Development and application of desulfurization process for 180 t RH vacuum refining furnace |
ZHAO Jia-qi,CAI Xiao-feng,ZOU Chang-dong |
(Institute of Research of Iron and Steel, Jiangsu Province(Shasteel), Zhangjiagang 215625, Jiangsu, China) |
|
|
Abstract The desulfurization technology in the RH process was developed to reducethe sulfur mass percent in the non-oriented silicon steel. The desulfurization degree was controlled at 30%-60% in a RH reactor, and the ratio of in the W800 non-oriented silicon steel with[w([S])≤0.005 0%] was increased from 72.19% upto 98%. Meanwhile, this process was able to ensure that [w(T[O])<]0.002 0% and[w([N])<]0.001 5% at the end of the RH treatment. Through the slag deoxy-modification during the tapping and the RH treatment,[w((TFe))]at the end of the RH treatment was controlled below 3%. The slag basicity was kept above 5.0, and the sulfur distribution ratio between slag and steel was controlled at 80-260,which is favored to the improvement of the desulfurization process in the RH treatment.
|
Received: 28 March 2018
Published: 20 November 2018
|
|
|
|
[1] |
Boc I. Correlation of Aluminum Content Inclusion Structure and Core Loss of Non-oriented Electrical Steel[J]. Appl. Phys. 1986,64(10):53-50.
|
[1] |
Boc I. Correlation of Aluminum Content Inclusion Structure and Core Loss of Non-oriented Electrical Steel[J]. Appl. Phys. 1986,64(10):53-50.
|
[2] |
吴爽,樊立峰,毛一标,等.高牌号无取向电工钢中硫化物、氮化物析出的热力学分析[J].冶金丛刊,2009,180(2):13-15.
|
[2] |
吴爽,樊立峰,毛一标,等.高牌号无取向电工钢中硫化物、氮化物析出的热力学分析[J].冶金丛刊,2009,180(2):13-15.
|
[3] |
Okada Y, FukagawaS, ledaK, et al.Development of RH Powder Top Blowing Process[J].ISIJ,1994,80(1):9-12.
|
[3] |
Okada Y, FukagawaS, ledaK, et al.Development of RH Powder Top Blowing Process[J].ISIJ,1994,80(1):9-12.
|
[4] |
区铁,刘振清,刘良田,等.RH装置的粉剂顶吹脱硫[J].钢铁,2006,41(2):250-255.
|
[4] |
区铁,刘振清,刘良田,等.RH装置的粉剂顶吹脱硫[J].钢铁,2006,41(2):250-255.
|
[5] |
艾立群,蔡开科.RH处理过程钢液脱硫[J].炼钢,2001,17(3):53-57.
|
[5] |
艾立群,蔡开科.RH处理过程钢液脱硫[J].炼钢,2001,17(3):53-57.
|
[6] |
徐匡迪.关于洁净钢的若干基本问题[J].金属学报,2009,45(3):257-269.
|
[6] |
徐匡迪.关于洁净钢的若干基本问题[J].金属学报,2009,45(3):257-269.
|
[7] |
区铁,周国治,刘建功.RH法的脱碳及脱硫速率[J].炼钢,2000,16(2):57-62.
|
[7] |
区铁,周国治,刘建功.RH法的脱碳及脱硫速率[J].炼钢,2000,16(2):57-62.
|
[8] |
赵家七,邹长东,耿涛,等.炉渣脱氧改质工艺对铝镇静硅钢总氧含量的影响[J].炼钢,2016.32(2):12-17.
|
[8] |
赵家七,邹长东,耿涛,等.炉渣脱氧改质工艺对铝镇静硅钢总氧含量的影响[J].炼钢,2016.32(2):12-17.
|
[9] |
邹长东,耿涛,周彦召,赵家七,等.沙钢管线钢LF精炼的低成本深脱硫工艺[J].钢铁,2012.47(11):36-40.
|
[9] |
邹长东,耿涛,周彦召,赵家七,等.沙钢管线钢LF精炼的低成本深脱硫工艺[J].钢铁,2012.47(11):36-40.
|
[10] |
Ogura Y, Kikuchi Y, Hasegawa T, et al. Development of Secondary Refining Process and Its
|
[10] |
Ogura Y, Kikuchi Y, Hasegawa T, et al. Development of Secondary Refining Process and Its
|
|
Application to Production of Clean Steel [J]. Tetsu-to-Hagane, 1986, 72 (9): 1309-1315.
|
|
Application to Production of Clean Steel [J]. Tetsu-to-Hagane, 1986, 72 (9): 1309-1315.
|
[11] |
Endoh K, Kaneko T,Nagata S, et al. Effect of MgO content in CaO-CaF2 based flux on desulphurization of steel[J].ISIJ,1986,72(12):1108.
|
[11] |
Endoh K, Kaneko T,Nagata S, et al. Effect of MgO content in CaO-CaF2 based flux on desulphurization of steel[J].ISIJ,1986,72(12):1108.
|
[12] |
于学斌,时启龙,陈清泉,等.RH用新型脱硫剂的开发[J].炼钢,2006,22(4):51-54.
|
[12] |
于学斌,时启龙,陈清泉,等.RH用新型脱硫剂的开发[J].炼钢,2006,22(4):51-54.
|
[13] |
张才贵,吴旭峰,韩乃川.预熔型RH脱硫剂的开发与应用[J].炼钢,2009,25(6):26-28.
|
[13] |
张才贵,吴旭峰,韩乃川.预熔型RH脱硫剂的开发与应用[J].炼钢,2009,25(6):26-28.
|
[14] |
Endoh K, Kaneko T,Nagata S, et al. Effects of some factors on desulphurization by RH-injection method [J].ISIJ,1986,72(4):263.
|
[14] |
Endoh K, Kaneko T,Nagata S, et al. Effects of some factors on desulphurization by RH-injection method [J].ISIJ,1986,72(4):263.
|
[1] |
LI Zhao-zhen, SONG Xin-li, LIU Jing, CHENG Zhao-yang, BI Yun-jie, JIA Juan. Effect of Cr,Mn and annealing temperature on properties of non-oriented silicon steel[J]. Iron and Steel, 2020, 55(5): 80-86. |
[2] |
LIU Qing-song, PEI Ying-hao, SHI Li-fa, XIA Xue-lan, HE Zhi-jian, CHENG Guo-qing. Effect of annealing tension on magnetic anisotropy of Fe-3.0%Si non-oriented silicon steel[J]. Iron and Steel, 2020, 55(4): 95-99. |
[3] |
ZHU Cheng-yi1,2,HUANG Luo-yi1,2,LUO Xiao-yan1,2,LIU Yu-long1,2,WANG Yong1,2,LI Guang-qiang1,3. Effect of calcium treatment on characteristics of inclusions in finished non-oriented silicon steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 117-128. |
[4] |
YIN Chuan-lei, YANG Li-mei, TIAN Chun-yang, MA Jian-chao. Analysis of KR hot metal desulfurizer escaped and slag agglomeration in agitator[J]. Iron and Steel, 2020, 55(1): 34-37. |
[5] |
ZENG Jianhua,ZHANG Min,WU Guorong,XIE Xin. Inclusions control technology in smelting #br# process of 30Cr13 stainless steel[J]. Iron and Steel, 2019, 54(8): 43-47. |
[6] |
LIN Chao-yang,ZHU De-qing,GUO Zheng-qi. Application of waste desulphurization catalyst to iron ore sintering#br#[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(3): 272-279. |
|
|
|
|