| Insitu Surface Oxidation of 00Cr25Ni7Mo3.5N Supper Duplex Stainless Steel |
| ZANG Huaxun1,LI Jun1,XIAO Xueshan1,ZHAO Junliang2,JIANG Laizhu2 |
| 1. Institution of Materials, Shanghai University, Shanghai 200072, China; 2. Baoshan Iron and Steel Co., Ltd., Shanghai 201900, China |
|
|
|
|
Abstract Insitu surface oxidation of 00Cr25Ni7Mo3.5N supper duplex stainless steel was studied by high temperature XRD. The samples were continually heated in the air and tested at several temperature. The growth of surface oxide was investigated and precipitation of secondphase was investigated. The results showed that the surface layer was only composed of α phase and γ phases below 600 ℃,α was oxidized to αFe2O3 at about 800 ℃, then to αFe2O3+Fe3O4 at about 900 ℃,and disappeared completely up to 1000 ℃. However, γ was not oxidized even at up to 1100 ℃. The microstructure of the samples quenched from various temperatures were of α and γ, and the fraction of α phase was gradually increased with the temperature. In addition, σ phase in surface layer and interior of quenched samples was almost precipitated and dissolved simultaneously during heating.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
MA Xiao-cong, AN Zi-jun, CHEN Lei, MEI Rui-xue, HAO Shuo, PENG Cheng. Influence of loading direction on tensile properties of a TRIP-assisted duplex stainless steel sheet[J]. Iron and Steel, 2020, 55(2): 112-118. |
| [2] |
WANG Guo-fu， YU Hai-feng. Discussion about on-line pickling technology of medium plate of special metal and alloy[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 18-. |
| [3] |
YANG Ji-chun, WANG Jun, REN Lei, FU Xiao-yang, LIU Xiang-jun, ZHANG Ze-ning. Effect of Ce on microstructure and impact propertiesof S32550 duplex stainless steel[J]. Iron and Steel, 2020, 55(1): 86-92. |
| [4] |
GAO Xiangming1，PEI Mingde1，2，LI Guoping1，2. Influence of cold rolling on precipitation of S32750 super duplex stainless steel[J]. Iron and Steel, 2019, 54(9): 94-98. |
| [5] |
CHEN Xingrun, CHENG Guoguang, HUI Kai, PAN Jixiang, LI Jingyu. Formation mechanism of inclusions in 2205 duplex stainless steel during continuous casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(5): 452-459. |
| [6] |
YAN Chun-guang1,CHEN Sheng-hu2,LI Ya-ping1,XU Hai-tao1. Influence of hydrogen on tension property of 316H stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(11): 1004-1011. |
|
|
|
|
2008, Vol. 43 