Improvement of quality of 320 mm×410 mm bloom in continuous casting of railway steel and its application |
CHEN Liang1,2,SONG Bo1,CHEN Tian-ming2,LI Yang-zhou3,LI Zhi-qiang2,LI Jian-quan3 |
(1. School of Metallurgyical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Pangang Group Research Institute Co., Ltd., Chengdu 611731, Sichuan, China 3. Steel and Vanadium Co., Ltd., Pangang Group, Panzhihua 617022, Sichuan, China) |
|
|
Abstract In order to improve the inner quality of bloom of railway steels and meet the requirement of rail flaw inspection. Appropriate secondary cooling system, F-EMS, dynamic soft reduction technology, control of molten steel superheat and casting speed were put forward to solve the segregation and center porosity of railway steel bloom in current study. The producing technology of 320 mm×410 mm continuous bloom of railway steel was established based on the above. The center equiaxial crystal rate of bloom was steadily controlled not less than 40%. The rate of center porosity that was not more than 0.5 level was above 91%. The rate of center segregation that was not more than 0.5 level was above 87%. Carbon segregation index of bloom ranged from 0.95 to 1.07. The quality of bloom and steel rail produced is better and can meet the requirement of CRCC。
|
Received: 07 July 2016
Published: 18 April 2017
|
|
|
|
|
[1] |
沈峰, 吴夜明, 张兴中, 等.国内外连铸生产重轨钢的工艺及特点[J]. 连铸, 2006, 03:1-6
|
[1] |
沈峰, 吴夜明, 张兴中, 等.国内外连铸生产重轨钢的工艺及特点[J]. 连铸, 2006, 03:1-6
|
[2] |
王玉昌, 张家泉.高速重轨钢洁净度与均质性控制关键技术[J]. 中国冶金, 2015, 04:7-11.
|
[2] |
王玉昌, 张家泉.高速重轨钢洁净度与均质性控制关键技术[J]. 中国冶金, 2015, 04:7-11.
|
[3] |
陈光友, 冯文圣, 李小明, 等.重轨钢连铸工艺优化[J]. 连铸, 2011, S1:99-102.
|
[3] |
陈光友, 冯文圣, 李小明, 等.重轨钢连铸工艺优化[J]. 连铸, 2011, S1:99-102.
|
[4] |
段永卿, 王建锋, 郭朝军.重轨钢连铸坯中心偏析的分析和工艺改进[J]. 特殊钢, 2016, 01:25-28
|
[4] |
段永卿, 王建锋, 郭朝军.重轨钢连铸坯中心偏析的分析和工艺改进[J]. 特殊钢, 2016, 01:25-28
|
[5] |
陈永, 杨素波.重轨钢连铸坯内部质量控制技术[J]. 钢铁研究学报, 2007, 10:16-20.
|
[5] |
陈永, 杨素波.重轨钢连铸坯内部质量控制技术[J]. 钢铁研究学报, 2007, 10:16-20.
|
[6] |
陈永.重轨钢连铸的质量控制[J]. 钢铁, 2004, 03:23-26.
|
[6] |
陈永.重轨钢连铸的质量控制[J]. 钢铁, 2004, 03:23-26.
|
[7] |
陈永, 李桂军, 苟淑云.提高重轨钢连铸大方坯质量的技术[J]. 钢铁钒钛, 2002, 04:41-46.
|
[7] |
陈永, 李桂军, 苟淑云.提高重轨钢连铸大方坯质量的技术[J]. 钢铁钒钛, 2002, 04:41-46.
|
[8] |
张楠.末端电磁搅拌对钢连铸坯成分偏析及缩松影响的模拟研究[D].大连理工大学, 2012:17.
|
[8] |
张楠.末端电磁搅拌对钢连铸坯成分偏析及缩松影响的模拟研究[D].大连理工大学, 2012:17.
|
[9] |
王晓东.重轨钢连铸大方坯轻压下的分析研究[D].内蒙古科技大学, 2007:9-10.
|
[9] |
王晓东.重轨钢连铸大方坯轻压下的分析研究[D].内蒙古科技大学, 2007:9-10.
|
[10] |
钱刚, 阮小江, 蔡燮鳌.连铸轴承钢大方坯中心偏析的成因及对策[J]. 钢铁, 2002, 05:16-18.
|
[10] |
钱刚, 阮小江, 蔡燮鳌.连铸轴承钢大方坯中心偏析的成因及对策[J]. 钢铁, 2002, 05:16-18.
|
[1] |
WANG Xing-yu, HAN Yan-shen, LIU Qing, XIAO Dong,CHEN Jun, GUAN Min. Effect of F-EMS on inner quality of spring steel continuous casting billet[J]. Iron and Steel, 2020, 55(5): 59-67. |
[2] |
. Formation reasons and control measures of abnormal oscillation marks for 10B21 cold-heading steel billets[J]. , 2020, 45(3): 0-0. |
[3] |
chishirong chishirongchishirong. [J]. , 2020, 45(3): 0-0. |
[4] |
LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22. |
[5] |
ZHANG Si-yuan1,2,LONG Mu-jun1,2,AI Song-yuan1,2,TAN Kai1,2,CHEN Deng-fu1,2,HUANG Yun-wei1,2. Oxidation behavior of continuous casting slabs and its effect on temperature during cooling process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 129-134. |
[6] |
. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0. |
|
|
|
|