30MnVS非调质钢的开发

doi:10.13228/j.boyuan.issn0449-749x.20160285

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract 30MnVS non-quenched and tempered steel for direct cutting is produced by the following processes： 100 t electric arc furnace smelting→LF＋VD refining→320 mm×480 mm bloom continuous casting with soft reduction-controlled rolling and cooling process. The rational chemical composition has been formulated， Other measurements， such as the critical processes of the EAF end-point control， the deoxidization by producing white slag in LF， the addition of nitrogen and sulfur， the modification of sulphide and the casting with full protection at the low overheating temperature， etc. were proposed. The carbon difference on the cross section of steel bar was approximately 0.02%， and the grain size maitained No. 10 grade. Thus， the steel had an excellent combination of strength and toughness， as well as high thermal stability. The impact energy of as rolled steel bar was higher than 160 J. The yield strength was above 620 MPa， the impact energy was above 120 J， and the elongation was higher than 20% after normalizing at 1 160-1 200 ℃， which were much better than that of normal non-quenched and tempered steel.

Received: 29 June 2016 Published: 10 March 2017

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHOU Lei

Cite this article:

ZHOU Lei. Development of 30MnVS non-quenched and tempered steel[J]. Iron and Steel, 2017, 52(3): 76-81.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20160285 OR http://www.chinamet.cn/Jweb_gt/EN/Y2017/V52/I3/76

[1]	宋宇,武国平,吴天礼. 氧化物冶金技术在改善钢材组织和性能中的应用[J]. 中国冶金，2012，6(22):1
[1]	宋宇,武国平,吴天礼. 氧化物冶金技术在改善钢材组织和性能中的应用[J]. 中国冶金，2012，6(22):1
[2]	Shim J H, Cho Y W, Nucleation of intragranular Ferrite at Ti2O3 particle in Low carbon steels [J]. Mater Trans., 2000, 41(12):1663.
[2]	Shim J H, Cho Y W, Nucleation of intragranular Ferrite at Ti2O3 particle in Low carbon steels [J]. Mater Trans., 2000, 41(12):1663.
[3]	常开地，王萍，刘卫萍. 非调质钢的发展现状和应用进展[J]. 金属热处理，2011，36(3)：80
[3]	常开地，王萍，刘卫萍. 非调质钢的发展现状和应用进展[J]. 金属热处理，2011，36(3)：80
[4]	蔡爱国，王瑞珍，庞干云，章洪涛. 易切削妮钒复合微合金中碳钢的研究[J]. 钢铁，1995，30：80
[4]	蔡爱国，王瑞珍，庞干云，章洪涛. 易切削妮钒复合微合金中碳钢的研究[J]. 钢铁，1995，30：80
[5]	Al Hajeri K F, Garcia C I, Hua M J, et al. Particle stimulated Nucleation of Ferrite in Heavy Steel Section [J]. ISIJ Int., 2006, 46(8):1233
[5]	Al Hajeri K F, Garcia C I, Hua M J, et al. Particle stimulated Nucleation of Ferrite in Heavy Steel Section [J]. ISIJ Int., 2006, 46(8):1233
[6]	Wu K, Li Z G. Microstructure Evolution in a Low Carbon Nb-Ti Micro-alloyed Steel [J]. ISIJ International, 2006, 46(1):161
[6]	Wu K, Li Z G. Microstructure Evolution in a Low Carbon Nb-Ti Micro-alloyed Steel [J]. ISIJ International, 2006, 46(1):161
[7]	Goro MIY AMOTO, Ryota HORI, et al. Interface precipitation of VC and resultant hardening in V-added medium carbon steels [J]. ISIJ International, 2011, 51(10):1733
[7]	Goro MIY AMOTO, Ryota HORI, et al. Interface precipitation of VC and resultant hardening in V-added medium carbon steels [J]. ISIJ International, 2011, 51(10):1733
[8]	谢文新王新社卢明霞曹红福李芸. 非调质钢48MnV的研制[J]. 特殊钢,2009,30(3)：44-45
[8]	谢文新王新社卢明霞曹红福李芸. 非调质钢48MnV的研制[J]. 特殊钢,2009,30(3)：44-45
[9]	马福昌，刘永龙，宋瑞甫，郑京辉. Nb、V、Ti微合金元素对连铸坯表面质量的影响[J]. 宽厚板,2003,9(4)：14-18
[9]	马福昌，刘永龙，宋瑞甫，郑京辉. Nb、V、Ti微合金元素对连铸坯表面质量的影响[J]. 宽厚板,2003,9(4)：14-18
[10]	刘乐东. 硫系易切削钢氧化物和硫化物变性的分析[J]. 特钢技术，2011,17(67):40
[10]	刘乐东. 硫系易切削钢氧化物和硫化物变性的分析[J]. 特钢技术，2011,17(67):40
[11]	吴夜明，姚留枋. 电磁搅拌对铸坯化学成分偏析影响机理[J]. 特殊钢,1999,20(3):13
[11]	吴夜明，姚留枋. 电磁搅拌对铸坯化学成分偏析影响机理[J]. 特殊钢,1999,20(3):13
[12]	周蕾程维玮南钢合金结构钢工艺改进实践[J]. 物理测试，2012,30（3）：22
[12]	周蕾程维玮南钢合金结构钢工艺改进实践[J]. 物理测试，2012,30（3）：22
[13]	非调质钢奥氏体动态再结晶研究王进、褚忠、陈军材料导报 2010 24（11）：116-118
[13]	非调质钢奥氏体动态再结晶研究王进、褚忠、陈军材料导报 2010 24（11）：116-118
[14]	F45V非调质钢动态再结晶模型及数值模拟马文龙，王　进１，王宝平１，许德鹏１，陈学文锻压技术 2013 38（2）138-142
[14]	F45V非调质钢动态再结晶模型及数值模拟马文龙，王　进１，王宝平１，许德鹏１，陈学文锻压技术 2013 38（2）138-142