Numerical Simulation for Effect of Width on Flow Field of Slab Continuous Casting Mould |
TANG De-chi1,FENG Jie2,LI Yong-lin1,ZHU Li-xin1 |
1. Shougang Research Institute of Technology, Beijing 100041, China 2. School of Materials Science and Engineering, Hebei University of Science and Technology, Shijiazhuang 050018, Hebei, China |
|
|
Abstract Slab continuous casting mould was calculated by software fluent 6.3, the effects of mould width on the flow field were investigated. It is concluded that: as for mould of 230mm thickness,as the increase of mould width, maximum horizontal velocity on the level liquid decreases, then approaches to a flat, maximum velocity perpendicular to level liquid and velocity of impact point on the narrow side decrease; when the mould width are 1400mm,1600mm and 2150mm, and the distance to the narrow side are 460mm,540mm and 750mm, horizontal velocity on the level liquid reach the maximum, the impact points on the narrow side are 370mm, 400mm and 460mm to the level liquid, and the velocity on the impact point are 5.2cm·s-1, 4.4cm·s-1 and 2.5cm·s-1.
|
Received: 02 December 2010
Published: 15 December 2011
|
|
|
|
[1] |
DAI Jing-xin1,DING Xue-yong1,XU Hai-fa2,LIU Cheng-hong1,JU Tian-hua1. Numerical simulation of conveying characteristics of dense phase pulverized coal in bend pipe[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 377-385. |
[2] |
ZOU Tao1,ZHAN Dong-ping1,ZHANG Hui-shu2,LI Da-liang3,HAN Jian-lin3,LIU Xi-feng3. Mathematical and physical experimental study on mould nozzle optimization in slab continuous casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 304-310. |
[3] |
. Formation reasons and control measures of abnormal oscillation marks for 10B21 cold-heading steel billets[J]. , 2020, 45(3): 0-0. |
[4] |
zheng yuanshou. High speed production technology of 160 × 160mm2 continuous casting in SanGangsteel[J]. , 2020, 45(3): 0-0. |
[5] |
Shuang-jiang Li. Numerical simulation of the effect of nozzle nodule on the behavior of molten steel in slab continuous casting mold[J]. , 2020, 45(3): 0-0. |
[6] |
suai. Reason and Control of Surface depression defect in Slab of Low-carbon Low-silicon Aluminum Killed Steel[J]. , 2020, 45(2): 0-0. |
|
|
|
|