8Cr4MoV Low Alloyed Forged Super-Deep Hardening Layer Cold Work Roll Trial-Manufacture and Application |
吴国胜 WU Guo-Sheng |
|
|
Abstract 8Cr4MoV low alloyed forged super-deep hardening layer cold work roll steels were studied in laboratory containing about 4%Cr, 0.8%C, and appending a little of N and Re in it individually or together. After smelt in 50 kg vacuum induction furnace primarily, then forged, quenched and tempered in turn, the steels′ mechanics performances, microstructures and hardenability by end quenching test were compared each other, the better was put into trial-manufacture of super-deep hardening layer cold work rolls of 1700㎜body length for 4 H tandem cold mill in Cold Strip Mills WISCO. With quenched by 50/250Hz induction hardening machine, the rolls had uniform hardness on the body surface, and proved their resistance to wear higher, having longer service life over 1.6 times of Cr2 conventional cold work roll, deeper hardening layer depth corresponding to Cr5 super-deep hardening layer cold work roll, and no spalling, better resistance to accident.
|
Received: 27 November 2009
|
|
|
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
CAO Yan-guang, LI Zhao-dong, DING Can-can, ZHANG Jin-wen, YONG Qi-long, GAO Jian-bing. Effect of niobium addition on hardenability of high-speed railway axle steel[J]. Iron and Steel, 2020, 55(6): 107-112. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
FAN Xiu-feng, YAN Yong-wang, LIU Su-xia, LUO Long, LI Xiao-wei, HUO Wen-xia. Discussion about CuO doping on microstructure and properties of Ni 0.4 Zn 0.6 Fe 2 O 4 ferrite[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 13-. |
[5] |
YANG Yu-dan,ZHAO Hong-shan,LIU Teng-shi,DONG Han. Microstructure and properties of new high-carbon martensitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 135-142. |
[6] |
LI Yu-feng1,2,TANG Xing-chang3,PAN Ji-xiang1,2,WANG Chang-bo1,2. Dynamic recrystallization behavior of 904L stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 159-165. |
|
|
|
|