-zhao. Mechanism and experimental for dephosphorizion and chromium conservation of chromium containing melted iron[J]. Iron and Steel, 2017, 52(12): 16-20.
[4]	Lü Yan-chun，，，WANG Xin-hua，QIN Deng-ping，，WANG Hai-bao，. Enrichment and influencing factors of phosphorus in slag of converter steelmaking[J]. Iron and Steel, 2017, 52(10): 29-37.
[5]	TANG Ping，LI Jing-xiang，ZHOU Hai，PENG Qing-liang，LIU Bing-yu，LI Ju-zhong. Fundamental and application of converter fluxing agent based on ladle casting residue for dephosphorization[J]. Iron and Steel, 2016, 51(3): 84-88.
[6]	LIAO Peng,HOU Ze-wang,QIN Zhe,ZHANG Xing-zhong,QIU Sheng-tao. Experimental Study of Double Slag Combined-Blowing Converter Blowing Dephosphorization Process[J]. Iron and Steel, 2013, 48(1): 30-36.