Analysis of the Hardness Inhomogeneity in Hot-Rolled Product of H13 Steel |
TIAN Jun,LIU Yan,CHENG Guo-guang |
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract Annealing experiment was performed, and the samples before and after annealed were studied by SEM (Scanning Electron Microscope) and EDS (Energy Disperse spectroscopy). The hardness of samples was tested. The reasons causing the hardness inhomogeneity in hot-rolled product of H13 steel were analyzed. The results show that the hardness of freckle area is 91.43 HRB, 7.53% higher than the hardness of normal area. The freckle area is mainly comprised of white spot and black particle, the main chemical composition of white spot is iron and the black particle is alloy carbide. After the H13 samples were annealed, the hardness of freckle area decreased obviously, from 190.2 HB to 168.26 HB. The size of black particle is smaller, and its carbon percentage content decreased significantly, from 80% to 15%. The hardness inhomogeneity in hot-rolled product of H13 steel is mainly due to non-uniform composition of molten steel during the casting solidification process.
|
Received: 20 October 2010
Published: 16 January 2012
|
|
|
|
[1] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
[2] |
TIAN Ya-qiang1,BI Wen-qiang1,PAN Hong-bo2,LI Hong-bin1,ZHENG Xiao-ping1,CHEN Lian-sheng1. Effect of carbide evolution on Lüders behavior of cold rolled ART 0.1C-7Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 505-511. |
[3] |
FENG Lu-lu1,2,HU Feng1,QIAO Wen-wei3,LU Xiu-yu4,ZHANG Guo-hong5. Microstructure and properties of 150mm ultra heavy 07MnCrMoVR hydropower steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 400-405. |
[4] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[5] |
LIU Qing-song, PEI Ying-hao, SHI Li-fa, XIA Xue-lan, HE Zhi-jian, CHENG Guo-qing. Effect of annealing tension on magnetic anisotropy of Fe-3.0%Si non-oriented silicon steel[J]. Iron and Steel, 2020, 55(4): 95-99. |
[6] |
XU De-chao1,2, ZHANG Bo-ming, WANG Peng-tao, LI Run-chang,TENG Hua-xiang. Effect of Si and Mn on continuous cooling transformation behavior of hot forming steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 1-. |
|
|
|
|