Continuous Cooling Transformation Microstructure and Mechanical Property of 1000MPa Low Carbon Bainitic Steel |
YI Min1,2 ,WANG Guo-dong1,CHEN Tao2,WANG Li-feng2,TONG Qian2 |
1. The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004,Liaoning, China 2. The Research Institute of Technology, Shougang Group, Beijing 100043, China |
|
|
Abstract The microstructure of Si-Mn low carbon bainitic steel during continuous cooling was investigated by Gleeble-2000 thermal simulation test. Furthermore, the low carbon bainitic steel was also manufactured in the Shougang Steel Rod Rolling Plant. The effects of the process factors on the microstructure and the mechanical properties were studied.The results show that the cooling rate has a direct impact on both the microstructures type and properties. Full bainitic microstructures with UTS is as high as 1000MPa could obtain for this series of low carbon bainitic steel at a cooling rate of 2.0℃/s. Fine bainitic structure with good plasticity and impact properties could be obtained through the controlled rolling process.
|
Received: 18 April 2012
Published: 27 February 2013
|
|
|
|
[2] |
王建泽 康永林 杨善武 等.ULCB钢相变产物粒状与板条状贝氏体组织性能研究[J].材料工程,2006, 增刊: 252-258
|
[1] |
尚成嘉 王学敏 杨善武 等.高强度低碳贝氏体钢的工艺与组织细化 [J].金属学报,2003,39 (10): 1019-1024
|
[2] |
王建泽 康永林 杨善武 等.ULCB钢相变产物粒状与板条状贝氏体组织性能研究[J].材料工程,2006, 增刊: 252-258
|
[3] |
方鸿生 徐平光 白秉哲 等.一种新的复相组织-仿晶界型铁素体/粒状贝氏体[J].金属热处理, 2000,11: 1-5
|
[3] |
方鸿生 徐平光 白秉哲 等.一种新的复相组织-仿晶界型铁素体/粒状贝氏体[J].金属热处理, 2000,11: 1-5
|
[4] |
徐平光 方鸿生 白秉哲 等 .仿晶界型铁素体/粒状贝氏体复相组织的韧性[J].金属学报,2002,38(3):255-260
|
[4] |
徐平光 方鸿生 白秉哲 等 .仿晶界型铁素体/粒状贝氏体复相组织的韧性[J].金属学报,2002,38(3):255-260
|
[5] |
罗志俊 沈俊昶 苏航 等 .10CrNi5MoV钢板条M/B组织亚单元对强韧性的影响 [J].材料热处理学报, 2010,31(10):63-69
|
[5] |
罗志俊 沈俊昶 苏航 等 .10CrNi5MoV钢板条M/B组织亚单元对强韧性的影响 [J].材料热处理学报, 2010,31(10):63-69
|
[6] |
姚忠凯.钢的组织转变(书)[J].机械工业出版社,1980 ,:-
|
[6] |
姚忠凯.钢的组织转变(书)[J].机械工业出版社,1980 ,:-
|
[7] |
朱子新 杜则裕 胡光立 等 .残余奥氏体对300 M超高强度钢冲击疲劳性能的影响[J].天津大学学报,2001 ,34(3 ):379-382
|
[7] |
朱子新 杜则裕 胡光立 等 .残余奥氏体对300 M超高强度钢冲击疲劳性能的影响[J].天津大学学报,2001 ,34(3 ):379-382
|
|
|
|