Effect of carbon partitioning behavior on microstructure in a kind of Fe-C-Si-Mn-Cr-Mo steel |
LIU Yan-lin |
(Laiwu Branch Company of Shandong Iron and Steel Co.,Ltd.,Laiwu 271104,Shandong,China) |
|
|
Abstract The carbon partitioning behavior and its effect on martensite and retained austenite of Fe-0.24C-0.3Si-1.0Mn-0.56Cr-0.17Mo(mass prcent,%)steel during coolling processes after hot punching were investigated by using fully autodilatometer Formastor-FⅡ. The microstructure characterization was carried out by means of scanning electron microscopy and transmission electron microscopy,and the austenite fraction measurement was determined by X-ray diffraction and electron back scattered diffraction. The results show that martensite and retained austenite were obtained in different cooling processes after hot punching. Using direct fast cooling process after hot punching,the martensite lath was relatively confused and shorter and the amount of retained austenite was less. While using slow cooling process in the end,the martensite lath was longer. It’s found that the carbon partition occurred in the slow cooling process. More retained austenite distributed among the martensite lath and formed thin films. High density dislocation distributed within martensite lath.
|
Received: 20 July 2015
Published: 14 April 2016
|
|
|
|
|
[ 1 ] |
徐伟力,管曙荣,艾健,等. 钢板热冲压新技术关键装备和核心技术[J]. 世界钢铁,2009(2):30-33. XU Wei-li, GUAN Shu-rong, AI Jian, et al. Key equipment and core technology of new technology for hot stamping of steel sheet[J]. World Iron & Steel, 2009(2) : 30-33.
|
[ 1 ] |
徐伟力,管曙荣,艾健,等. 钢板热冲压新技术关键装备和核心技术[J]. 世界钢铁,2009(2):30-33. XU Wei-li, GUAN Shu-rong, AI Jian, et al. Key equipment and core technology of new technology for hot stamping of steel sheet[J]. World Iron & Steel, 2009(2) : 30-33.
|
[ 2 ] |
H.Karbasian, A.E. Tekkaya. A review on hot stamping[J]. Journal of Materials Processing Technology, 210(15): 2103-2118.
|
[ 2 ] |
H.Karbasian, A.E. Tekkaya. A review on hot stamping[J]. Journal of Materials Processing Technology, 210(15): 2103-2118.
|
[ 3 ] |
解西强. Q&P工艺获得的新型马氏体钢微观组织及性能研究[D]. 昆明理工大学,2008.XIE Xi-qiang. Research on the microstructure and properties of new type martensitic steel obtained by Q&P process[D]. Kunming University of Science and Technology, 2008.
|
[ 3 ] |
解西强. Q&P工艺获得的新型马氏体钢微观组织及性能研究[D]. 昆明理工大学,2008.XIE Xi-qiang. Research on the microstructure and properties of new type martensitic steel obtained by Q&P process[D]. Kunming University of Science and Technology, 2008.
|
[ 4 ] |
王存宇,时捷,曹文全,等. Q&P工艺处理低碳CrNi3Si2MoV钢中马氏体的研究[J]. 金属学报,2011,47(6):720-726.WANG Cun-yu, SHI Jie, CAO Wen-quan, et al. Study on the martensite in low carbon CrNi3Si2MoV steel treated by Q&P process[J]. Acta Metallurgica Sinica, 2011, 47(6): 720-726.
|
[ 4 ] |
王存宇,时捷,曹文全,等. Q&P工艺处理低碳CrNi3Si2MoV钢中马氏体的研究[J]. 金属学报,2011,47(6):720-726.WANG Cun-yu, SHI Jie, CAO Wen-quan, et al. Study on the martensite in low carbon CrNi3Si2MoV steel treated by Q&P process[J]. Acta Metallurgica Sinica, 2011, 47(6): 720-726.
|
[ 5 ] |
刘宗昌,任慧平,宋义全. 金属固态相变教程[M]. 北京:冶金工业出版社,2011:97-107.LIU Zong-chang, REN Hui-ping, SONG Yi-quan. Metal solid phase transition course[M]. Beijing: Metallurgical Industry Press, 2011: 97-107.
|
[ 5 ] |
刘宗昌,任慧平,宋义全. 金属固态相变教程[M]. 北京:冶金工业出版社,2011:97-107.LIU Zong-chang, REN Hui-ping, SONG Yi-quan. Metal solid phase transition course[M]. Beijing: Metallurgical Industry Press, 2011: 97-107.
|
[ 6 ] |
姜 超,单忠德,庄百亮,等. 热冲压成形22MnB5钢板的组织和性能[J]. 材料热处理学报,2012(3):78-81.JIANG Chao, SHAN Zhong-de, ZHUANG Bai-liang, et al. Microstructure and properties of hot stamping 22MnB5 steel[J]. Transaction of Materials and Heat Treatment, 2012(3): 78-81.
|
[ 6 ] |
姜 超,单忠德,庄百亮,等. 热冲压成形22MnB5钢板的组织和性能[J]. 材料热处理学报,2012(3):78-81.JIANG Chao, SHAN Zhong-de, ZHUANG Bai-liang, et al. Microstructure and properties of hot stamping 22MnB5 steel[J]. Transaction of Materials and Heat Treatment, 2012(3): 78-81.
|
[ 7 ] |
江海涛,唐荻,米振莉,等. 工艺参数对热冲压成型钢组织性能及硼偏聚的影响[J]. 材料工程,2010,38(2):69-73.JIANG Hai-tao, TANG Di, MI Zhen-li, et al. Influence of processing parameters of hot stamping to mechanical properties of martensite steel and segregation of boron[J]. Journal of Materials Engineering, 2010, 38(2): 69-73.
|
[ 7 ] |
江海涛,唐荻,米振莉,等. 工艺参数对热冲压成型钢组织性能及硼偏聚的影响[J]. 材料工程,2010,38(2):69-73.JIANG Hai-tao, TANG Di, MI Zhen-li, et al. Influence of processing parameters of hot stamping to mechanical properties of martensite steel and segregation of boron[J]. Journal of Materials Engineering, 2010, 38(2): 69-73.
|
[ 8 ] |
赵松山,唐荻,赵才,等. Q&P钢残余奥氏体定量分析及其与性能关系研究[C]. 2007中国钢铁年会论文集,2007:144-147.ZHAO Song-shan, TANG Di, ZHAO Cai, et al. Study on the quantity of the retained austenite and relationship with the mechanical property in the Q&P steel[C]. CSM 2007 Annual Meeting Proceedings, 2007: 144-147.
|
[ 8 ] |
赵松山,唐荻,赵才,等. Q&P钢残余奥氏体定量分析及其与性能关系研究[C]. 2007中国钢铁年会论文集,2007:144-147.ZHAO Song-shan, TANG Di, ZHAO Cai, et al. Study on the quantity of the retained austenite and relationship with the mechanical property in the Q&P steel[C]. CSM 2007 Annual Meeting Proceedings, 2007: 144-147.
|
[ 9 ] |
高绪涛,赵爱民,赵征志,等. 热轧TRIP钢残余奥氏体及其稳定性研究[J]. 材料工程,2011,39(11):39-41.GAO Xu-tao, ZHAO Ai-min, ZHAO Zheng-zhi, et al. Investigation of retained austenite and its stability in hot rolled TRIP steel[J]. Journal of Materials Engineering, 2011, 39(11): 39-41.
|
[ 9 ] |
高绪涛,赵爱民,赵征志,等. 热轧TRIP钢残余奥氏体及其稳定性研究[J]. 材料工程,2011,39(11):39-41.GAO Xu-tao, ZHAO Ai-min, ZHAO Zheng-zhi, et al. Investigation of retained austenite and its stability in hot rolled TRIP steel[J]. Journal of Materials Engineering, 2011, 39(11): 39-41.
|
[10] |
余伟,陈银莉,徐立善,等. 直接淬火-碳分配处理后高强度钢的组织与力学性能[J]. 材料热处理学报,2012(4):62-67.YU Wei, CHEN Yin-li, XU Li-shan, et al. Microstructure and mechanical properties of high strength steel after direct quenching and partitioning[J]. Transaction of Materials and Heat Treatment, 2012(4): 62-67.
|
[10] |
余伟,陈银莉,徐立善,等. 直接淬火-碳分配处理后高强度钢的组织与力学性能[J]. 材料热处理学报,2012(4):62-67.YU Wei, CHEN Yin-li, XU Li-shan, et al. Microstructure and mechanical properties of high strength steel after direct quenching and partitioning[J]. Transaction of Materials and Heat Treatment, 2012(4): 62-67.
|
[11] |
刘俊亮,张作贵,宓小川,等. X80钢中残余奥氏体定量分析的XRD与EBSD法比较[J]. 电子显微学报,2010,29(1):689-692.LIU Jun-liang, ZHANG Zuo-gui, MI Xiao-chuan, et al. Comparison of XRD and EBSD for quantitative analysis of remaining austenite in X80 pipeline steel[J]. Journal of Chinese Electron Microscope Society, 2010,29(1):689-692.
|
[11] |
刘俊亮,张作贵,宓小川,等. X80钢中残余奥氏体定量分析的XRD与EBSD法比较[J]. 电子显微学报,2010,29(1):689-692.LIU Jun-liang, ZHANG Zuo-gui, MI Xiao-chuan, et al. Comparison of XRD and EBSD for quantitative analysis of remaining austenite in X80 pipeline steel[J]. Journal of Chinese Electron Microscope Society, 2010,29(1):689-692.
|
[12] |
程俊业,赵爱民,陈银莉,等. 不同温度回火后30MnB5热成形钢的EBSD研究[J]. 金属学报,2013,49(2):137-145.CHENG Jun-ye, ZHAO Ai-min, CHEN Yin-li, et al. EBSD studies of 30MnB5 hot stamping steel tempered at different temperature[J]. Acta Metallurgica Sinica, 2013, 49(2): 137-145.
|
[12] |
程俊业,赵爱民,陈银莉,等. 不同温度回火后30MnB5热成形钢的EBSD研究[J]. 金属学报,2013,49(2):137-145.CHENG Jun-ye, ZHAO Ai-min, CHEN Yin-li, et al. EBSD studies of 30MnB5 hot stamping steel tempered at different temperature[J]. Acta Metallurgica Sinica, 2013, 49(2): 137-145.
|
[1] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[2] |
TIAN Ya-qiang1,BI Wen-qiang1,PAN Hong-bo2,LI Hong-bin1,ZHENG Xiao-ping1,CHEN Lian-sheng1. Effect of carbide evolution on Lüders behavior of cold rolled ART 0.1C-7Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 505-511. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
YANG Yu-dan,ZHAO Hong-shan,LIU Teng-shi,DONG Han. Microstructure and properties of new high-carbon martensitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 135-142. |
[5] |
SU Chong-tao,GUO Xiao-jing,ZOU Hai-xia,ZHAO Guang-dong. Detection and analysis of microstructure of cold rolled dual phase steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 17-. |
[6] |
LI Dong-hui, XIAO Mao-guo, SUN Hao, HE Wen-chao, ZHANG Xu, LI Shao-hong. Effects of deep cryogenic treatment on microstructure and thermal stability of H13 steel[J]. Iron and Steel, 2020, 55(2): 95-102. |
|
|
|
|