HRB400螺纹钢的高温氧化行为及动力学

doi:10.13228/j.boyuan.issn0449-749x.20210569

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (2519 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to optimize the oxide layer structure of HRB400 rebar to improve corrosion resistance, the oxidation behavior of test steel under air condition at temperatures of 800, 850, 900, 950, 1 000 and 1050 ℃ was investigated using the thermogravimetric method. An oxidation kinetic model was developed, the oxidation activation energy of test steel was calculated, and the structure and composition of oxide layer was analyzed and determined by scanning electron microscopy (SEM). The oxidation layer formation law was discussed in relation with the actual production of rebar and an oxidation skin growth model was established. The results showed that the oxidation of test steel had a fast oxidation phase with a linear oxidation kinetic curve in the early stages and a slow oxidation phase with a parabolic oxidation kinetic curve in the middle and late stages, and the time required to change from linear to parabolic increased with the temperature increasing. The oxidation activation energy of test steel was 208.4 kJ/mol which was calculated by Origin fitting. The best macroscopic condition of test steel oxide skin surface appeared at an oxidation temperature of 900 ℃, and varying degrees of flaking and damage to the test steel oxide skin at all other oxidation temperatures. At the oxidation temperatures of 850 and 900 ℃, only dark grey outer layer of Fe₃O₄ and light grey inner layer of FeO were observed in the test steel oxide due to the low oxidation temperature which could not break through the energy barrier for Fe₂O₃ production. The oxide skin of test steel at oxidation temperatures of 950, 1 000 and 1 050 ℃ consisted of a three-layer structure of Fe₂O₃, Fe₃O₄ and FeO. As the oxide skin undergone pre-eutectoid reaction (precipitation of Fe₃O₄ from FeO) and eutectoid reaction (transformation of FeO into Fe₃O₄ + Fe) during cooling, a complex oxide skin structure was resulted in.

Key words： HRB400 rebar oxidation kinetics oxide scale high temperature oxidation activation energy

Received: 17 September 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHOU Da-qian
	LU Heng-chang
	LI Zhi-feng
	WEI Xi-cheng
	DONG Han

Cite this article:

ZHOU Da-qian,LU Heng-chang,LI Zhi-feng等. High temperature oxidation behavior and kinetics of HRB400 rebar[J]. Iron and Steel, 2022, 57(3): 108-114.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20210569 OR http://www.chinamet.cn/Jweb_gt/EN/Y2022/V57/I3/108

[1] 李成刚, 单文超, 刘怡私, 等. 基于热轧全流程氧化铁皮控制的耐蚀性工艺[J].钢铁, 2021, 56(9):129.(LI Cheng-gang, SHAN Wen-chao, LIU Yi-si, et al. Corrosion resistance process based on iron oxide control throughout the hot rolling process[J]. Iron and Steel, 2021, 56(9):129.)
[2] 杨森. 高强度钢筋开发及抗锈蚀性研究[D]. 西安:西安建筑科技大学, 2015. (YANG Sen. Development of High-Strength Steel Bars and Research into Corrosion Resistance[D]. Xi′an: Xi′an University of Architecture and Technology, 2015.)
[3] 程兆, 俊宋丹, 江静华, 等. 混凝土中钢筋腐蚀与防护研究进展[J]. 热加工工艺, 2016, 45(6):14. (CHENG Zhao, JUN Song-dan, JIANG Jing-hua, et al. Advances in research on corrosion and protection of reinforcement in concrete[J]. Thermal Processes, 2016, 45(6):14.)
[4] Collazo A, Nóvoa X R, Pérez C, et al. EIS study of the rust converter effectiveness under different conditions[J]. Electrochimica Acta, 2008, 53 (25): 7565.
[5] DUAN H, DU K, YAN C, et al. Electrochemical corrosion behavior of composite coatings of sealed MAO film on magnesium alloy AZ91D[J]. Electrochimica Acta, 2006, 51 (14):2898.
[6] 张华民, 齐公台, 戴金彪, 等. 钢铁表面高温氧化皮对基体钢腐蚀的影响[J]. 材料保护, 1995(6):24. (ZHANG Hua-min, QI Gong-tai, DAI Jin-biao, et al. Effect of high temperature oxide on steel surface on corrosion of base steel[J]. Material Protection, 1995(6):24.)
[7] 谷征满, 李艳杰, 邓倩, 等. 螺纹钢表面锈蚀的实验研究[J]. 材料与冶金学报, 2016, 15(2):143. (GU Zheng-man, LI Yan-jie, DENG Qian, et al. Experimental study of surface rusting of rebar[J]. Journal of Materials and Metallurgy, 2016, 15(2):143.
[8] 张波, 曹杰, 郭湛, 等. 上冷床温度对螺纹钢筋表面氧化铁皮抗锈蚀性能的影响[J].安徽工业大学学报(自然科学版), 2018, 35(4):301. (ZHANG Bo, CAO Jie, GUO Zhan, et al. Effect of upper cooling bed temperature on the rust resistance of iron oxide on the surface of rebar[J]. Journal of Anhui University of Technology (Natural Science Edition), 2018, 35(4):301.)
[9] Chen R Y, Yeun W Y D. Review of the high-temperature oxidation of iron and carbon steels in air or oxygen[J]. Oxidation of Metals, 2003, 59(5):433.
[10] Chen R Y, Yeun W Y D. Yuen. A Study of the scale structure of hot-rolled steel strip by simulated coiling and cooling[J]. Oxidation of Metals, 2000, 53(5/6): 539.
[11] 蔡伟, 金梁, 毛俊春, 等. 不同相区轧制对螺纹钢组织和性能影响[J]. 中国冶金, 2021, 31(10): 75.(CAI Wei, JIN Liang, MAO Jun-chun, et al. Effect of different phase zones rolling on microstructures and properties of thread steels[J]. China Metallurgy, 2021, 31(10): 75.)
[12] 李志峰, 贺帅, 邢淑清, 等. 铬元素添加对热轧低碳钢高温氧化行为的影响[J]. 钢铁, 2021,56(9): 110. (LI Zhi-feng, HE Shuai, XING Shu-qing, et al. Effect of chromium addition on the high temperature oxidation behaviour of hot rolled mild steel[J]. Iron and Steel, 2021, 56(9):110.)
[13] Klaus Schwerdtfeger, Zhou Shun-xin. A Contribution to scale growth during hot rolling of steel[J]. Steel Research International,2003,74(9):538.
[14] Kofstad P. Low-pressure oxidation of tantalum at 1 300-1 800 ℃[J]. Journal of the Less Common Metala, 1964, 7(4): 241.
[15] 章华明. CSP生产SPHC氧化皮研究[D]. 昆明:昆明理工大学, 2006. (ZHANG Hua-ming. Research on the Production of SPHC Oxide Scale by CSP[D]. Kunming: Kunming University of Science and Technology, 2006.)
[16] 徐蓉. 热轧氧化铁皮表面状态研究和控制工艺开发[D]. 沈阳:东北大学, 2012. (XU Rong. Research on the Surface Condition of Hot Rolled Oxide Scale and Development of Control Technology[D]. Shenyang: Northeastern University,2012.)