Control Technology of the Transverse Cracks in 400mm Ultra-Thick Slabs |
ZHU Zhi-yuan,ZHEN Xin-gang,JIANG Hai-tao,LI Jing-guang,WANG Yu-long,BAI Zhan-lu |
Shouqin Metal Material Co., Ltd., Qinhuangdao 066000, Hebei, China |
|
|
Abstract Factors influencing transverse cracks such as compositions of liquid steel, casting powder, mold oscillation, SEN, secondary cooling, and so on, were investigated. The results show that the compositions of liquid steel and the mechanical properties in the low ductility region Ⅲ are the internal reasons which effect transverse cracks; Strong cooling in secondary cooling area and the straightening force are the external cause. Based on these reasons mentioned above, some effective countermeasures were proposed in 400mm ultra-thick slabs: the SEN with concave bottom, the thickness of liquid slag film keeps 8-13mm, soft cooling in secondary cooling area, the surface temperature of slabs in vertical segment keeps above 1100℃, the surface temperature in straighten segment keeps above 940℃. With all these countermeasures, the transverse cracks incidence of the ultra-thick slabs has been reduced to 488%, and the surface quality of slabs has been effectively improved.
|
Received: 04 May 2011
Published: 15 December 2011
|
|
|
|
|
[1] |
WANG Weihua1,2,LI Zhanjun1,2,CHU Rensheng1,2,CHEN Xia1,2. Hydrogen diffusion in slab for stacking slowcooling[J]. Iron and Steel, 2019, 54(11): 49-55. |
[2] |
. Some considerations for new generation of high-efficiency continuous casting technology development[J]. , 0, (): 0-0. |
[3] |
Jia-Quan ZHANG. Investigation of Overall Mold Metallurgical Behavior Under Electromagnetic Stirring For Round Bloom Casting Process[J]. , 0, (): 0-0. |
[4] |
ZENG Zhi-qi,,YANG Qian-kun,,AI Ke-nan,,XIE Jian-bo,,LI Jian,,FU Jian-xun,. Analysis on nozzle clogging of 49MnVS steel during production[J]. Iron and Steel, 2019, 54(1): 43-48. |
[5] |
WEI Jie-ping,XU Zhi-qiang,SUN Ming-han,ZHU Zhi-wang,WANG Hai-jun,DU Feng-shan. Experimental research of vibratory cast-rolling strips for 20CrMn alloy steel[J]. Iron and Steel, 2018, 53(12): 118-121. |
[6] |
ZHAO Jun-pu ,,LIU Liu,RAO Jin-yuan. Effect of solidification reduction process on center compactness of continuous casting bloom[J]. Iron and Steel, 2018, 53(9): 30-36. |
|
|
|
|