Rolling Process and Microstructure and Properties of Thin Gauge Ultra-High Strength Strip Manufactured by CSP Line |
CHEN Liang1,ZHANG Chao1,ZHU Shuai2,KANG Yong-lin2 |
1. Wuhan Iron and Steel Company Limited, Wuhan 430080, Hubei, China 2. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract The process and technology characteristics of CSP line were introduced. Through optimizing continuous casting and slab quality controlling, using 1180 ℃ tapping temperature and 850-920 ℃ finishing rolling temperature, the mechanical properties of thin gauge ultra-high strength strip were analyzed based on different cooling modes and coiling temperatures. The production results show that the head continuous cooling mode is helpful to grain refinement, higher coiling temperature is beneficial to the sufficient dispersed precipitate fine TiC particles, 70% of the TiC particle size is below 20nm causing significant precipitation strengthening. The machnanical properties of thin gauge strength were affected both by fine grain strengthening caused by and cooling rate and thinner gauge and precipitation strengthening caused by coiling temperature. By optimizing cooling mode and coiling temperature, 500, 600 and 700MPa strength grade strips with 1.2-6.0mm thickness were developed successfully.
|
Received: 08 April 2013
Published: 20 January 2014
|
|
|
|
|
[1] |
康永林,傅杰,柳得橹,等。薄板坯连铸连轧钢的组织性能控制[M]. 北京,冶金工业出版社,2006.
|
[2] |
黎先浩,康永林,陈林恒,等。CSP生产600MPa级低碳贝氏体钢的相变[J]. 北京科技大学学报,2009,31(6):701-707.
|
[2] |
黎先浩,康永林,陈林恒,等。CSP生产600MPa级低碳贝氏体钢的相变[J]. 北京科技大学学报,2009,31(6):701-707.
|
[3] |
康永林,赵征志,于浩,等。轧制工艺对CSP线热轧汽车用高强钢板组织特征的影响[J]. 北京科技大学学报,2007,29(1):30-33.
|
[3] |
康永林,赵征志,于浩,等。轧制工艺对CSP线热轧汽车用高强钢板组织特征的影响[J]. 北京科技大学学报,2007,29(1):30-33.
|
[4] |
霍向东,毛新平,吕盛夏,等。CSP生产Ti微合金化高强钢中纳米碳化物[J]. 北京科技大学学报,2011,33(8):941-946.
|
[4] |
霍向东,毛新平,吕盛夏,等。CSP生产Ti微合金化高强钢中纳米碳化物[J]. 北京科技大学学报,2011,33(8):941-946.
|
[5] |
康永林,周建,毛新平。CSP生产Ti微合金化高强耐候钢组织、应用性能与耐候性分析[J]. 河南冶金,2007,15(4):7-11.
|
[5] |
康永林,周建,毛新平。CSP生产Ti微合金化高强耐候钢组织、应用性能与耐候性分析[J]. 河南冶金,2007,15(4):7-11.
|
[6] |
Kang Y,Thunman M,Du S C,et a1.Aluminum deoxidation equilibrium of molten iron-aluminum alloy with wide aluminum composition range at 1873K [J].ISIJ International,2009,49(10):1483-1489.
|
[6] |
Kang Y,Thunman M,Du S C,et a1.Aluminum deoxidation equilibrium of molten iron-aluminum alloy with wide aluminum composition range at 1873K [J].ISIJ International,2009,49(10):1483-1489.
|
[7] |
Pak J J,Jo J O,Kim S I,et a1.Thermodynamics of titanium and oxygen dissolved in liquid iron equilibrated with titanium oxides[J].ISIJ International,2007,47(1):16-24.
|
[7] |
Pak J J,Jo J O,Kim S I,et a1.Thermodynamics of titanium and oxygen dissolved in liquid iron equilibrated with titanium oxides[J].ISIJ International,2007,47(1):16-24.
|
[8] |
霍向东,毛新平,杨青峰,等。CSP热轧工艺对Ti微合金化钢组织和性能的影响[J]. 钢铁钒钛,2010,31(2):26-31.
|
[8] |
霍向东,毛新平,杨青峰,等。CSP热轧工艺对Ti微合金化钢组织和性能的影响[J]. 钢铁钒钛,2010,31(2):26-31.
|
[1] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[2] |
HE Ya-yuan,LI Li-wei,YIN Yun-yang,DENG Zhao-jun. Evolution of microstructure and properties of thickness section of wearresistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 512-518. |
[3] |
YANG Guang-feng,LU Meng-ke,ZHANG Hang,ZHAI Wei,CUI Jing. Corrosion behavior and mechanism of 300M ultra high strength steel in neutral salt spray environment[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 406-415. |
[4] |
YANG Geng-wei1,HU Zhuo-li1,YIN Qi-long1,MAO Xin-ping1,2,MIAO Li-sha1,LIU Yang2. Effect of phase transformation time on microstructure and mechanical properties of hotrolled TRIP steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 143-149. |
[5] |
YI Hang1,YANG Geng-wei1,MAO Xin-ping1,2,ZHAO Gang1,XU Yao-wen1,BAO Si-qian1. Effect of deformation temperature on phase transformation behavior of hot rolled 65Mn steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(1): 74-80. |
[6] |
XIAO Zunhu,SUI Yafei,LIU Peng,XU Gangjun,LI Ciying. Evolution and control of inclusions in aluminumcontaining on #br# oriented electrical steel through CSP process[J]. Iron and Steel, 2019, 54(7): 42-48. |
|
|
|
|