Development and application on non-quenched and tempered steel for high strength fasteners |
WANG Li-jun1,2,RUAN Shi-peng1,2,WANG Ning-tao1,2,ZHAI Jin-po1,2, ZHANG Su-ping1,2,WANG Jing1,2 |
(1. Technology Center, Xingtai Iron and Steel Co., Ltd., Xingtai 054027, Hebei, China 2. Hebei Engineering Research Center for Wire Rod, Xingtai 054027, Hebei, China) |
|
|
Abstract In order to develop energy-saving non quenched and tempered cold heading steel with high strength,high toughness and good processability,non-quenched and tempered steel for high strength fasteners was produced by “BOF-LF-CC-controlling rolling and cooling” process. The microstructure and properties,drawing process,aging process of test steel were studied. The results showed that the steel was fine ferrite and pearlite,the tensile strength and elongation ratio of the steel were respectively 739 MPa and 22.2%. The tensile strength could meet the demand of 9.8 and 10.9 stage bolt when drawing reductions respectively at the range of 15%-25% and 30%-40%. As the aging temperature increased, the tensile strength and hardness initially increased and then decreased after 150-450 ℃ aging. The tensile strength and hardness reaches a maximum value. The tensile strength and hardness increased with aging time increased after 0-2 h at 250 ℃. When the drawing reduction is 40%,the steel can bear the compression of 24.6% height ratio of front and back without cracking.
|
Received: 19 March 2018
Published: 20 November 2018
|
|
|
|
|
[1] |
王瑞珍,章洪涛.微合金非调质紧固件用钢[J].机械工程材料, 1993, 17(3):6-8
|
[1] |
王瑞珍,章洪涛.微合金非调质紧固件用钢[J].机械工程材料, 1993, 17(3):6-8
|
[2] |
曹杰,刘雅政,阎军,等.高强度非调质冷镦钢研究和开发现状[J].特殊钢, 2010, 31(5):26-27
|
[2] |
曹杰,刘雅政,阎军,等.高强度非调质冷镦钢研究和开发现状[J].特殊钢, 2010, 31(5):26-27
|
[3] |
董成瑞,任海鹏,金同哲,等.微合金化非调质钢[M]. 北京:冶金工业出版社,2000:223.(Dong Cheng-rui, Ren Hai-peng, Jin Tong-zhe, et al. Nonquenched Microalloyed steel[M]. Beijing: Metallurgical Industry Press, 2000:223. )
|
[3] |
董成瑞,任海鹏,金同哲,等.微合金化非调质钢[M]. 北京:冶金工业出版社,2000:223.(Dong Cheng-rui, Ren Hai-peng, Jin Tong-zhe, et al. Nonquenched Microalloyed steel[M]. Beijing: Metallurgical Industry Press, 2000:223. )
|
[4] |
杨金峰,惠卫军,于同仁,等.时效温度对贝氏体型冷作强化非调质钢力学性能的影响[J].钢铁, 2011, 46(10):84-85
|
[4] |
杨金峰,惠卫军,于同仁,等.时效温度对贝氏体型冷作强化非调质钢力学性能的影响[J].钢铁, 2011, 46(10):84-85
|
[5] |
蔡路,赵秀明,贺显聪.时效工艺对非调质钢螺栓组织和性能的影响[J].钢铁, 2010, 45(3):75-77
|
[5] |
蔡路,赵秀明,贺显聪.时效工艺对非调质钢螺栓组织和性能的影响[J].钢铁, 2010, 45(3):75-77
|
[6] |
毛向阳,王章忠,蔡路,等.低温时效对非调质钢组织和耐疲劳性能的影响[J].钢铁研究学报, 2013, 25(2):56-57
|
[6] |
毛向阳,王章忠,蔡路,等.低温时效对非调质钢组织和耐疲劳性能的影响[J].钢铁研究学报, 2013, 25(2):56-57
|
[7] |
罗志俊,李舒笳,孙齐松,等.静态载荷下非调质钢高强螺栓的变形行为[J].材料热处理学报, 2016, 37(11):119-121
|
[7] |
罗志俊,李舒笳,孙齐松,等.静态载荷下非调质钢高强螺栓的变形行为[J].材料热处理学报, 2016, 37(11):119-121
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
SUN Chao-fan, FANG Yuan, WANG Ya-qing, LIU Wei. Influence of temper rolling reduction rate on microstructure and mechanical properties of TS290 steel[J]. Iron and Steel, 2020, 55(6): 75-79. |
[3] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[4] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
[5] |
SHAO Chun-juan,ZHEN Fan,ZHANG Ji-ming,QU Jin-bo,ZHANG Lei. Effect of sample thinning on DWTT property of heavy wall X80 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 497-504. |
[6] |
LI Xiao-yuan,SHI Jie. Ballistic behavior of high strength steel targets during high speed impact of projectile[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 429-436. |
|
|
|
|