Dual-Phase Weathering Steel Cu-P-Cr-Ni-Mo Prepared by Directly Hot-Rolling |
ZHANG Chun-ling,CAI Da-yong,LIAO Bo |
(Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, China) |
|
|
Abstract Cu-P-Cr-Ni-Mo weathering steel, in which dual-phase microstructures can be obtained by directly hot-rolling, was developed through readjustment of alloy elements based on the composition of weathering steel 09CuPCrNi. The wide temperature range of ferrite precipitation in the continuous cooling transformation (CCT) diagram of the hot deformed austenite can be applied as cooling speed windows. And between the precipitation range of ferrite and the transformation range of bainite, a wide metastable-austenite range of 80℃ exists, which can be held as coiling windows. The bainite transformation also can be avoided during the coiling process for the enveloped bainite transformation range in the CCT diagram. Based on the CCT diagram of deformed austenite, dual-phase weathering steel Cu-P-Cr-Ni-Mo is produced through simulated continuous hot-rolling on Gleeble-3500 thermal simulator. The microstructure of the hot-rolled dual-phase weathering steel Cu-P-Cr-Ni-Mo under different conditions is characterized as irregular distribution of island-shaped martensite in the matrix of equiaxed ferrite grains.
|
Received: 10 October 2011
Published: 30 July 2012
|
|
|
|
|
[1] |
C. Zhang, D. Cai, B. Liao. Microstructure and Mechanical Properties of Dual-Phase Weathering Steel 09CuPTiRe[J]. Journal of Materials Science, 2004, 39(13):4393.
|
[2] |
张春玲, 蔡大勇, 廖波. 09CuPCrNi耐候钢的双相化研究[J].钢铁, 2004, 39(3):50. (Zhang Chunling, Cai Dayong, Liao Bo. Study on the Dual-Phase Treatment of Steel 09CuPCrNi [J]. Steel and Iron, 2004, 39(3):50. )
|
[1] |
C. Zhang, D. Cai, B. Liao. Microstructure and Mechanical Properties of Dual-Phase Weathering Steel 09CuPTiRe[J]. Journal of Materials Science, 2004, 39(13):4393.
|
[3] |
戴雅康, 杜林秀, 戚正风. 耐候钢的双相化处理-耐候双相钢[J].机械工程材料, 1992, 16(3):38. (Dai Yakang, Du Linxiu, Qi Zhengfeng. Dual-Phase Treatment of Weathering Steel-Dual-Phase Weathering Steel [J]. Materials for Mechanical Engineering, 1992, 16(3): 38.)
|
[2] |
张春玲, 蔡大勇, 廖波. 09CuPCrNi耐候钢的双相化研究[J].钢铁, 2004, 39(3):50. (Zhang Chunling, Cai Dayong, Liao Bo. Study on the Dual-Phase Treatment of Steel 09CuPCrNi [J]. Steel and Iron, 2004, 39(3):50. )
|
[4] |
樊云昌. 双相钢及其在铁路客、货车辆上的应用前景[J]. 石家庄铁道学院学报, 1999, 12(3): 57. (Fan Yunchang. Dual-Phase Steels and the Prospects for Their Applications in Manufacturing of Railway Stocks [J]. Journal of Shijiazhuang Railway Institute, 1999, 12(3): 57.)
|
[3] |
戴雅康, 杜林秀, 戚正风. 耐候钢的双相化处理-耐候双相钢[J].机械工程材料, 1992, 16(3):38. (Dai Yakang, Du Linxiu, Qi Zhengfeng. Dual-Phase Treatment of Weathering Steel-Dual-Phase Weathering Steel [J]. Materials for Mechanical Engineering, 1992, 16(3): 38.)
|
[4] |
樊云昌. 双相钢及其在铁路客、货车辆上的应用前景[J]. 石家庄铁道学院学报, 1999, 12(3): 57. (Fan Yunchang. Dual-Phase Steels and the Prospects for Their Applications in Manufacturing of Railway Stocks [J]. Journal of Shijiazhuang Railway Institute, 1999, 12(3): 57.)
|
[5] |
A. P. Coldren, G. Tither. Development of a Mn-Si-Cr-Mo As-Rolled Dual-Phase Steel [J]. Journal of Metals, 1978, 4: 6.
|
[5] |
A. P. Coldren, G. Tither. Development of a Mn-Si-Cr-Mo As-Rolled Dual-Phase Steel [J]. Journal of Metals, 1978, 4: 6.
|
[6] |
T. Gréday, H. Mathy and P. Messien. About Different Ways to Obtain Multiphase Steels [A]. R.A.Kot, J.W.Morris. Structure and Properties of Dual-Phase Steels [C]. New York: The Metallurgical Society of AIME, 1979. 260-280.
|
[7] |
张久信, 王明微, 谭佃龙. 640MPa级直接热轧双相钢SX65的研制[J]. 鞍钢技术, 1994, 6(4):1. (Zhang Jiuxin, Wang Mingwei, Tan Dianlong. Development of Directly Hot-Rolling Dual-Phase Steel SX65 with Grade 640MPa [J]. Technology of Angang, 1994, 6(4):1.)
|
[6] |
T. Gréday, H. Mathy and P. Messien. About Different Ways to Obtain Multiphase Steels [A]. R.A.Kot, J.W.Morris. Structure and Properties of Dual-Phase Steels [C]. New York: The Metallurgical Society of AIME, 1979. 260-280.
|
[8] |
宋义全. 0.1C-1.5Si-1.5Mn-0.4Cr热轧双相钢的相变和组织[J].特殊钢, 2001, 22(5):16. (Song Yiquan. Transformation and Structure of As-Hot Rolled Dual Phase Steel 0.1C-1.5Si-1.5Mn-0.4Cr [J]. Special Steel, 2001, 22(5):16.)
|
[7] |
张久信, 王明微, 谭佃龙. 640MPa级直接热轧双相钢SX65的研制[J]. 鞍钢技术, 1994, 6(4):1. (Zhang Jiuxin, Wang Mingwei, Tan Dianlong. Development of Directly Hot-Rolling Dual-Phase Steel SX65 with Grade 640MPa [J]. Technology of Angang, 1994, 6(4):1.)
|
[8] |
宋义全. 0.1C-1.5Si-1.5Mn-0.4Cr热轧双相钢的相变和组织[J].特殊钢, 2001, 22(5):16. (Song Yiquan. Transformation and Structure of As-Hot Rolled Dual Phase Steel 0.1C-1.5Si-1.5Mn-0.4Cr [J]. Special Steel, 2001, 22(5):16.)
|
|
|
|