Study on Removal of Inclusions From Molten Steel by Blowing During LF Refining |
TANG Haiyan1,LI Jingshe1,WANG Jianbin1,SUN Kaiming1,2,WEN Desong1,2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. No.1 Steelmaking Plant, Tianjin Pipe Corporation Ltd., Tianjin 300301, China |
|
|
Abstract Based on the water model experimental results, 150 t ladle argon blowing process at No.1 Steelmaking Plant, Tianjin Pipe Corporation Ltd. was improved. Analytical techniques such as tracers, metallographic examination, electrolysis, SEM and EDS were applied to compare the effect of inclusion removal for casing steel treated by two different argon blowing processes during LF refining. The results show that the reduction rate of total oxygen,with microinclusions and largesized inclusions was 35.42%, 59.85% and 93.43% respectively after ladle refining before improvement.The corresponding values of improved process were 44.31%, 64.29% and 95.88%.
|
Received: 01 January 1900
|
|
|
|
[1] |
HOU Xin-mei, LIU Yun-song, WANG En-hui. Effect of ladle-lining refractory on non-metallic inclusions in steel[J]. Iron and Steel, 2020, 55(6): 15-24. |
[2] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[3] |
CHU Yan-ping, CHEN Zhi-yong, LIU Nan, ZHANG Li-feng. Formation and control of spinel inclusions in high-speed heavy rail steel[J]. Iron and Steel, 2020, 55(1): 38-46. |
[4] |
LI Muming,YU Huixiang,PAN Ming,BAI Hao. Effect of refining slag on nonmetallic inclusions in #br# high manganese steel[J]. Iron and Steel, 2019, 54(6): 37-42. |
[5] |
ZHANG Qing-song, MIN Yi, XU Hai-sheng, XU Jiu-jian, LIU Cheng-jun. Effect of magnesium treatment on formation and evolution of inclusion in Si-Mn deoxidized steel[J]. Iron and Steel, 2019, 54(4): 37-42. |
[6] |
WANG Linzhu1,LI Junqi1,YANG Shufeng2,CHEN Chaoyi1,JIN Huixin1. Effect of calcium treatment on characteristics of nonmetallic #br#
inclusions in steel containing high Al[J]. Iron and Steel, 2019, 54(11): 27-32. |
|
|
|
|