Effect of Prior Cold Rolling Deformation on Strengthening of Maraging Steel |
YANG Zhuoyue,SU Jie,CHEN Jiayan |
China Iron and Steel Research Institute Group, Beijing 100081, China |
|
|
Abstract The effect of cold rolling deformation prior to aging on the strengthening of a maraging steel was investigated. The results of experiments indicated that the net strength increment caused by aging at 510 ℃ for 3 h is almost constant, irrespective of percentage of reduction in thickness. Final strength can be expressed as σ=σ0+ΔσCR+ΔσAge,where σ0 is initial strength, and ΔσCR and ΔσAge are strengthening contribution due to cold working and aging respectively, and ΔσCR is only related to percentage of reduction in thickness. It was confirmed by electron diffraction analysis that the strengthening precipitates are Ni3(Ti,Mo) and Ni3Mo, regardless of percentage of reduction in thickness.
|
Received: 01 January 1900
|
|
|
|
[1] |
HE Ya-yuan,LI Li-wei,YIN Yun-yang,DENG Zhao-jun. Evolution of microstructure and properties of thickness section of wearresistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 512-518. |
[2] |
YANG Chen-xing1,2,WU Zhi-wei1,2,YANG Mao-sheng2,ZHAO Kun-yu1. Microstructure and mechanical properties of Ni-Cr bearing alloy in solution aging treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 242-252. |
[3] |
HUI Ya-jun, WU Ke-min, XU Ke-hao, XIAO Bao-liang, LINGHU Ke-zhi, LIU Kun. Development of 500 MPa grade high ductility square tube steel and its work hardening behavior[J]. Iron and Steel, 2020, 55(2): 131-138. |
[4] |
ZHOU Liu-tao, PAN Hong-bo, PAN Shuo, WU Jie-wen. Effect of annealing process on microstructure texture and mechanical properties of 0.025C-0.326Mn steel[J]. Iron and Steel, 2020, 55(1): 93-100. |
[5] |
YANG Geng-wei,LU Jia-wei,SUN Hui,FANG Zi-wei,ZHOU Yi-liao,YAO Nan. Microstructure, mechanical properties and phase transformation behavior of TiV microalloyed highstrength hotstrip steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 726-732. |
[6] |
GONG Zhihua,YAO Bin,WANG Liwei,HE Yudong,BAO Hansheng,YANG Gang. Effect of heat treatment process on microstructure and property of 2Cr11Mo1VNbN heatresistant steel[J]. Iron and Steel, 2019, 54(6): 56-62. |
|
|
|
|