mm Thickness of X80 Plates Production for the Second WesttoEast Natural Gas Transmission Pipeline by Using OHTP |
NIE Wenjin,WANG Zhifu,LI Ran,LI Yucang,ZHANG Xiaobing |
Jiangsu Shagang Group, Zhangjiagang 215625, Jiangsu, China |
|
|
Abstract According to the technical requirements of X80 heavy thickness plates for the second westtoeast natural gas transmission pipeline project and the capability of steelmaking and plate mill of Shagang, a HTP chemical design of low carbon and high niobium was adopted and the OHTP of control rolling and cooling for plates was developed. A mass production of 22 mm thickness of X80 plate and manufacturing of LSAW JCOE pipes of 22 mm×1219 mm were carried out. The results show that the mechanical properties, DWTT properties at -15 ℃ of plates and the yield/tensile ratio of the pipes were significantly improved by comparing that of HTP X80 plates. The absorb energy of Charpy Vnotch impact test at -80 ℃ remains at its top platform above 270 J, the 50% FATT is below -100 ℃. At -30 ℃, the DWTT fracture shear area is 90%, and 85% DWTT value is at -34 ℃.
|
Received: 01 January 1900
|
|
|
|
[1] |
SUN Deng-yue, HOU Hai-tao, RU Wen-di, XU Shi-min. Design of multi-point flexible pressure straightening device for wide and heavy plates and calculation of reverse bending amount[J]. Iron and Steel, 2020, 55(6): 113-117. |
[2] |
RUAN Jin-hua,WANG Zhi-gang,ZHAO San-xing,LI You-rong,MENG Qing-da. Inhomogenous plastic deformation mechanism of wide and heavy plate during vertical rolling[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(7): 644-650. |
[3] |
HE Yu-ming,HU Bing,ZHOU Hong,WANG Qian,ZHANG Hui5. Development of corner crack control technology for continuous casting strand of wide-thick plate[J]. Iron and Steel, 2016, 51(7): 34-40. |
[4] |
WANG Chang,YU Yang,NIU Tao,WANG Lin,CHEN Jin. Growth mechanism of oxidized film of X80 pipeline steel at high temperature[J]. Chinese Journal of Iron and Steel, 2016, 28(5): 57-63. |
[5] |
L Ze- an,NI Hong- wei. Research of titanium alloy to improvement of precipitation of sulfide in X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2016, 28(2): 19-26. |
[6] |
behavior of X80 pipeline and its weld joint XIE Fei,XU Chang- hao,WANG Dan,WU Ming,WANG Hai- yan,XIE Hong- yu. Influence of temperature on electrochemical corrosion[J]. Iron and Steel, 2015, 50(8): 89-94. |
|
|
|
|