Inclusions in 430 Stainless Steelmaking During AOD-LF-CC Process |
FU Bang-hao1,CHEN Chao1,CHENG Guo-guang1,PAN Ji-xiang2,LI Yan2,PAN Wei2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Jiuquan Iron and Steel Co., Jiayuguan 735100, Gansu, China |
|
|
Abstract Samples taken from the end of AOD, LF and tundish casting operations of the AOD-LF-TD process during 430 stainless smelting process were investigated and identified through the scanning electron microscope with an EDS X-ray analyzer to characterize the inclusions in terms of the chemical composition, size and morphology. The results show that the total oxygen content, the inclusion content and size decrease throughout the AOD-LF-TD process. Additionally, the types of inclusions change at different stages of the process; the inclusions in AOD are mainly CaO-SiO2-MgO compounds, while in LF and tundish, it is detected mostly CaO-SiO2-MgO-Al2O3 inclusions, besides, inclusions with MnO compound are also found in tundish. Meanwhile, the inclusions in AOD with the compounds of CaO-SiO2-MgO are found to be close to the slag composition. The variation of the composition of the inclusions in LF and tundish are related to the refining process, continuous casting protection as well as temperature drop.
|
Received: 08 April 2011
Published: 16 January 2012
|
|
|
|
[1] |
李道明.不锈钢中非金属夹杂物的危害及去除[J].山西冶金,2008,31(4):24.
|
[1] |
李道明.不锈钢中非金属夹杂物的危害及去除[J].山西冶金,2008,31(4):24.
|
[2] |
姜周华,李阳.洁净不锈钢冶炼技术[C]//2006年全国炼钢、连铸生产技术会议文集.北京:中国金属学会,2006:59.
|
[2] |
姜周华,李阳.洁净不锈钢冶炼技术[C]//2006年全国炼钢、连铸生产技术会议文集.北京:中国金属学会,2006:59.
|
[3] |
Hiroyasu Itoh, Mitsutaka Hino, Shiro Ban-Ya. Deoxidation Equilibrium of Calcium in Liquid Iron [J[. Tetsu-to-Hagane, 1997, 83(11): 695.
|
[3] |
Hiroyasu Itoh, Mitsutaka Hino, Shiro Ban-Ya. Deoxidation Equilibrium of Calcium in Liquid Iron [J[. Tetsu-to-Hagane, 1997, 83(11): 695.
|
[4] |
Kanae Suzuki, Shiro Ban-Ya, Mitsutaka Hino. Deoxidation Equilibrium of Chromium Stainless Steel with Si at the Temperatures from 1828 to 1923K [J]. ISIJ International, 2001, 41(8): 813.
|
[4] |
Kanae Suzuki, Shiro Ban-Ya, Mitsutaka Hino. Deoxidation Equilibrium of Chromium Stainless Steel with Si at the Temperatures from 1828 to 1923K [J]. ISIJ International, 2001, 41(8): 813.
|
[5] |
Jong wan Kim, Sun koo Kim, Dong sik Kim, et al. Formation Mechanism of Ca-Si-Al-Mg-Ti-O Inclusions in Type 304 Stainless Steel [J]. ISIJ International, 1996, 36(1): S140.
|
[5] |
Jong wan Kim, Sun koo Kim, Dong sik Kim, et al. Formation Mechanism of Ca-Si-Al-Mg-Ti-O Inclusions in Type 304 Stainless Steel [J]. ISIJ International, 1996, 36(1): S140.
|
[6] |
Woo-Yeol Cha, Dong-Sik Kim, Yong-Deuk Lee, et al. A Thermodynamic Study on the Inclusion Formation in Ferritic Stainless Steel Melt [J]. ISIJ International, 2004, 44(7): 1134.
|
[6] |
Woo-Yeol Cha, Dong-Sik Kim, Yong-Deuk Lee, et al. A Thermodynamic Study on the Inclusion Formation in Ferritic Stainless Steel Melt [J]. ISIJ International, 2004, 44(7): 1134.
|
[7] |
Herrera-Trejo M., Castro M.R., Mendez J.N., et al. Evolution of Inclusion Nature during the EAF-LF-CC Process [J]. Scandinavian Journal of Metallurgy, 1998, 27(6): 233.
|
[7] |
Herrera-Trejo M., Castro M.R., Mendez J.N., et al. Evolution of Inclusion Nature during the EAF-LF-CC Process [J]. Scandinavian Journal of Metallurgy, 1998, 27(6): 233.
|
[1] |
HOU Xin-mei, LIU Yun-song, WANG En-hui. Effect of ladle-lining refractory on non-metallic inclusions in steel[J]. Iron and Steel, 2020, 55(6): 15-24. |
[2] |
YU Hui-xiang, PAN Ming, YANG De-xin. Behavior of inclusions in ultra-low carbon IF steel during deoxidation and alloying process[J]. Iron and Steel, 2020, 55(6): 46-53. |
[3] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[4] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[5] |
QIN Zheng-feng, XUE Zheng-liang, LI Jin-bo, LI Bo-si. Origin of large spherical or bar-shaped inclusions in calcium treated steel[J]. Iron and Steel, 2020, 55(5): 31-38. |
[6] |
WANG Yi, ZHANG Li-feng, REN Ying, REN Qiang. Mechanism of inclusion evolution during refining process of 37Mn5 steel production[J]. Iron and Steel, 2020, 55(5): 39-44. |
|
|
|
|