Characteristics of Solute Segregation on Brittle Zone at Solidifying Front of Microalloy Steel |
ZENG Ya-nan,SUN Yan-hui,CAI Kai-ke |
Metallurgical and Ecological Engineering School, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract Based on numerous cracks in continuous cast billets during solidification, the crack susceptibility and solute segregation was investigated by theoretical calculation and thermal simulation experiment. The results show that the solid volume fraction of microalloy steel between 0.75 and 1.00, the segregation degree of elements C, Mn is lower than S, P, Ti. While the S content raises to 1.2%, the segregation degree of element S decreases to 20.7; the influence degree of brittle zone is Mn>S>C>P>Ti, the brittle zone temperature enlarges from 25K to 33K, 15K to 38K with the content of S, Mn increases from 0.002% to 0.02%, 0.2% to 1.6%, respectively. Meanwhile, steel embitterment has no direct relation with solidification structure was confirmed by thermal simulation experiment.
|
Received: 28 April 2012
Published: 14 January 2013
|
|
|
|
|
[1] |
Thomas B G,Brimacombe J K,Samarasekera I V.The Formation of Panel Cracks in Steel Ingots: A State-of-the-art Review[J].ISS Transactions,1986,((7)):7-20
|
[1] |
Thomas B G,Brimacombe J K,Samarasekera I V.The Formation of Panel Cracks in Steel Ingots: A State-of-the-art Review[J].ISS Transactions,1986,((7)):7-20
|
[2] |
Kim K,Han H N,Yeo T,et al.Analysis of Surface and Internal Cracks in Continuous Cast Beam Blank[J].Ironmaking and Steelmaking,1997,24(3):249-256
|
[2] |
Kim K,Han H N,Yeo T,et al.Analysis of Surface and Internal Cracks in Continuous Cast Beam Blank[J].Ironmaking and Steelmaking,1997,24(3):249-256
|
[3] |
蔡兆镇,朱苗勇.溶质偏析对连铸坯凝固前沿裂纹敏感性影响的研究[J].铸造技术,2009,30(11):1396-1401
|
[3] |
蔡兆镇,朱苗勇.溶质偏析对连铸坯凝固前沿裂纹敏感性影响的研究[J].铸造技术,2009,30(11):1396-1401
|
[4] |
Brody H D,Flemings M C.Solute redistribution during dendritic solidification[J].AIME,1966,236:615-618
|
[4] |
Brody H D,Flemings M C.Solute redistribution during dendritic solidification[J].AIME,1966,236:615-618
|
[5] |
刘洋,王新华,王文军等.低碳纯净钢连铸坯凝固前沿元素微观偏析模型的研究[J].铸造技术,2011,32(1):49-54
|
[5] |
刘洋,王新华,王文军等.低碳纯净钢连铸坯凝固前沿元素微观偏析模型的研究[J].铸造技术,2011,32(1):49-54
|
[6] |
Yamanaka A, Yakima K, Okamura K, et al. .Critical strain for internal crack formation in continuous casting[J].Ironmaking and Steelmaking.,1992,22(6):508-512
|
[6] |
Yamanaka A, Yakima K, Okamura K, et al. .Critical strain for internal crack formation in continuous casting[J].Ironmaking and Steelmaking.,1992,22(6):508-512
|
[1] |
chishirong chishirongchishirong. [J]. , 2020, 45(3): 0-0. |
[2] |
. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0. |
[3] |
Gan-Shui ZHOU. Diagnosis of instability during trial production of the billet continuous casting in a steel factory in Vietnam[J]. , 2020, 45(2): 0-0. |
[4] |
LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22. |
[5] |
ZHANG Si-yuan1,2,LONG Mu-jun1,2,AI Song-yuan1,2,TAN Kai1,2,CHEN Deng-fu1,2,HUANG Yun-wei1,2. Oxidation behavior of continuous casting slabs and its effect on temperature during cooling process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 129-134. |
[6] |
. Application of digital delivery in continuous casting engineering construction and production[J]. , 2020, 45(1): 0-0. |
|
|
|
|