Study on Microstructure and Properties of HighMartensite DualPhase Steel |
LUO Juanjuan,SHI Wen,HUANG Qunfei,LI Lin |
Shanghai University Material Science and Engineering College, Shanghai 200072, China |
|
|
Abstract The microstructure, tensile properties as well as fracture mechanism of highmartensite content dualphase steel were studied by OM,SEM and tension test. Results show that with the increase of intercritical quenching temperature in (α+γ) range, the volume fraction of martensite continuously rises, enhanceing the strength of the steel. In addition,the volume fraction of martensite exhibits a certain influence on transformsation from ductile to brittle fracture. Finally, microscopic holes are formed near the fracture surface,the morphology of which is changed with the increase of volume fraction of martensite.
|
Received: 01 January 1900
|
|
|
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
SUN Chao-fan, FANG Yuan, WANG Ya-qing, LIU Wei. Influence of temper rolling reduction rate on microstructure and mechanical properties of TS290 steel[J]. Iron and Steel, 2020, 55(6): 75-79. |
[3] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[4] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[5] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
[6] |
SHAO Chun-juan,ZHEN Fan,ZHANG Ji-ming,QU Jin-bo,ZHANG Lei. Effect of sample thinning on DWTT property of heavy wall X80 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 497-504. |
|
|
|
|