Study on Sulphide Capacity of BF Slag Containing Alkali Metals |
XIE Haishen1,LI Fumin1,2,MA Mingxin2,L Qing2 |
1. School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China; 2. College of Metallurgy and Energy, Hebei Polytechnic University, Tangshan 063009, Hebei, China |
|
|
Abstract The sulphide capacity of B.F. slag containing alkali metals at 1500 ℃ was studied using gasslag equilibrium technique. The results reveal that, at fixed w(MgO), w(Al2O3) and w(K2O+Na2O), sulphide capacity increases with increasing of w(CaO)/w(SiO2) from 0.86 to 1.26; while w(MgO) increases from 5% to 18%, the sulphide capacity increases firstly, and decreases afterwards, it reaches its maximum when w(MgO) is about 8%; while w(Al2O3) increases from 12% to 18% at fixed w(CaO)/w(SiO2),and w(MgO), w(K2O+Na2O), the sulphide capacity increases first and decreases afterwards,reaches its maximum when Al2O3 content is about 13%; at constant w(Al2O3 )and w(MgO), when w(CaO)/w(SiO2) is 0.86,0.96,1.06 and 1.16, the sulphide capacity increases lightly with increasing of w(K2O+Na2O).
|
Received: 01 January 1900
|
|
|
|
[1] |
ZENG Zhi-hao1,ZOU Chong1,SHE Yuan1,2,YANG Jun1,MA Cheng1,HE Jiang-yong1. Effects of alkali metal enrichment on structure and gasification reactivity of blast furnace tuyere coke[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 452-461. |
[2] |
ZHOU Qi-qi1,LI Ji-peng1,2,CHENG Shu-sen1,LIU Kai1,LIU Zhao1. Application of IMCT model and KTH model in S50C steel desulfurization practice[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 297-303. |
[3] |
LÜ Xue-wei, YAN Zhi-ming, PANG Zheng-de, BAI Chen-guang, LIANG Dong, XIE Hao. Effect of Al2O3 on physicochemical properties and structure of blast furnace slag: review[J]. Iron and Steel, 2020, 55(2): 1-10. |
[4] |
ZHANG Jun, YAN Ding-liu, WAN Xin-yu, GAO Jian-jun. Comparative test on different dry granulation methods of blast furnace slag[J]. Iron and Steel, 2020, 55(2): 139-143. |
[5] |
LIU Zhe,WANG Yi-ci,ZHAO Feng-guang,LUO Guo-ping,ZHAO Bin. Influence of binary basicity on physical properties of blast furnace slag of Baogang Group[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 696-701. |
[6] |
YAO Jia-bin,LIU Weguo,JU Jiantao,XING Xiangdong,AN Jialiang. Study on desulphurization capacity of CaO-SiO2-MgO-Al2O3-BaO slag systems[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(3): 280-286. |
|
|
|
|