Development of Hot Rolling Plate Q450NQR1 With High Corrosion Resistant for Railway Boxcar |
LU Jun-hui1,WANG Xiao-chun2,LIU Jia-qi1,ZHANG Cheng-wu2,ZHANG Hui1,PIAO Feng-yun2 |
1. State Key Laboratory of Advanced Steel Processing and Products, Central Iron and Steel Research Institute, Beijing 100081, China 2. Technology Center, Tonghua Iron and Steel Group Co., Ltd., Tonghua 134000, Jilin, China |
|
|
Abstract The hot rolling plate Q450NQR1 with high corrosion resistant for railway boxcar was developed by hot metal pre-treatment—120t top and bottom combined blown converter—LF refining—FTSC continuous casting machine—2R—5F mill—coiling with TMCP process. The results show that the microstructure of plate is ferrite-pearlite and grain size rating is 12, the yield strength and tensile strength are 509.2MPa and 580MPa, respectively. The impact absorbing energy at -40℃ is about 170J, and corrosion resistant is very good, and the corrosion rate for 144h is decreased 33.33% compared with the Q345B. The production can meet the requirement of railway boxcar.
|
Received: 27 June 2012
Published: 27 February 2013
|
|
|
|
[1] |
李晓非,金纪勇,李文权.Si-Cr-Nb高强钢轨钢的研制[J].钢铁,2001,(12):46-49
|
[1] |
李晓非,金纪勇,李文权.Si-Cr-Nb高强钢轨钢的研制[J].钢铁,2001,(12):46-49
|
[2] |
钱余海,李自刚.加速腐蚀环境下高强耐候钢Q450NQR1的耐蚀性能研究[J].宝钢技术,2007,(2):5-8
|
[2] |
钱余海,李自刚.加速腐蚀环境下高强耐候钢Q450NQR1的耐蚀性能研究[J].宝钢技术,2007,(2):5-8
|
[3] |
文小明.铁道货车用Q450NQR1高强钢的研制开发[J].第4届中国金属学会青年学术年会,2008,:152-156
|
[3] |
文小明.铁道货车用Q450NQR1高强钢的研制开发[J].第4届中国金属学会青年学术年会,2008,:152-156
|
[4] |
H.E. Townsend. Effects of alloying elements on the corrosion of steel in industrial atmospheres[J].Corrosion,2001,57(6):497-501
|
[4] |
H.E. Townsend. Effects of alloying elements on the corrosion of steel in industrial atmospheres[J].Corrosion,2001,57(6):497-501
|
[5] |
Yamashita M,Nagano H,Misawa T,et al.Structure of protective rust layers formed on weathering steels by long- term exposure in the industrial atmospheres of Japan and North America[J].ISIJ International,1998,38(3):285-290
|
[5] |
Yamashita M,Nagano H,Misawa T,et al.Structure of protective rust layers formed on weathering steels by long- term exposure in the industrial atmospheres of Japan and North America[J].ISIJ International,1998,38(3):285-290
|
[6] |
Chiaki OUCHI,Tetsuya SAMPEI,Isao KOZASU.The Effect of Hot Rolling Condition and Chemical Composition on the Onset Temperature of Gamma-Alpha Transformation after Hot Rolling [J].Transactions of the ISIJ,1982,22(3):214-222
|
[6] |
Chiaki OUCHI,Tetsuya SAMPEI,Isao KOZASU.The Effect of Hot Rolling Condition and Chemical Composition on the Onset Temperature of Gamma-Alpha Transformation after Hot Rolling [J].Transactions of the ISIJ,1982,22(3):214-222
|
[7] |
杨松柏.铁道车辆用耐候钢耐腐蚀性能评价方法[J].铁道车辆,2001,39(5):9-11
|
[7] |
杨松柏.铁道车辆用耐候钢耐腐蚀性能评价方法[J].铁道车辆,2001,39(5):9-11
|
[1] |
WANG Zhan-hua1, HUI Wei-jun1, ZHANG Yong-jian1, HAO Yan-ying2, DAI Guan-wen2. High-cycle fatigue properties of controlled rolling and cooling microalloyed medium-carbon forging steels[J]. Iron and Steel, 2019, 54(3): 69-75. |
[2] |
YUAN Guo,CHEN Dong,KANG Jian,LI Zhen- lei,WANG Guo- dong. Development and application of NG- TMCP technology based on ultra- fast cooling for large scale hot rolled strip lines[J]. , 2019, 31(2): 150-158. |
[3] |
WANG Bing-xing,XIONG Lei,ZHANG Tian,WANG Zhao-dong,WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Iron and Steel, 2017, 52(9): 60-65. |
[4] |
ZHANG Qiang,XU Shao- pu,LI Zhong- bo,TANG Zheng- lei,GAO Zhao- hai,YANG Yang. Research and development of extra- thick steel plate of Q345E- Z35[J]. Chinese Journal of Iron and Steel, 2015, 27(11): 73-76. |
[5] |
NIU Wei,LI Run-xia,GUO Qiang,HAN Feng-jun. Discussion on mechanical properties of Q345E rolled flat steel[J]. Chinese Journal of Iron and Steel, 2015, 33(1): 13-16. |
[6] |
LIU Wei-jian,LI Jing,HUO Xiang-dong. Mechanism of Strengthening and Toughening for Wear Resistant Steel NM400 With High Strength and Low Alloy[J]. Chinese Journal of Iron and Steel, 2014, 26(7): 77-81. |
|
|
|
|