Effect of Metallurgical Process on Morphology and Size Distribution of MnS Inclusions |
XIA Zhixin1,YE Bing2,YANG Zhuoyue1,SU Jie1 |
1. Institute for Structure Materials, Central Iron and steel Research Institute, Beijing 100081, China; 2. Technique center, Pangang Group Sichuan Changcheng Special Steel Co., Ltd., Jiangyou 621701, Sichuan, China |
|
|
Abstract The morphology and size distribution of inclusions in G50 steel produced by different metallurgy processes were analyzed by SEM, EDAX. Results indicated that in the G50 produced by VIM+VAR the size of MnS inclusions was slightly smaller and their aspect ratio,mean spacing were distinctly larger.There were much more fine inclusions concentrated locally. Size distribution and morphology of MnS in G50 produced by VIM +VAR were dispersed evenly due to higher calcium content in composite MnS inclusions, leading to poor deformability.
|
Received: 01 January 1900
|
|
|
|
[1] |
NIU Yan-long, LIU Qing-you, JIA Shu-jun, TONG Shuai, WANG Bing, REN Yi. Influence of microstructure and M/A island evolution on toughness of pipeline steel under controlled cooling process[J]. Iron and Steel, 2020, 55(6): 91-100. |
[2] |
GAN Gui-ping,YE Jiang,FAN Lei. Effect of tempering treatment on microstructure and low temperature toughness of a low carbon bainite steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 258-264. |
[3] |
DUAN He, SHAN Yi-yin, YANG Ke, SHI Xian-bo, YAN Wei, REN Yi. Experimental on process, microstructure and mechanical properties of X80 high strength pipeline steel for low temperature[J]. Iron and Steel, 2020, 55(2): 103-111. |
[4] |
YANG Ji-chun, WANG Jun, REN Lei, FU Xiao-yang, LIU Xiang-jun, ZHANG Ze-ning. Effect of Ce on microstructure and impact propertiesof S32550 duplex stainless steel[J]. Iron and Steel, 2020, 55(1): 86-92. |
[5] |
WANG Bingxing,ZHU Fuxian,WANG Chao,LOU Haonan,. Application of oxide metallurgy in high heat input welding steels[J]. Iron and Steel, 2019, 54(9): 12-21. |
[6] |
CHEN Hao1,2,XU Haifeng2,ZHOU Tianpeng1,2,CHEN Zejun1,. Effect of quenching and low temperature treatment on microstructure and properties of X30 CrMoN 15 1[J]. Iron and Steel, 2019, 54(9): 85-93. |
|
|
|
|