盾构机轴承用钢的开发与质量控制

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract Recently accompanying with the process of industrialization and the demand of infrastructure development, large excavation equipment tunnel shield machine is widely used on the constructions of a large amount of traffic tunnels, subways, tunnels for water supply and drainage and cable tunnels. The requirement of service life and reliability for tunnel shield machine is pretty high because of its special work condition. The development and quality control of bearing steel for large tunnel shield machine is the main factor which influences the service life and the safety of the whole construction. The problem of choosing steel grades for rolling body and ring of large tunnel shield machine has been studied respectively by analyzing the service condition and the requirement of tunnel shield machine bearing. Besides, the main key measures for the quality control of tunnel shield machine bearing have been proposed. Purification is fundamental and the homogenizing and refining of deformation of cast microstructure is critical to the quality of rolled or forged product. The integrated control of microstructure and performance during the following process of heat treatment including the control of hardening layer, martensite, residual carbide and austenite is the significant way to keep the strength and toughness of tunnel shield machine bearing.

Received: 30 December 2013 Published: 07 May 2014

PACS:

TG142.1

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Ya-Zheng
	JIANG Bei
	WEN Xin-Li
	ZHANG Dan
	ZHOU Le-Yo
	ZHANG Zhao-Lei

Cite this article:

LIU Ya-Zheng,JIANG Bei,WEN Xin-Li等. Development and Quality Control of Bearing Steel for Tunnel Shield Machine[J]. Iron and Steel, 2014, 49(5): 1-6.

URL:

http://www.chinamet.cn/Jweb_gt/EN/ OR http://www.chinamet.cn/Jweb_gt/EN/Y2014/V49/I5/1

[1]	胡胜利，乔世珊．盾构机概论[J]．建筑机械，1999，11：16-20．
[1]	胡胜利，乔世珊．盾构机概论[J]．建筑机械，1999，11：16-20．
[2]	白杉，周洁．我国隧道盾构掘进机的发展和应用[J]．工程机械，2004，35(5)：26-28．
[2]	白杉，周洁．我国隧道盾构掘进机的发展和应用[J]．工程机械，2004，35(5)：26-28．
[3]	黄旭就．关于国内盾构机开发的探讨[J]．装备制造技术，2006，2：3-7．
[3]	黄旭就．关于国内盾构机开发的探讨[J]．装备制造技术，2006，2：3-7．
[4]	刘雅政，周乐育，张朝磊，等．重大装备用高品质轴承用钢的发展及其质量控制[J]．钢铁，2013，48(8)：1-8．
[4]	刘雅政，周乐育，张朝磊，等．重大装备用高品质轴承用钢的发展及其质量控制[J]．钢铁，2013，48(8)：1-8．
[5]	Koyama Y. Present status and technology of shield tunneling method in Japan[J]. Tunnelling and Underground Space Technology, 2003, 18(2): 145-159.
[5]	Koyama Y. Present status and technology of shield tunneling method in Japan[J]. Tunnelling and Underground Space Technology, 2003, 18(2): 145-159.
[6]	张凤祥，朱合华，傅德明．盾构隧道．北京：人民交通出版社，2004．
[6]	张凤祥，朱合华，傅德明．盾构隧道．北京：人民交通出版社，2004．
[7]	崔国华，王国强，何恩光，等．盾构机的研究现状及发展前景[J]．矿山机械，2006，34(6)：24-27．
[7]	崔国华，王国强，何恩光，等．盾构机的研究现状及发展前景[J]．矿山机械，2006，34(6)：24-27．
[8]	吉冰旭，周琳，徐绍仁，等．土压平衡盾构主轴承的结构设计分析[J]．轴承，2010 (009)：12-13．
[8]	吉冰旭，周琳，徐绍仁，等．土压平衡盾构主轴承的结构设计分析[J]．轴承，2010 (009)：12-13．
[9]	陈沛，管会生，赵晶石．盾构机大轴承结构参数优化设计[J]．建筑机械：上半月，2010 (004)：87-89．
[9]	陈沛，管会生，赵晶石．盾构机大轴承结构参数优化设计[J]．建筑机械：上半月，2010 (004)：87-89．
[10]	祝燮权．实用滚动轴承手册[M]．上海：上海科学技术出版社，2002
[10]	祝燮权．实用滚动轴承手册[M]．上海：上海科学技术出版社，2002
[11]	刘源泂．低速重载滚动轴承的状态监测与寿命预测方法研究[D]．武汉科技大学，2006．
[11]	刘源泂．低速重载滚动轴承的状态监测与寿命预测方法研究[D]．武汉科技大学，2006．
[12]	姚文峰，罗玉田．高碳铬轴承钢的质量要求和轧制生产工艺[J]．科技情报开发与经济，1998，5：44-45．
[12]	姚文峰，罗玉田．高碳铬轴承钢的质量要求和轧制生产工艺[J]．科技情报开发与经济，1998，5：44-45．
[13]	中国轴承工业协会．滚动轴承基础知识[M]．郑州：河南人民出版社，2006．
[13]	中国轴承工业协会．滚动轴承基础知识[M]．郑州：河南人民出版社，2006．
[14]	虞明全．轴承钢钢种系列的发展状况[J]．上海金属，2008，30(3)：49-54
[14]	虞明全．轴承钢钢种系列的发展状况[J]．上海金属，2008，30(3)：49-54
[15]	Matsuzaki A, Hoshino T, Hagihara H. Advanced Medium Carbon Steel for Bearing Use with Excellent Rolling Contact Fatigue Life Developed by Using New Alloy Design Method[J]. Kawasaki Steel Giho, 2002, 34(2): 104-108.
[15]	Matsuzaki A, Hoshino T, Hagihara H. Advanced Medium Carbon Steel for Bearing Use with Excellent Rolling Contact Fatigue Life Developed by Using New Alloy Design Method[J]. Kawasaki Steel Giho, 2002, 34(2): 104-108.
[16]	付化刚，沈高伟，陈康胤，等．Wind power bearing steel: Application 201010549735[P]. 2010-11-18.
[16]	付化刚，沈高伟，陈康胤，等．Wind power bearing steel: Application 201010549735[P]. 2010-11-18.
[17]	张鹏，夏琴香，李哲林，等．长轴类大锻件自由锻造工艺研究[J]．锻压技术，2011，36(1)：21-25．
[17]	张鹏，夏琴香，李哲林，等．长轴类大锻件自由锻造工艺研究[J]．锻压技术，2011，36(1)：21-25．
[18]	白志斌，谭红，李运兴，等．镦粗过程中锻件内孔洞缺陷的有限元分析[J]．吉林工业大学自然科学学报，1998，2：34-39．
[18]	白志斌，谭红，李运兴，等．镦粗过程中锻件内孔洞缺陷的有限元分析[J]．吉林工业大学自然科学学报，1998，2：34-39．
[19]	孙艳坤，吴迪．轴承钢棒材超快速冷却新工艺的应用研究[J]．钢铁，2008，43(7)：47-50．
[19]	孙艳坤，吴迪．轴承钢棒材超快速冷却新工艺的应用研究[J]．钢铁，2008，43(7)：47-50．
[20]	斯别克托尔．轴承钢的组织与性能[M]．上海：上海科学技术文献出版社，1983．
[20]	斯别克托尔．轴承钢的组织与性能[M]．上海：上海科学技术文献出版社，1983．
[21]	Riveroa I V, Ruudb C O. Deviation of residual stress patterns in 52 100 bearing steel due to inherent microstructural transformations after rolling contact[J]. 2004,53(5):381-393.
[21]	Riveroa I V, Ruudb C O. Deviation of residual stress patterns in 52 100 bearing steel due to inherent microstructural transformations after rolling contact[J]. 2004,53(5):381-393.
[22]	梁皖伦，方金凤，曹军．GCr15轴承钢的热变形模拟实验研究[J]．理化检验-物理分册，2002，38(1)：4-6．
[22]	梁皖伦，方金凤，曹军．GCr15轴承钢的热变形模拟实验研究[J]．理化检验-物理分册，2002，38(1)：4-6．
[23]	王东兴，肖攸毅．连轧GCr15轴承钢的控轧控冷工艺[J]．特殊钢，2004，25(3)：48-49．
[23]	王东兴，肖攸毅．连轧GCr15轴承钢的控轧控冷工艺[J]．特殊钢，2004，25(3)：48-49．
[24]	李胜利．大断面轴承钢控轧控冷工艺的模拟分析[J]．东北大学学报，2006，26(6)：658-660．
[24]	李胜利．大断面轴承钢控轧控冷工艺的模拟分析[J]．东北大学学报，2006，26(6)：658-660．
[25]	张务林．轴承钢棒线材生产技术的研究与应用[J]．特钢技术，1997(3)：7-9．
[25]	张务林．轴承钢棒线材生产技术的研究与应用[J]．特钢技术，1997(3)：7-9．
[26]	王有铭，李曼云，韦光．钢材的控制轧制和控制冷却[M]．北京：冶金工业出版社，1995．
[26]	王有铭，李曼云，韦光．钢材的控制轧制和控制冷却[M]．北京：冶金工业出版社，1995．
[27]	吕炎．锻造工艺学[M]．北京：机械工业出版社，1995．
[27]	吕炎．锻造工艺学[M]．北京：机械工业出版社，1995．
[28]	刘宗昌，任慧平，安胜利．马氏体相变[M]．北京：科学出版社，2012
[28]	刘宗昌，任慧平，安胜利．马氏体相变[M]．北京：科学出版社，2012
[29]	徐祖耀．条状马氏体形态对钢力学性质的影响[J]．热处理，2009，24(3)：1-6．
[29]	徐祖耀．条状马氏体形态对钢力学性质的影响[J]．热处理，2009，24(3)：1-6．
[30]	Inoue T, Matsuda S, Okamura Y, et al. The fracture of a low carbon tempered martensite[J]. Transactions of JIM, 1970, 11(1): 36-43.
[30]	Inoue T, Matsuda S, Okamura Y, et al. The fracture of a low carbon tempered martensite[J]. Transactions of JIM, 1970, 11(1): 36-43.
[31]	Wang C, Wang M, Shi J, et al. Effect of microstructure refinement on the strength and toughness of low alloy martensitic steel[J]. Journal of Materials Science and Technology, 2007, 23(5): 659-664.
[31]	Wang C, Wang M, Shi J, et al. Effect of microstructure refinement on the strength and toughness of low alloy martensitic steel[J]. Journal of Materials Science and Technology, 2007, 23(5): 659-664.
[32]	陈国民．残留碳化物与钢的强韧性[J]．金属热处理，1981，6(11)：1-11．
[32]	陈国民．残留碳化物与钢的强韧性[J]．金属热处理，1981，6(11)：1-11．
[33]	Dong Z, Fu-Xing W, Qi-Gong C, et al. Effect of retained austenite on rolling element fatigue and its mechanism[J]. Wear, 1985, 105(3): 223-234.
[33]	Dong Z, Fu-Xing W, Qi-Gong C, et al. Effect of retained austenite on rolling element fatigue and its mechanism[J]. Wear, 1985, 105(3): 223-234.
[34]	Bhadeshia H. Steels for bearings[J]. Progress in materials science, 2012, 57(2): 268-435.
[34]	Bhadeshia H. Steels for bearings[J]. Progress in materials science, 2012, 57(2): 268-435.
[35]	刘耀中，左传付．轴承钢零件淬回火后的残余奥氏体[J]．轴承，2008，6：48-51．
[35]	刘耀中，左传付．轴承钢零件淬回火后的残余奥氏体[J]．轴承，2008，6：48-51．
[36]	杨信，陈海英．深冷处理对GCr15钢组织性能的影响[J]．焊接技术，2001，30(6)：12-13．
[36]	杨信，陈海英．深冷处理对GCr15钢组织性能的影响[J]．焊接技术，2001，30(6)：12-13．
[37]	贺红勋，黄宗响．热处理工艺对轴承尺寸稳定性的影响[J]．中原工学院学报，2005，16(3)：69-71．
[37]	贺红勋，黄宗响．热处理工艺对轴承尺寸稳定性的影响[J]．中原工学院学报，2005，16(3)：69-71．
[38]	郑善举，杨卯生，雷霆，等．冷处理对16Cr14Co12Mo5轴承钢组织和性能的影响[J]．钢铁，2012，47(12)：76-80．
[38]	郑善举，杨卯生，雷霆，等．冷处理对16Cr14Co12Mo5轴承钢组织和性能的影响[J]．钢铁，2012，47(12)：76-80．
[39]	薛淑芬，刘洪补．滚动体附加回火试验[J]．轴承，1992(5)：55-57．
[39]	薛淑芬，刘洪补．滚动体附加回火试验[J]．轴承，1992(5)：55-57．
[40]	康沫狂，朱明．淬火合金钢中的奥氏体稳定化[J]．金属学报，2005，41(7)：673-679．
[40]	康沫狂，朱明．淬火合金钢中的奥氏体稳定化[J]．金属学报，2005，41(7)：673-679．