锻态奥氏体基低密度钢的低温高速冲击力学行为

doi:10.13228/j.boyuan.issn0449-749x.20200390

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (2794 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to evaluate the ability of the as-forged austenite-based low-density steel to resist high-speed impact loading at low temperature,a low-temperature and high-speed impact test using a Split Hopkinson Pressure Bar (SHPB) apparatus at -50 ℃ and engineering strain rate of about 4 300 s^-1 was carried out on an as-forged austenite-based low-density steel sample of Fe-28.13Mn-10.04Al-1.05C (Mn28Al10) with dimensions of ø3.94 mm×2.88 mm. The mechanical behavior of the steel at low-temperature and high-speed impact loading was studied. The result showed that,the impacted sample experienced elastic deformation of about 18 μs,compression plastic deformation of about 110 μs,tensile plastic deformation of about 20 μs and fracture under the above-mentioned experimental process. The plastic energy and the adiabatic temperature rise of the impacted sample before fracture were about 1 558 J/cm³ and 178 ℃,respectively. The stress-strain curve of the impacted sample showing a typical strain-strengthening characteristic,and the existence of adiabatic temperature rise made the stress-strain curve showed fluctuation phenomenon. The impacted sample was broken down into three fragments,which were induced mainly by compression plastic deformation and tensile plastic deformation. The fracture showed compression zone and tensile zone,both of which belong to ductile fracture characterized by the dimple. The substructures of the deformation zone near the compression zone and the tensile zone were all high-density movable dislocations. The dislocation density of the compression deformation zone is lower than that of the tension deformation zone,and the length and width of the high-density dislocation in the compression deformation zone were larger than that in the tension deformation zone. The deformation mechanism of the as-forged austenite-based low-density steel of Mn28Al10 at -50 ℃ and engineering strain rate of about 4 300 s^-1 was dislocation slip.

Key words： austenite-based low-density steel as-forged cryogenic temperature high-speed impact compressive loading mechanical behavior deformation mechanism

Received: 29 July 2020

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Ping
	HUANG Hua-qin
	LI Xiang
	XIE Qian
	HOU Qing-yu
	HUANG Zhen-yi

Cite this article:

WANG Ping,HUANG Hua-qin,LI Xiang等. Mechanical behavior of an as-forged austenite-based low-density steel under high-speed impact loading at cryogenic temperature[J]. Iron and Steel, 2021, 56(3): 111-119.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20200390 OR http://www.chinamet.cn/Jweb_gt/EN/Y2021/V56/I3/111

[1] Kayak G L. Fe-Mn-Al precipitation-hardening austenitic alloys[J]. Metal Science and Heat Treatment,1969,11(2):95.
[2] 曹文全,徐海峰,张明达,等. 新型低密度高强高韧热轧层状钢研发[J]. 钢铁,2016,51(9):1. (CAO Wen-quan,XU Hai-feng,ZHANG Ming-da,et al. Research and development of a new hot rolled laminated structure[J]. Iron and Steel,2016,51(9):1.)
[3] 高建兵,范思鹏,张树才,等. 新型超级奥氏体不锈钢654SMo偏析行为及均匀化工艺[J]. 钢铁,2018,53(8):83.(GAO Jian-bing,FAN Si-peng,ZHANG Shu-cai,et al. Segregation behavior and homogenization process of new super austenitic stainless steel 654SMO[J]. Iron and Steel,2018,53(8):83.)
[4] 邓泽,张立峰,杨文,等. Fe-22Mn-5Al-0.38C-0.55Si合金的微观组织及力学性能[J]. 中国冶金,2018,28(s1):46.(DENG Ze,ZHANG Li-feng,YANG Wen,et al. Microstructure and mechanical properties of Fe-22Mn-5Al-0.38C-0.55Si alloy[J]. China Metallurgy,2018,28(s1):46.)
[5] 戴鑫宇,方旭东,徐芳泓,等. 奥氏体耐热钢低周疲劳性能研究进展[J]. 钢铁,2020,55(3):58.(DAI Xin-yu,FANG Xu-dong,XU Fang-hong,et al. Research progress in low cycle fatigue performance of austenitic heat resistant steel[J]. Iron and Steel,2020,55(3):58.)
[6] Zambrano O A. A general perspective of Fe-Mn-Al-C steels[J]. Journal of Materials Science,2018,53(20):14003.
[7] Chen S,Rana R,Haldar A,et al. Current state of Fe-Mn-Al-C low density steels[J]. Progress in Materials Science,2017,89:345.
[8] Moon J,Ha H Y,Park S J,et al. Effect of Mo and Cr additions on the microstructure,mechanical properties and pitting corrosion resistance of austenitic Fe-30Mn-10.5Al-1.1C lightweight steels[J]. Journal of Alloys and Compounds,2019,775:1136.
[9] 王伟胜,朱航宇,宋明明,等. Fe-23Mn-xAl-0.7C低密度钢中非金属夹杂物形成机理[J]. 钢铁,2020,55(10):29. (WANG Wei-sheng,ZHU Hang-yu,SONG Ming-ming,et al. Formation mechanism of non-metallic inclusions in Fe-23Mn-xAl-0.7C lightweight steels[J]. Iron and Steel,2020,55(10):29.)
[10] ZHANG F C,FU R D,QIU L,et al. Microstructure and property of nitrogen-alloyed high manganese austenitic steel under high strain rate tension[J]. Materials Science and Engineering:A,2008,492(1/2):255.
[11] Sahu P,Curtze S,Das A,et al. Stability of austenite and quasi-adiabatic heating during high-strain-rate deformation of twinning-induced plasticity steels[J]. Scripta Materialia,2010,62(1):5.
[12] Howell R A,Montgomery J S,Aken D C V. Advancements in steel for weight reduction of P900 armor plate[J]. Iron and Steel Technology,2008,6(7):8.
[13] Howell R,Weerasooriya T,Van Aken D. Tensile,high strain rate compression and microstructural evaluation of lightweight age hardenable cast Fe-30Mn-9Al-XSi-0.9C-0.5Mo steel[J]. International Journal of Metalcasting,2010,4(1):7.
[14] Curtze S,Kuokkala V T. Dependence of tensile deformation behavior of TWIP steels on stacking fault energy,temperature and strain rate[J]. Acta Materialia,2010,58(15):5129.
[15] Park K T,Hwang S W,Ji J H,et al. Static and dynamic deformation of fully austenitic high Mn steels[J]. Procedia Engineering,2011,10:1002.
[16] Kim J,Lee S J,De Cooman B C. Effect of Al on the stacking fault energy of Fe-18Mn-0.6C twinning-induced plasticity[J]. Scripta Materialia,2011,65(4):363.
[17] Khosravifard A. Influence of high strain rates on the mechanical behavior of high-manganese steels[J]. Iranian Journal of Materials Forming,2014,1:1.
[18] Bartlett L N,Avila B R. Grain refinement in lightweight advanced high-strength steel castings[J]. International Journal of Metalcasting,2016,10(4):401.
[19] HUANG Z Y,HOU A L,JIANG Y S,et al. Rietveld refinement,microstructure,mechanical properties and oxidation characteristics of Fe-28Mn-xAl-1C(x=10 and 12wt.%) low-density steels[J]. Journal of Iron and Steel Research,International,2017,24(12):1190.
[20] HUANG Z Y,JIANG Y S,HOU Q Y,et al. Rietveld refinement,microstructure and high-temperature oxidation characteristics of low-density high manganese steels[J]. Journal of Materials Science and Technology,2017,33(12):1531.
[21] HOU Q Y,WANG J T. A modified Johnson-Cook constitutive model for Mg-Gd-Y alloy extended to a wide range of temperatures[J]. Computational Materials Science,2010,50(1):147.
[22] Kolsky H. An investigation of the mechanical properties of materials at very high rates of loading[J]. Proceedings of the Physical Society,2002,62:676.
[23] 王佳斌,丁军,宋鹍,等. 冲击载荷下20CrMnTi钢动态应力响应与考虑绝热温升修正J-C本构模型研究[J]. 机械强度,2019,41(5):1066. (WANG Jia-bin,DING Jun,SONG Kun,et al. Studied on dynamic stress response of 20CrMnTi steel under impact load and considered for adiabatic temperature rise modification of the J-C constitutive model[J]. Journal of Mechanical Strength,2019,41(5):1066.)
[24] Lewandowski C M,Coinvestigator N,Lewandowski C M. Split Hopkinson (Kolsky) Bar:Design,Testing and Applications[M]. Springer New York Dordrecht Heidelberg London:Springer US,2015.
[25] 钟群鹏,赵子华,张峥. 断口学的发展及微观断裂机理研究[J]. 机械强度,2005,27(3):358.(ZHONG Qun-peng,ZHAO Zi-hua,ZHANG Zheng. Development of "fractography" and research of fracture micromechanism[J]. Journal of Mechanical Strength,2005,27(3):358.)
[26] 姜锡山,赵晗. 钢铁显微断口速查手册[M]. 北京:机械工业出版社,2010.(JIANG Xi-shan,ZHAO Han. Manual for Quick Inspection of Micro Fracture of Iron and Steel[M]. Beijing:China Machine Press,2010.)
[27] Allain S,Chateau J P,Bouaziz O,et al. Correlations between the calculated stacking fault energy and the plasticity mechanisms in Fe-Mn-C alloys[J]. Materials Science and Engineering:A,2004,387/388/389:158.
[28] Park K T,Jin K G,Han SH,et al. Stacking fault energy and plastic deformation of fully austenitic high manganese steels:Effect of Al addition[J]. Materials Science and Engineering:A,2010,527(16/17):3651.
[29] Mahato B,Shee S K,Sahu T,et al. An effective stacking fault energy viewpoint on the formation of extended defects and their contribution to strain hardening in a Fe-Mn-Si-Al twinning-induced plasticity steel[J]. Acta Materialia,2015,86:69.
[30] Pierce D T,Jiménez J A,Bentley J,et al. The influence of stacking fault energy on the microstructural and strain-hardening evolution of Fe-Mn-Al-Si steels during tensile deformation[J]. Acta Materialia,2015,100:178.
[31] Kim C W,Terner M,Lee J H,et al. Partitioning of C into κ-carbides by Si addition and its effect on the initial deformation mechanism of Fe-Mn-Al-C lightweight steels[J]. Journal of Alloys and Compounds,2019,775:554.
[32] Frommeyer G,Brüx U. Microstructures and mechanical properties of high-strength Fe-Mn-Al-C light-weight triplex steels[J]. Steel Research International,2006,77:627.
[33] Yoo J D,Park K T. Microband-induced plasticity in a high Mn-Al-C light steel[J]. Materials Science and Engineering:A,2008,496(1/2):417.
[34] Kim H,Suh D-W,Kim NJ. Fe-Al-Mn-C lightweight structural alloys:A review on the microstructures and mechanical properties[J]. Science and Technology of Advanced Materials,2013,14(1):014205.
[35] Curtze S,Kuokkala V T,Oikari A,et al. Thermodynamic modeling of the stacking fault energy of austenitic steels[J]. Acta Materialia,2011,59(3):1068.
[36] Saeed-Akbari A,Imlau J,Prahl U,et al. Derivation and variation in composition-dependent stacking fault energy maps based on subregular solution model in high-manganese steels[J]. Metallurgical and Materials Transactions A,2009,40(13):3076.
[37] Dumay A,Chateau J P,Allain S,et al. Influence of addition elements on the stacking-fault energy and mechanical properties of an austenitic Fe-Mn-C steel[J]. Materials Science and Engineering:A,2008,483/484:184.
[38] YANG W S,WAN C M. The influence of aluminium content to the stacking fault energy in Fe-Mn-Al-C alloy system[J]. Journal of Materials Science,1990,25:1821.
[39] Zambrano O A. Stacking fault energy maps of Fe-Mn-Al-C-Si steels:Effect of temperature,grain size,and variations in compositions[J]. Journal of Engineering Materials and Technology,2016,138(4):041010.
[40] Bale C W,Bélisle E,Chartrand P,et al. FactSage thermochemical software and database—Recent developments[J]. Calphad,2009,33(2):295.