Reason and Control on Edge Cracks of J55 Hot Rolled Strip |
LIU Guo-liang1,NI You-jin2,JI Chen-xi1,CUI Yang1,CHEN Jin2,BAO Chun-lin1 |
1. Strip Technology Department, Shougang Research Institute of Technology, Beijing 100043, China 2. Shougang Qian’an Iron and Steel Co., Ltd., Qian’an 064404, Hebei, China |
|
|
Abstract The edge crack was investigated through optical microscope and SEM, and the reasons of edge crack were analyzed. Results show that transversal corner cracks of slabs are the origin of the edge cracks of hot rolled strips, and AlN, Nb(N, C) precipitates around the prior austenite grain boundaries due to intensive cooling rate rendered the slabs more susceptible to cracks. After rolling stands, the transverse cracks of the slabs will propagate to serrated edge cracks.
|
Received: 23 November 2011
Published: 30 October 2012
|
|
|
|
|
[1] |
赵长亮,孙彦辉,田志红等.CSP热轧板卷边部裂纹成因[J].北京科技大学学报,2007,29(5):499-503.
|
[1] |
赵长亮,孙彦辉,田志红等.CSP热轧板卷边部裂纹成因[J].北京科技大学学报,2007,29(5):499-503.
|
[2] |
刘 洋,韦耀环,马瑞金等.连铸坯角部横裂纹在轧后钢板边部演化研究[C].2011年第九届全国连铸学术会议论文集:358-366.
|
[2] |
刘 洋,韦耀环,马瑞金等.连铸坯角部横裂纹在轧后钢板边部演化研究[C].2011年第九届全国连铸学术会议论文集:358-366.
|
[3] |
关立春,韩立海,唐海明.集装箱板SPA-H边部缺陷的机制研究及控制实践[J] .炼钢,2011,46(7):36-40.
|
[3] |
关立春,韩立海,唐海明.集装箱板SPA-H边部缺陷的机制研究及控制实践[J] .炼钢,2011,46(7):36-40.
|
[4] |
陈家祥.炼钢常用图表数据手册.北京:冶金工业出版社,1984:586.
|
[5] |
孙彦辉,赵长亮,孟征兵等.CSP工艺生产热轧板卷边裂的分析和控制[J].特殊钢,2006,27(4):47-49.
|
[4] |
陈家祥.炼钢常用图表数据手册.北京:冶金工业出版社,1984:586.
|
[5] |
孙彦辉,赵长亮,孟征兵等.CSP工艺生产热轧板卷边裂的分析和控制[J].特殊钢,2006,27(4):47-49.
|
[6] |
王新华,昌波,李景捷等.700-1000℃间含Nb钢铸坯的延塑性降低与Nb(C,N)析出[J].金属学报,1997,33(5):485-490.
|
[7] |
刘光明,李洪泉,李大明.含铌钢铸坯横裂纹的分析及改进措施[J].炼钢,2006,22(1):37-39.
|
[6] |
王新华,昌波,李景捷等.700-1000℃间含Nb钢铸坯的延塑性降低与Nb(C,N)析出[J].金属学报,1997,33(5):485-490.
|
[7] |
刘光明,李洪泉,李大明.含铌钢铸坯横裂纹的分析及改进措施[J].炼钢,2006,22(1):37-39.
|
[1] |
LIU Wen-hua,XU Gang-jun,ZHANG Li-qin. Causes and control measures of corner crack in DC01EK[J]. , 2019, 44(1): 49-53. |
[2] |
XU Gang-jun,LIU Peng,SUI Ya-fei. Research and application of light LF refining technology on hot rolled coil[J]. , 2018, 43(5): 19-25. |
[3] |
ZHAO Shuo,,MA Liang,,YAN Tao,,MA Guang-min. Effect of microstructure and inclusions on the formation of edge crack in 40Cr[J]. Chinese Journal of Iron and Steel, 2017, 42(2): 43-47. |
[4] |
ZHANG Jian-jun,,ZHANG Hui,XI Chang-suo,TAN Wen,WANG Chun-feng. Analysis and control of transverse corner cracking formation on middle carbon steel in thin slab casting[J]. Iron and Steel, 2017, 52(11): 32-36. |
[5] |
FAN Xing-chen. Research on improving the surface quality of 400mm ultra-thick slabs with the technology of 3D sprays[J]. , 2017, 42(06): 50-52. |
[6] |
XU Zhang-yin,,ZHAO Zeng-wu,,JIANG Yin-ju,,LI Bao-wei,. Experiment on Nb-bearing microalloyed steel made directly by Nb-bearing hot metal[J]. Iron and Steel, 2015, 50(4): 13-16. |
|
|
|
|