Parameter Determination and Effects on Center Segregation of FEMS |
WANG Biao1,XIE Zhi1,JIA Guanglin1,LIN Guoqiang2,JI Zhenping1 |
1. Northeastern University, Shenyang 110004, Liaoning, China; 2. Nanjing Iron and Steel Co., Ltd., Nanjing 210035, Jiangsu, China |
|
|
Abstract The thickness of solidified shell of strand in secondary cooling zone was first calculated with mathematics model and then confirmed with pinshooting in EAF Steelmaking Plant of Nanjing Iron and Steel Co., Ltd.. The position of crater end 35~55 mm in diameter was found by calculation with modified mathematical model and pinshooting for given casting speed and steel grades and after that the FEMS was fixed at 8 m from meniscus. The optimal parameters for electromagnetic stirring were determined by teslameter:550 A and 13 Hz.The chemical composition at crater and of billets cast with and without FEMS was analysed. The results showed that the carbon and center segregation coeffient of billet cast with FEMS was decreased from 1.09% to 1.01% and the peak sulphur content in center was reduced obviously. The electromagnetic stirring parameters are suitable.
|
Received: 01 January 1900
|
|
|
|
[1] |
WANG Xing-yu, HAN Yan-shen, LIU Qing, XIAO Dong,CHEN Jun, GUAN Min. Effect of F-EMS on inner quality of spring steel continuous casting billet[J]. Iron and Steel, 2020, 55(5): 59-67. |
[2] |
. Formation reasons and control measures of abnormal oscillation marks for 10B21 cold-heading steel billets[J]. , 2020, 45(3): 0-0. |
[3] |
Gan-Shui ZHOU. Diagnosis of instability during trial production of the billet continuous casting in a steel factory in Vietnam[J]. , 2020, 45(2): 0-0. |
[4] |
XIE shizheng. Effect of roller EMS on macrostructure and properties of high strength steel[J]. , 2020, 45(1): 0-0. |
[5] |
WANG Pu,LI Shaoxiang,CHEN Lie,CHEN Xiqing,. Investigation of mold metallurgical behavior under #br# electromagnetic stirring for round bloom[J]. Iron and Steel, 2019, 54(8): 82-89. |
[6] |
ZHANG Jing,MA Liang,WU Huiping. Effect of nozzle structure on flow field and temperature field of #br#
medium low carbon steel in continuous casting[J]. Iron and Steel, 2019, 54(8): 116-123. |
|
|
|
|