Influence of initial temperature difference on high strength strip buckling in laminar cooling |
SONG Xiao-fang,HE An-rui,QIU Zeng-shuai |
(Engineering Research Institute,University of Science and Technology Beijing,Beijing 100083,China) |
|
|
Abstract Because of bilateral wave on high strength strip after laminar cooling for high temperature difference between edge and central area,initial temperature difference experimental devices were built up to measure residual stress in the length direction under different conditions. Then,the model of strip stability analysis was built,and analytical method was used to calculate the critical residual stress when the buckling of strip happens. According to the critical residual stress and fit result of initial temperature difference and residual stress,the critical initial temperature difference was calculated,which is 40 ℃ and the result is important to guide the production.
|
Received: 22 July 2015
Published: 26 April 2016
|
|
|
|
|
[2] |
董 峰.热轧带钢层流冷却过程板形研究[D].燕山:燕山大学,2014.
|
[1] |
王澜,曹建国,贾生晖,等.冷轧带钢板形屈曲变形失稳限的有限元分析[J]. 中南大学学报(自然科学版),2007,38(6):1157-1161.
|
[3] |
陈银莉,余 伟,等.热轧带钢层流冷却过程中残余应力分析[J].材料热处理学报,2010,31(6):155-160.
|
[2] |
董 峰.热轧带钢层流冷却过程板形研究[D].燕山:燕山大学,2014.
|
[4] |
苏艳萍,杨 荃,何安瑞,等.热轧带钢层流冷却过程中的热力耦合求解[J].重型机械,2007,4:30-34.
|
[3] |
陈银莉,余 伟,等.热轧带钢层流冷却过程中残余应力分析[J].材料热处理学报,2010,31(6):155-160.
|
[5] |
万仁保.层流冷却过程中热轧带钢的应力及计算机仿真[J].热加工工艺,2015,44(5):150-156.
|
[4] |
苏艳萍,杨 荃,何安瑞,等.热轧带钢层流冷却过程中的热力耦合求解[J].重型机械,2007,4:30-34.
|
[6] |
韩 斌,佘广夫,等.热轧板带钢冷却过程中热力耦合计算及变形分析[J].钢铁,2005,40(4):39-56.
|
[5] |
万仁保.层流冷却过程中热轧带钢的应力及计算机仿真[J].热加工工艺,2015,44(5):150-156.
|
[7] |
朱冬梅,刘国勇,等.中厚板冷却过程中热残余应力的控制[J].北京科技大学学报,2008,30(8):947-951.
|
[6] |
韩 斌,佘广夫,等.热轧板带钢冷却过程中热力耦合计算及变形分析[J].钢铁,2005,40(4):39-56.
|
[8] |
张清东,刘赟赟,周晓敏,等.高温带钢的局部宽度内压屈曲及后屈曲分析[J].机械工程学报,2005,41(3):102-106.
|
[7] |
朱冬梅,刘国勇,等.中厚板冷却过程中热残余应力的控制[J].北京科技大学学报,2008,30(8):947-951.
|
[8] |
张清东,刘赟赟,周晓敏,等.高温带钢的局部宽度内压屈曲及后屈曲分析[J].机械工程学报,2005,41(3):102-106.
|
[9] |
WISTREICH J G. Control of strip shape during cold rolling[J].Journal of the Iron and Steel Institute, 1968, 206(12):1203-1206.
|
[9] |
WISTREICH J G. Control of strip shape during cold rolling[J].Journal of the Iron and Steel Institute, 1968, 206(12):1203-1206.
|
[10] |
杨 荃,陈先霖.冷轧带材的屈曲理论及其在冷轧机板形控制中的应用[J]. 冶金设备,1994,(1): 1-4.
|
[10] |
杨 荃,陈先霖.冷轧带材的屈曲理论及其在冷轧机板形控制中的应用[J]. 冶金设备,1994,(1): 1-4.
|
[11] |
吴连元.板壳理论[M].上海:上海交通大学出版社,1989:11-59,419-513.
|
[11] |
吴连元.板壳理论[M].上海:上海交通大学出版社,1989:11-59,419-513.
|
[12] |
戴杰涛,张清东. 冷轧薄板中浪板形缺陷的屈曲及后屈曲理论与轧制试验研究[J].机械工程学报,2011,47(2): 44-50.
|
[12] |
戴杰涛,张清东. 冷轧薄板中浪板形缺陷的屈曲及后屈曲理论与轧制试验研究[J].机械工程学报,2011,47(2): 44-50.
|
[13] |
林振波.冷带轧机板形判别模型的有限条分析[D].秦皇岛:燕山大学,1993.
|
[13] |
林振波.冷带轧机板形判别模型的有限条分析[D].秦皇岛:燕山大学,1993.
|
[14] |
卿伟杰 ,杨荃.冷轧带钢整体和局部屈曲及后屈曲的有限元分析[J].北京科技大学学报,2000,22(4):377-380.
|
[14] |
卿伟杰 ,杨荃.冷轧带钢整体和局部屈曲及后屈曲的有限元分析[J].北京科技大学学报,2000,22(4):377-380.
|
[15] |
陈 骥.钢结构稳定理论与设计[M].北京:科学出版社,2001:1.
|
[15] |
陈 骥.钢结构稳定理论与设计[M].北京:科学出版社,2001:1.
|
[1] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[2] |
. 本钢三连铸的单流宽板坯连铸机从达涅利公司引进,于2008年12月4日建成投产,结晶器液位控制采用NKK技术。本文介绍了7#连铸机生产过程中,结晶器液位出现不稳定性波浪的原因,并通过改进NKK液位控制工艺,微调PID控制参数,以及优化结晶器流场等措施,提高了宽幅汽车板生产时的结晶器液位控制精度,并且解决和消除了不稳定型波浪的问题,使宽幅汽车板的轧制成材率大幅提升。[J]. , 2020, 45(2): 0-0. |
[3] |
Gan-Shui ZHOU. Diagnosis of instability during trial production of the billet continuous casting in a steel factory in Vietnam[J]. , 2020, 45(2): 0-0. |
[4] |
ZHANG Yu-cheng,WEN Juan,CUI Gui-bin,JIA Hui-ping,QI Qi-ge,JU Xin-hua. Analysis of microstructure and stability of retained austenitein X90 pipeline steel[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(4): 6-11. |
[5] |
LIU Chun-quan1,2,PENG Qi-chun1,2,XUE Zheng-liang1,2,LI Jian-li1,2,ZHU Hang-yu1,2. Effect of different heat treatment processes on microstructure and mechanical properties of Nb-Mo microalloyed medium-Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(12): 1100-1114. |
[6] |
JING Jia-qiang,GUO Jie,,LIU Qing-you,HOU Wei. Research progress of low temperature’s effect on pipeline steel stability and welding technology[J]. Iron and Steel, 2018, 53(8): 8-14. |
|
|
|
|