Effect of heat treatment process on critical transformation and CCT curve of AISI4340 steel |
WANG Chun-fang1,LI Yong2,LI Nan1,LU Yan1, LI Ji-kang1 |
(1. Center Laboratory, Central Iron and Steel Research Institute, Beijing 100081, China 2. Institute for Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China) |
|
|
Abstract The critical transformation temperature of AISI4340 steel was determined by thermal expansion method, and the microstructure and hardness were observed. The effects of heat treatment process on critical temperature and austenite continuous cooling transformation curve(CCT curve) were studied. The results show that the hardenability of the experimental steel is good. The austenite transformation product is bainite when the cooling rate is 0.03 ℃/s. The austenite transformation products are marensite and bainite when the cooling rates lie in range of 0.03-0.78 ℃/s and martensite when the cooling rate is greater than 0.78 ℃/s.[Ac1]and[Ac3]are different with different heat treatment processes and CCT curve is similar.[Ac1]of the unstability initial microstructure is lower than the equilibrium initial microstructure. Effect of different initial microstructure to[Ac1]is larger than[Ac3.]
|
Received: 06 July 2016
Published: 10 March 2017
|
|
|
|
[1] |
周乐育, 刘雅政, 方圆等.对———双相钢相变规律、组织和性能的影响[J].钢铁, 2008, 43(7):76-80
|
[1] |
周乐育, 刘雅政, 方圆等.对———双相钢相变规律、组织和性能的影响[J].钢铁, 2008, 43(7):76-80
|
[2] |
Terzic A, Calcagnotto M, Guk S, et al.In?uence of Boron on Transformation Behavior during Continuous Cooling of Low Alloyed Steels[J]. Materials Science and Engineering A., 2013, 584:32–40.[J].Materials Science and Engineering A, 2013, 584(1):32-40
|
[2] |
Terzic A, Calcagnotto M, Guk S, et al.In?uence of Boron on Transformation Behavior during Continuous Cooling of Low Alloyed Steels[J]. Materials Science and Engineering A., 2013, 584:32–40.[J].Materials Science and Engineering A, 2013, 584(1):32-40
|
[3] |
魏 伟,单以银,杨 柯,等.添加 - 对超高强度管线钢相变组织的影响[J].金属学报, 2007, 43(9):943-948
|
[3] |
魏 伟,单以银,杨 柯,等.添加 - 对超高强度管线钢相变组织的影响[J].金属学报, 2007, 43(9):943-948
|
[4] |
LEE S, NA H, KIM B, et al.Effect of Niobium on the Ferrite Continuous-Cooling Transformation (CCT) Curve of Ultrahigh-Thickness Cr-Mo Steel[J].Metallurgical and Materials Transactions A, 2013, 44A(6):2523-2532
|
[4] |
LEE S, NA H, KIM B, et al.Effect of Niobium on the Ferrite Continuous-Cooling Transformation (CCT) Curve of Ultrahigh-Thickness Cr-Mo Steel[J].Metallurgical and Materials Transactions A, 2013, 44A(6):2523-2532
|
[5] |
Hanamura T, Torizuka S, Tamura S, et al.Effect of Austenite Grain Size on Transformation Behavior,Microstructure and Mechanical Properties of 01C–5Mn Martensitic Steel[J].ISIJ International, 2013, 53(12):2218-2225
|
[5] |
Hanamura T, Torizuka S, Tamura S, et al.Effect of Austenite Grain Size on Transformation Behavior,Microstructure and Mechanical Properties of 01C–5Mn Martensitic Steel[J].ISIJ International, 2013, 53(12):2218-2225
|
[6] |
王春芳,路岩,赵晓丽.热膨胀法在钢铁材料固态相变研究中的应用,钢铁研究学报,2015,vol 27, 11, 1-5。[J].钢铁研究学报, 2015, 27(11):1-5
|
[6] |
王春芳,路岩,赵晓丽.热膨胀法在钢铁材料固态相变研究中的应用,钢铁研究学报,2015,vol 27, 11, 1-5。[J].钢铁研究学报, 2015, 27(11):1-5
|
[1] |
XU De-chao1,2, ZHANG Bo-ming, WANG Peng-tao, LI Run-chang,TENG Hua-xiang. Effect of Si and Mn on continuous cooling transformation behavior of hot forming steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 1-. |
[2] |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
[3] |
HAN Yi, XIAO Yao, ZHANG Ao-yin, ZHAO Yu-fei, LIU Feng, LI Hong-bin. Recessive defects in electromagnetic heating process of electrical resistance welding steel pipe[J]. Iron and Steel, 2020, 55(1): 108-118. |
[4] |
ZHANG Ke,YE Xiao-yu,LI Zhao-dong,SUN Xin-jun,HUANG Zhenyi. Microstructure and properties of continuous cooling transformation of TiMo ferritic high strength steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 733-740. |
[5] |
REN Ze,CHEN Xu,DONG Pei,LIAN Jingbao. Effect of heat treatment process on microstructure and #br# tensile properties of super 13Cr stainless steel[J]. Iron and Steel, 2019, 54(7): 68-76. |
[6] |
ZHAO Baochun,ZHANG Tao,LI Guiyan,LIN Tianzi,YAN Pingyuan. Continuous cooling transformation behavior and modeling of #br# hot deformed austenite in a HSLA steel[J]. Iron and Steel, 2019, 54(7): 98-102. |
|
|
|
|