高强韧耐候桥梁钢Q690qNH的防断选材及验收方法

doi:10.13228/j.boyuan.issn0449-749x.20210583

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (4423 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract For the 40 mm thick Q690qNH weathering steel plates for bridge produced by TMCP+T and QT processes, tensile tests on longitudinal surface, longitudinal 1/4, longitudinal center and transverse surface at room temperature and Charpy V-shaped impact tests at -120 -+20 ℃ were carried out according to GB/T 228.1—2010 and GB/T 229—2020 standards respectively, and series temperature dynamic tearing tests of -120-+20 ℃ and type P2 non-plastic transition temperature drop hammer tests on longitudinal surface, longitudinal central and transverse surface were carried out according to GB/T 5482—2007 and GB/T 6803—2008 standards respectively, and longitudinal crack tip opening displacement (CTOD) tests and full-thickness deep notched wide plate tensile tests were carried out according to GB/T 21143—2014 and Q/725-1182—2005 standards. Then the experimental data and their correlations were analyzed, at the same time, the metallographic structure of different thickness of steel plate of two kinds of process were observed by using optical microscope, and the fracture morphology of experimental CTOD samples were observed by scanning electron microscope (SEM), and combining with the failure assessment FAD diagram of BS 7910 and the estimation of fracture driving force of typical bridge welded members, the material selection and acceptance method of fracture resistance for high strength and toughness weathering bridge steel Q690qNH were discussed. Results show that the steel plate with QT process has more uniform strength in transverse, longitudinal and thickness directions, and its plasticity, impact, dynamic tear, CTOD and fracture toughness K_C are better, and can be used as D-class steel for key components. However, if it is used as E-class steel, even for general components, there is a certain risk. While the steel plate with TMCP+T process has poor fracture toughness, and even as D-class steel, it does not meet the requirements of material selection based on fracture resistance. It also shows that the rapid increase of brittleness starting temperature at 1/4 thickness of longitudinal impact test has good reliability and applicability as the breaking criterion and acceptance of test Q690qNH weather-resistant bridge steel. When used as a key component, the fiber area ratio at 1/4 thickness of longitudinal impact fracture should be higher than 97.5% and the corresponding impact energy should not be less than 125 J.

Key words： Q690qNH weathering steel fracture toughness quenched and tempered thermo-mechanical control process (TMCP)

Received: 20 September 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	PENG Ning-qi
	FU Gui-qin
	ZHOU Wen-hao
	FAN Ming
	XIONG Xiang-jiang
	ZHU Miao-yong

Cite this article:

PENG Ning-qi,FU Gui-qin,ZHOU Wen-hao等. Material selection and acceptance of fracture resistance for high strength and toughness weather-resistant bridge steel of Q690qNH[J]. Iron and Steel, 2022, 57(3): 97-107.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20210583 OR http://www.chinamet.cn/Jweb_gt/EN/Y2022/V57/I3/97

[1] Okano S. High performance steels for bridge construction and examples of their application[J]. Welding International, 2008, 22(11): 746.
[2] Urban V, Krivy V, Kreislova K. The development of corrosion processes on weathering steel bridges[J]. Procedia Engineering, 2015, 114: 546.
[3] 陈焕德, 刘东升. TMCP型Q500qENH特厚耐候桥梁钢板的工业试制[J]. 钢铁, 2014, 49(4): 69.(CHEN Huan-de,LIU Dong-sheng. Industrial run to produce TMCP processed Q500qENH weathering heavy plate for bridge[J]. Iron and Steel, 2014, 49(4): 69.)
[4] QIN Shun-quan, GAO Zong-yu. Developments and prospects of long-span high-speed railway bridge technologies in China[J]. Engineering, 2017 (6): 23.
[5] 刘宝喜, 高彩茹, 郑文超, 等. 高韧性桥梁钢Q420qD的开发[J]. 中国冶金, 2018, 28(2): 67.(LIU Bao-xi, GAO Cai-ru, ZHENG Wen-chao, et al. Development of Q420qD bridge steel with high toughness[J]. China Metallurgy, 2018, 28(2): 67.)
[6] 武凤娟, 杨浩, 曲锦波. 强化机制对高强度桥梁钢Q500qE屈强比的影响[J]. 中国冶金, 2020, 30(12): 52. (WU Feng-juan, YANG Hao, QU Jin-bo. Effect of strengthening mechanism on yield ratio of high strength Q500qE bridge steel[J]. China Metallurgy, 2020, 30(12): 52.)
[7] 孙毅, 李冠楠, 刘彬, 等. 邯钢桥梁用耐候钢Q345qDNH的开发及应用[J]. 中国冶金, 2021, 31(1): 59.(SUN Yi, LI Guan-nan, LIU Bin, et al. Development and application of weathering steel Q345qDNH for bridge of Hangang[J]. China Metallurgy, 2021, 31(1): 59.)
[8] 卢军辉, 吴战芳, 李忠义, 等. 钙处理对耐候钢低温韧性和耐腐蚀性能的影响[J]. 中国冶金, 2020, 30(1): 44. (LU Jun-hui, WU Zhan-fang, LI Zhong-yi, et al. Effect of calcium treatment on low temperature impact toughness and corrosion resistance of weathering steel[J]. China Metallurgy, 2020, 30(1): 44.)
[9] 卓晓, 安同邦, 马成勇. 420 MPa级耐候桥梁钢用焊材熔敷金属强韧化规律[J]. 钢铁, 2020, 55(4): 88. (ZHUO Xiao, AN Tong-bang, MA Cheng-yong. Strengthening and toughening mechanisms of deposited metals for 420 MPa weathering bridge steel[J]. Iron and Steel, 2020, 55(4): 88.)
[10] 杨新龙,姜军,刘国良,等.建筑结构用耐火耐候钢Q355FRNH耐蚀性能研究[J].轧钢,2021,38(4):33.(YANG Xin-long, JIANG Jun, LIU Guo-liang, et al. Research on corrosion resistance property of fire-resistant and weathering steel Q355FRNH for building structure[J]. China Rolling, 2021, 38(4): 33.)
[11] 袁永旗, 许少普, 陈永彦, 等. 高耐候Q355GNHDZ25钢板的研制[J]. 轧钢, 2021, 38(2): 76.(YUAN Yong-qi, XU Shao-pu, CHEN Yong-yan, et al. Research and development of high weather resistance Q355GNHDZ25 plate[J]. Steel Rolling, 2021, 38(2): 76.)
[12] 王洪东,程政,缪成亮,等. 耐候钢层冷边浪缺陷原因分析与控制[J]. 轧钢, 2020, 37(5): 75.(WANG Hong-dong, CHENG Zheng, MIAO Cheng-liang, et al. Cause analysis and control of edge wave defect after laminar cooling of weathering strip[J]. Steel Rolling, 2020, 37(5): 75.)
[13] 史华跃,冯庆晓,董瀚,等.沙钢超薄带双辊铸轧工艺及超薄带耐候钢的发展现状[J].上海金属,2020,42(6):51.(SHI Hua-yue, FENG Qing-xiao, DONG Han, et al. Development status of Shasteel′s ultra-thin cast strip twin-roll casting and rolling process and weatherproof steel for ultra-thin cast strip[J]. Shanghai Metals, 2020,42(6):51.)
[14] 范建文,廉心桐,陆恒昌,等.经济型耐蚀耐候稀土钢的研制[J].上海金属,2020,42(6):58.(FAN Jian-wen, LIAN Xin-tong, LU Heng-chang, et al. Development of cost-saving corrosion-resistant weatherproof rare earth steel[J]. Shanghai Metals, 2020,42(6):58.)
[15] 易伦雄, 高宗余, 陈维雄. 沪通长江大桥高性能结构钢的研发与应用[J]. 桥梁建设, 2015, 45(6): 36.(YI Lun-xiong, GAO Zong-yu, CHEN Wei-xiong. Development and application of high-performance structural steel for Hutong Changjiang river bridge[J]. Bridge Construction, 2015, 45(6): 36.)
[16] 闫志刚, 赵欣欣, 徐向军. 沪通长江大桥Q500qE钢的适用性研究[J]. 中国铁道科学, 2017, 38(3): 40.(YAN Zhi-gang, ZHAO Xin-xin, XU Xiang-jun. Study on applicability of Q500qE steel for Hutong Yangtze River Bridge[J]. China Railway Science, 2017, 38(3): 40.)
[17] 田越. Q500qE高性能桥梁钢防断性能试验研究[J]. 桥梁建设, 2016, 46(1): 65.(TIAN Yue. Experimental study of fracture resistance properties of Q500qE high-performance bridge steel[J]. Bridge Construction, 2016, 46(1): 65.)
[18] 田越. CTOD与BS 7910结合的桥梁钢断裂韧度评定方法[J]. 中国铁道科学, 2010, 31(2): 40.(TIAN Yue. The fracture toughness assessment method of bridge steel with CTOD and BS 7910[J]. China Railway Science, 2010, 31(2): 40.)
[19] 赵建平, 张秀敏, 沈士明. 材料韧脆转变温度数据处理方法探讨[J]. 石油化工设备, 2004, 33(4): 29.(ZHAO Jian-ping, ZHANG Xiu-min, SHEN Shi-ming. On the method of data processing for ductile-beittle transition temperature[J]. Petro-chemical Eouipment, 2004, 33(4): 29.)
[20] Suresh S. Fatigue of Materials[M]. Second Edition. Cambridgeshire: Cambridge University Press, 1998.
[21] Det Norske Veritas. DNV-OS-C401 2014 Fabrication and Testing of Offshore Structures[S]. Oslo: Det Norske Veritas, 2014.
[22] American Petroleum Institute. API RP 2Z 2005 Recommended Practice for Preproduction Qualification for Steel Plates for Offshore Structures[S]. Washington: American Petroleum Institute, 2005.
[23] 刘冬, 薛欢, 吴立新, 等. 桥梁钢Q420qD断裂韧度CTOD失效评定图评估方法[J]. 物理测试, 2016, 34(6): 29.(LIU Dong, XUE Huan, WU Li-xin, et al. CTOD evaluation of bridge steel Q420qD by failure assessment diagram method[J]. Physics Examination and Testing, 2016, 34(6): 29.)
[24] British Standards Institution. BS 7910 Guide on Methods for Assessing the Acceptability of Flaws in Metallic Structures[S]. London: British Standards Institution, 2005.
[25] 张玉玲, 王冒明, 吴新如, 等. 铁路桥梁钢及焊缝的CTOD性能[J]. 清华大学学报(自然科学), 2005, 45(5): 585.(ZHANG Yu-ling, WANG Mao-ming, WU Xin-ru, et al. CTOD performance of railway bridge base steels and weld seams[J]. Journal of Tsinghua University(Science and Technology), 2005, 45 (5): 585.)
[26] 钱维平. 焊接桥梁结构的断裂驱动力分析[J]. 材料开发与应用, 2001, 16(5): 16.(QIAN Wei-ping. The stress intensity factor of welded bridge structure[J]. Development and Application of Materials, 2001, 16(5): 16.)
[27] The Japan Welding Engineering Society. WES 2805 Method of Assessment for Flaws in Fusion Welded Joints with Respect to Brittle Fracture and Fatigue Crack Growth[S]. Tokyo: The Japan Welding Engineering Society, 2011.
[28] 曲占元. 桥梁钢及其焊接接头的断裂驱动力分析[J]. 四川兵工学报, 2009 (11): 93.(QU Zhan-yuan. The stress intensity factor of bridge steel and its weldment[J]. Journal of Sichuan Ordnance, 2009 (11): 93.)
[29] 刘东升, 程丙贵, 罗咪, 等. 特厚EH47止裂钢板及焊接热影响区的组织性能[J]. 钢铁, 2021, 56(3): 92.(LIU Dong-sheng, CHENG Bing-gui, LUO Mi, et al. Microstructures and mechanical properties in ultra-thick EH47 steel plates and heat affected zones[J]. Iron and Steel, 2021, 56(3): 92.)
[30] 武凤娟,杨浩,邵伟,等.热轧后的冷却方式对Q500qE桥梁钢板屈强比的影响[J].上海金属,2020,42(4):11.(WU Feng-juan, YANG Hao, SHAO Wei, et al.Effect of cooling processes subsequent to hot-rolling on yield ratio of Q500qE bridge steel plate[J].Shanghai Metal, 2020,42(4):11.)
[31] 李强,王皓,郄俊懋.宽厚板Q420q桥梁钢铸坯内部质量的研究[J].连铸,2014(6):40.(LI Qiang, WANG Hao, QIE Jun-mao.Study on theinternal quality of bridge steels Q420q wide and thick slab[J]. Continuous Casting, 2014(6):40.)
[32] 姬凤芹,利成宁,唐帅,等. 低成本减量化Q690qENH高强桥梁钢的开发[J].中国冶金, 2015, 25(4): 1.(JI Feng-qin, LI Cheng-ning, TANG Shuai, et al. Development of Q690qENH high-strength bridge steels with lower cost and reduced technology[J] China Metallurgy, 2015, 25(4): 1.)
[33] 赵丽洋,刘东博,谯明亮,等.Q500qENH耐候桥梁钢形变奥氏体连续冷却转变行为研究[J].上海金属,2022,44(1):35.( ZHAO Li-yang, LIU Dong-bo, QIAO Ming-liang,et al. Study on continuous cooling transformation behavior of deformed austenite for Q500qENH weathering bridge steel[J]. Shanghai Metal, 2022,44(1):35.)
[34] 周任远, 朱丽慧, 柯志刚, 等. 回火温度对改进型T23钢冲击吸收功的影响[J].钢铁, 2021, 56(3): 51. (ZHOU Ren-yuan, ZHU Li-hui, KE Zhi-gang, et al. Effect of tempering temperature on impact absorbed energy of modified T23 steel[J]. Iron and Steel, 2021, 56(3): 51.)
[35] 龚志华,姚斌,王利伟,等. 热处理工艺对2Cr11Mo1VNbN耐热钢组织和性能的影响[J]. 钢铁, 2019, 54(6): 56. (GONG Zhi-hua,YAO Bin,WANG Li-wei,et al. Effect of heat treatment process on microstructure and property of 2Cr11Mo1VNbN heat-resistant steel[J]. Iron and Steel, 2019, 54(6): 56.)
[36] 蔡宁,王文昌,崔桂彬,等. 热处理对高强大梁钢冲击吸收功的影响分析[J]. 中国冶金, 2019, 29(6): 38. (CAI Ning,WANG Wen-chang,CUI Gui-bin, et al. Analysis on effect of heat treatment on impact energy of high-strength beam steel[J]. China Metallurgy, 2019, 29(6): 38.)
[37] Barsom J M, Rolfe S T. Correlations between K_IC and Charpy V-notch test results in the transition-temperature range[C]//Driscoll D E. STP 466: Impact Testing of Metals. West Conshohocken, PA: ASTM, 1970: 281.
[38] British Standards Institution. BS EN ISO 15653:2018 Metallic Materials. Method of test for the determination of quasistatic fracture toughness of welds[S]. Switzerland: BSI,2018.
[39] Barsom J M. Development of the AASHTO fracture toughness requirements for bridge steels[J]. Engineering Fracture Mechanics, 1975 (7): 605.
[40] Sailors R H, Corten H T. Relationship between material fracture toughness using fracture mechanics and transition temperature tests[C]//Corten H T. STP 514: Fracture Toughness: PartⅡ. West Conshohocken, PA: ASTM, 1972: 164.
[41] Sreenivasan P R. Simplicity, consistency and conservatism of some recent Charpy energy-fracture toughness correlations in estimating the ASTM E-1921 reference temperature[J]. Transactions of the Indian Institute of Metals, 2011, 64(4/5): 385.
[42] 薛钢, 宫旭辉, 苏洋, 等. Q500钢焊接接头断裂韧性K_C与冲击功KV₂的相关性统计规律[J]. 材料开发与应用, 2016, 31(4): 1.(XUE Gang, GONG Xu-hui, SU Yang, et al. The statistical natures of relativity between fracture toughness K_C and impact toughness for Q500 steel[J]. Development and Application of Materials, 2016, 31(4): 1.)
[43] 杨滨, 轩福贞. 基于夏比冲击吸收能量的断裂韧性估算方法比较[J]. 压力容器, 2016, 33(1): 32.(YANG Bin, XUAN Fu-zhen. Comparison of fracture toughness estimation methods based on charpy impact energy[J]. Pressure Vessel Technology, 2016, 33(1): 32.)