Effect of Cooling Process on Microstructure of Steel for Weld Bogie Frame of HighSpeed |
WANG Ning,DU Linxiu,WU Di,LIU Xianghua |
The State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning,China |
|
|
Abstract According to the property requirement to steel for weld bogie frame of highspeed train, a low carbon MnCu microalloyed steel was designed, and the continuous cooling transformation and effect of cooling process on the microstructure of this steel were studied in laboratory. It was found that proeutectoid ferrite and intermediate transformation products could be obtained at a cooling rate in range of 130 ℃/s. Cooling rate and coiling temperature have significant effect on refinement of final microstructure.By Accelerated cooling to 500600 ℃ followed by slow cooling, a fine microstructure of quasipolygonal ferrite, granular bainite and acicular ferrite could be formed. The yield strength of steel plate with such microstructure could reach 540 MPa, with a excellent plasticity and lowtemperature toughness.
|
Received: 01 January 1900
|
|
|
|
[1] |
LIANG Liang,XU De-qiang,LIU Xu-hui,LI Guo-cang,DENG Xiang-tao,HUANG Long. Effect of cooling process on microstructure and properties of low alloy abrasion resistance steel NM400[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(3): 1-6. |
[2] |
CUI Qing- ling,LI Jian- ping,LI Shi- yu,QIAO Chang- le. Microstructure evolution and crack formation of Zn based coating on 22MnB5 hot formed steel[J]. , 2019, 31(2): 227-232. |
[3] |
HAN Yi1,XIAO Yao1,MIN Xiangling2,YU Enlin1,LI Dalong1,GAO Ying3. Residual stress and microstructure evolution of high #br#
frequency welding of longitudinal pipe[J]. Iron and Steel, 2019, 54(11): 130-139. |
[4] |
HU Xiao,BAO Si- qian,CAI Zhen,,ZHAO Gang,LIU Bing- bing,KE Shan- shan. Deformation induced pearlite transformation and dynamic spheroidization in a eutectoid steel[J]. , 2018, 30(8): 657-665. |
[5] |
YU Zhi-chen,MI Zhen-li,GUO Jin,GONG Na,AN Ruo-wei. FEM analysis of stress state on microstructural evolution of low-temperature bainite[J]. Iron and Steel, 2018, 53(6): 76-84. |
[6] |
LIU Yan-lin. Effect of carbon partitioning behavior on microstructure in a kind of Fe-C-Si-Mn-Cr-Mo steel[J]. Iron and Steel, 2016, 51(4): 53-58. |
|
|
|
|