Change of Microstructure and Mechanical Property in the Failure Process of H13 Mandrel |
ZHOU Jian1,MA Dang-shen1,KANG Ai-jun2,XIAO Rui-yong3,LIU Zhen-tian2,CHEN Zai-zhi1 |
1. Institute of Special Steel, Central Iron and Steel Research Institute, Beijing 100081, China 2. Technology Center, Dongbei Special Steel Group Co., Ltd., Fushun 113001, Liaoning, China 3. Wuxi Yousiweike Petroleum Drilling Tools Co., Ltd., Wuxi 214154, Jiangsu, China |
|
|
Abstract Analysis of SEM, metallography and mechanical property was established based on the failed and unused H13 mandrels with the same heat treatment process. The results show that the failure of mandrel is mainly caused by two kinds of cracks (heat checking and mechanical wear crack), and matrix oxidation can be seen with the development of cracks. The carbides coarsening, recovery of martensite and reduction of hardness can be found on the edge of failed mandrel, and the more close to the surface, hardness decreases more obviously.The reduction of hardness and strength is the main reason of the early appearance of heat checking on the surface of No.1 mandrel, while toughness shortage seriously cause deep mechanical wear crack.
|
Received: 17 January 2012
Published: 27 February 2013
|
|
|
|
|
[1] |
M Akiyama,K Tsubouchi, M Tsumure. .A study of the mechanism of crack initiation on a mandrel bar for mandrel mill rolling in a seamless tube[J].,Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications,2000,214(2):61-70
|
[1] |
M Akiyama,K Tsubouchi, M Tsumure. .A study of the mechanism of crack initiation on a mandrel bar for mandrel mill rolling in a seamless tube[J].,Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications,2000,214(2):61-70
|
[2] |
徐小伟董霞, 侯宁娜,等. .H13钢芯棒过热断裂特征[J].理化检验物理分册,2006,42(4):174-176
|
[2] |
徐小伟董霞, 侯宁娜,等. .H13钢芯棒过热断裂特征[J].理化检验物理分册,2006,42(4):174-176
|
[3] |
张晓燕, 黄子阳, 沈江华, 等. .热轧钢管用芯棒的表面缺陷分析[J].上海金属,2008,20(2):41-44
|
[3] |
张晓燕, 黄子阳, 沈江华, 等. .热轧钢管用芯棒的表面缺陷分析[J].上海金属,2008,20(2):41-44
|
[4] |
谢培利. 影响限动连轧机组芯棒使用寿命的原因分析[J].金属材料与冶金工程,2007,35(5):31-
|
[4] |
谢培利. 影响限动连轧机组芯棒使用寿命的原因分析[J].金属材料与冶金工程,2007,35(5):31-
|
[5] |
Mitchell, J.Lewin. .H13 Die Life-Finding the Missing Link[J].Die Casting Engineer,1988,32(1):24-
|
[5] |
Mitchell, J.Lewin. .H13 Die Life-Finding the Missing Link[J].Die Casting Engineer,1988,32(1):24-
|
[6] |
W. Zleppning. .科研对日常实践中模具钢的选择的帮助[M]. 李洁.译[J].译齐齐哈尔国外模具钢文献汇编,1993,:-
|
[6] |
W. Zleppning. .科研对日常实践中模具钢的选择的帮助[M]. 李洁.译[J].译齐齐哈尔国外模具钢文献汇编,1993,:-
|
[7] |
田玉新,蔡海燕, 支玉明, 等. .影响H13芯棒钢冲击韧性的因素分析[J].宝钢技术,2009,5:22-26
|
[7] |
田玉新,蔡海燕, 支玉明, 等. .影响H13芯棒钢冲击韧性的因素分析[J].宝钢技术,2009,5:22-26
|
[1] |
. [J]. , 2019, 44(3): 0-0. |
[2] |
ZHENG Ai- qin,SONG Xin- li,MA Yu- xi,SUN Xin- jun,JIA Juan,LIANG Xiao- kai. Effect of copper on microstructure and strength and ductility of low alloy wear resistance steel[J]. , 2018, 30(9): 747-753. |
[3] |
TIAN Ya- qiang,TIAN Geng,ZHENG Xiao- ping,SONG Jin- ying,WEI Ying- li,CHEN Lian- sheng. Research status of low carbon high strength bainitic steel[J]. , 2018, 30(7): 505-514. |
[4] |
LIAN Xue- kui,LI Yong,WANG Chun- xu,LIU Xian- min. Effect of tempering on mechanical properties of 25Co15Ni11Cr2MoE steel[J]. , 2018, 30(5): 386-391. |
[5] |
CHENG Bing- gui,WU Feng- juan,LIU Dong- sheng. Microstructure and mechanical properties of low carbon copper- containing steel plate for shipbuilding with yield strength of 785 MPa[J]. Iron and Steel, 2015, 50(8): 83-88. |
[6] |
JIA Yu- ze,,YANG Mao- sheng,ZHOU Xiao- long,CAO Jian- chun,ZHENG Shan- ju,HAO Hong- wei. Effect of preparation processes on strength and toughness of high nitrogen bearing steel[J]. Chinese Journal of Iron and Steel, 2015, 27(7): 62-67. |
|
|
|
|