Formation Mechanism of the Transverse Cracks in Ultra-Thick Slabs for Shouqin |
ZHEN Xin-gang1,ZHU Zhi-yuan1,YANG Jian-ping1,WANG Yu-long1,LIU Yang2,ZHAO Xin-yu2 |
1. Steelmaking Department, Shouqin Metal Material Co., Ltd., Qinhuangdao 066000, Hebei, China 2. Shougang Research Institute of Technology, Beijing 100043, China |
|
|
Abstract Factors influencing transverse cracks such as the thickness of slabs, the carbon and niobium content in liquid steel, the casting speed, the dynamics model and the technology of 3D sprays, were investigated. The results show that, because of the defects in the dynamic secondary cooling model, for the ultra-thick slabs with low casting speed, by the minimum water restrictions of the secondary cooling zone, and under the comprehensive action of the straightening force and the thermal stress, if the total strain of shell is more than its critical strain, the transverse cracks finally forms along the grain boundary, located at the vibrating mark trough distance slab corner 150-500mm.
|
Received: 04 September 2012
Published: 18 June 2013
|
|
|
|
|
[1] |
MAO Jinghua,SHUAI Yong,XIE Guiqiang,WANG Yatao. Key technology of internal quality control for#br# continuous casting extrathick slab[J]. Iron and Steel, 2019, 54(8): 64-69. |
[2] |
. Research on Central segregation control of 400mm ultra-thick slab[J]. , 2019, 44(6): 0-0. |
[3] |
ZHAO Jing,WANG Zhen-ming,WANG Guo-lian,ZHEN Xin-gang,WANG Yu-long,HU Xian-tang. Research of casting technology on tail slab of 400 mm thick slab[J]. , 2019, 44(1): 1-4. |
[4] |
DU Chen- wei,,WANG Chun- lei,LI Bo,LI Bin,MA Bing- chuan,ZHANG Jia- quan. Effect of temperature field and cooling rate along casting direction on surface transverse cracks of microalloyed steel[J]. , 2018, 30(7): 523-528. |
[5] |
LAN Peng,DU Chen-wei,CHEN Pei-li,LIU Hua-song,QIU Dong-sheng,ZHANG Jia-quan. Research status of surface transverse cracking formation mechanism and control technique for continuously cast microalloyed steels[J]. Chinese Journal of Iron and Steel, 2017, 29(1): 1-12. |
[6] |
DU Chen-wei,LAN Peng,LI Yang,LU Jue-yu,ZHANG Jia-quan,JIANG Zhong-kuai,SU Rui-xian,ZHOU Xiu-li,WANG Hong-feng. Thermodynamic analysis on solidification and solid phase transformation control of J55 steel continuous casting slab[J]. Chinese Journal of Iron and Steel, 2017, 42(1): 64-67. |
|
|
|
|