Effect of Ultra-Fast Cooling on Steel Strength |
YUAN Peng-ju1,2,WU Di1,FU Chang-wei2,ZHAO Xian-ming1,HUO Xi-wei2 |
(1. The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China 2. Technology Center, Laiwu Iron and Steel Group |
|
|
Abstract The ultra-fast cooling mechanism of rolled stock was investigated. The experiment was carried out on H-beam by using ultra-fast cooling device of Northeastern University. The effects of different cooling rates and cooling methods on structure and properties of Q235B and Q345B rolled stocks after rolling were analyzed. The results show that the strength is improved by 205MPa at 444.4℃/s of cooling rate by using single-stage cooling. The strength is improved by 230MPa by using two-stage cooling, when the cooling rate reaches to 385 and 297℃/s. Two types of cooling methods can both dramatically improve the strength of rolled stocks. Where as the cooling effect of two-stage cooling is apparently higher than single-stage cooling. It will provide technical supports for realizing low cost industrial production of H-beam and production of higher level steel.
|
Received: 08 October 2011
Published: 30 October 2012
|
|
|
|
[1] |
Ai J H,Zhao T C. Effect of controlled rolling and cooling on the microstructure and mechanical properties of 60Si2MnA spring steel rod [J].Journal of Material Process Technology,2005,160:390-395.
|
[1] |
Ai J H,Zhao T C. Effect of controlled rolling and cooling on the microstructure and mechanical properties of 60Si2MnA spring steel rod [J].Journal of Material Process Technology,2005,160:390-395.
|
[2] |
王国栋.新一代TMCP的实践和工业应用举例[J].上海金属,2008,30(3):1-4.
|
[2] |
王国栋.新一代TMCP的实践和工业应用举例[J].上海金属,2008,30(3):1-4.
|
[3] |
Li Z,Wu D. Study of the high strength and low yield ratio cold forging steel[J].Materials Science and Engineering A,2007,452/453(4):142-148.
|
[3] |
Li Z,Wu D. Study of the high strength and low yield ratio cold forging steel[J].Materials Science and Engineering A,2007,452/453(4):142-148.
|
[4] |
Iris V R, Clayton O R. Deviation of residual stress patterns in 52100 bearing steel by inherent microstructure transformations after rolling contact[J].Materials Characterization,2004,53(8):381-393.
|
[4] |
Iris V R, Clayton O R. Deviation of residual stress patterns in 52100 bearing steel by inherent microstructure transformations after rolling contact[J].Materials Characterization,2004,53(8):381-393.
|
[5] |
孙艳坤,吴迪.超快冷终冷温度对轴承钢板材组织性能影响[J].东北大学学报:自然科学版,2008,29(11):1572-1576.
|
[5] |
孙艳坤,吴迪.超快冷终冷温度对轴承钢板材组织性能影响[J].东北大学学报:自然科学版,2008,29(11):1572-1576.
|
[5] |
孙艳坤,吴迪.超快冷终冷温度对轴承钢板材组织性能影响[J].东北大学学报:自然科学版,2008,29(11):1572-1576.
|
[5] |
孙艳坤,吴迪.超快冷终冷温度对轴承钢板材组织性能影响[J].东北大学学报:自然科学版,2008,29(11):1572-1576.
|
[6] |
赵宪明,孙艳坤,王永红.轴承钢棒材超快速冷却的试验研究[J]. 东北大学学报:自然科学版,2010,31(7):947-951.
|
[6] |
赵宪明,孙艳坤,王永红.轴承钢棒材超快速冷却的试验研究[J]. 东北大学学报:自然科学版,2010,31(7):947-951.
|
[1] |
CHENG Xiang-kui, ZHAO Ying-tao, ZHAO Xu, WANG Jun, HUANG Xiao-li, PU Chun-lei. Preparation of V-Ti magnetite ore basic pellet containing NaOH[J]. Iron and Steel, 2020, 55(6): 33-37. |
[2] |
LI Xiao-yuan,SHI Jie. Ballistic behavior of high strength steel targets during high speed impact of projectile[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 429-436. |
[3] |
RONG Tao, TANG Hui-qing, FAN Kai, SUN Yan-jun. Applying high-carbon metallic briquette in blast furnace for coke saving[J]. Iron and Steel, 2020, 55(5): 10-19. |
[4] |
XIAO Shao-bin, WANG Wei, LIU Tian-yu, ZHANG Qin, LÜ Zhi-qing. Effects of vacancies and C atoms on mechanical properties of Fe grain boundary[J]. Iron and Steel, 2020, 55(4): 75-81. |
[5] |
LIU Qing-song, PEI Ying-hao, SHI Li-fa, XIA Xue-lan, HE Zhi-jian, CHENG Guo-qing. Effect of annealing tension on magnetic anisotropy of Fe-3.0%Si non-oriented silicon steel[J]. Iron and Steel, 2020, 55(4): 95-99. |
[6] |
CHEN Ya-jun1,KUANG Shuang2,ZHAO Zheng-zhi3. Study status of hydrogen induced delayed fracture of advanced high strength automotive steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 265-272. |
|
|
|
|